Durability of Polymers for Cement Modifier in Autoclave Cure
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Durability of Polymers for Cement Modifier in Autoclave Cure
Joo, Myung-Ki; Lee, Youn-Su;
  PDF(new window)
The purpose of this study is to make clear the durability of the polymer films formed in the autoclaved polymer-modified mortars and concretes. The polymer films prepared with polymer dispersions such as a styrene-butadiene rubber (SBR) latex, a poly (ethylene-vinyl acetate)(EVA) emulsion and a polyacrylic ester (PAE) emulsion for polymeric admixtures are exposed to autoclaving at 18 in temperature and 1.01 MPa in vapor pressure, and subjected to tensile test and infrared spectroscopy. The durability of the polymer films is evaluated from the application of autoclaving to the polymer films under saturated Ca(OH) solution immersion causes no degradation for SBR films and a significant degradation due to the saponification of the polymers for EVA and PAE films. Accordingly, in the application of autoclaving to polymer-modified mortars and concretes, it is suggested that SBR-modified mortars and concretes are hardly degraded but EVA- and PAE-modified mortars and concretes are markedly degraded by the saponification of the polymers.
autoclaving;polymer-dispersion for polymeric admixture;tensile behavior;infrared spectroscopy;durability polymer film;saponification;
 Cited by
Y.Ohama, "Handbook of Polymer-Modified Concrete and Mortars-Properties and process Technology,' Noyes Publications, 1994,pp.12-16

出材克宣,"セメント混和用ポリマ一', コンクリ-トエ學, Vol.33, No.3, 1995, pp.25-29

大濱嘉彦, 出村克宣, 三宅雅之, "ポリマ一セメントモルタル及びコンクリ-トにおける鹽化物ィォィソ携散性狀',セメント技術年報, Vol.40,1986, 90pp

大浜嘉彦, 'ポリマ-セメントコンクリ-トの性質と調合設計', セメント.コンクリ-ト, No.410, 1981, pp.10-17

Y. Ohama and S. Kan, 'Effects of Specimen Size on Strength and Drying Shrinkage of Polymer-Modified Concrete,' The International Journal of Cement Composites and Lightweight Concrete, Vol.4, No.4, 1982, pp.229-233 crossref(new window)

朱明基, 大濱嘉彦, 出村克宣,"ォ-トクし-ブ養生ポリマ-セメントモルタルの性質に及ぼす高爐スラク"微粉未及び高희度シリカの影響', セメント.コンクリ-ト論文集, No.53,1995,pp.717-724

朱明基, 大濱嘉彦, 出村克宣, '高爐スラグ微粉未を含むSBR混入ポリマ-セメントコンクリ-トの强度性狀',コンクリ-ト工學論文集,VOI.12,NO.1,2001, pp.55-61

出村克宣, 大濱嘉彦, 朱明基, 'ォ-トクレ-ブ養生ポリマ-セメントモルタルの强さに及ぼすオ-トクレ-ブ養生條件の影響', コンクリ-ト工學年次論文集, VOI.22,No.2, 2000, pp.565-570

安伸二, 小林一輔, 'ポリマ-ディスパ-ジョンによって形成されたポリマ-フイルムの耐アルカリ性に開する2,3の考察', コンクリ-ト工學論文集, Vol.5, No.1, 1994,pp.99-108

內山壯士, "10年間室外暴露したポリマ-セメントモルタルの耐候性', 日本大學修士學位論文, 1998, pp.158-194