Alkali-Activated Coal Ash(Fly Ash, Bottom Ash) Artificial Lightweight Aggregate and Its Application of Concrete
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Alkali-Activated Coal Ash(Fly Ash, Bottom Ash) Artificial Lightweight Aggregate and Its Application of Concrete
Jo Byung-Wan; Park Seung-Kook; Kwon Byung-Yoon;
  PDF(new window)
 Abstract
Artificial lightweight aggregates and solids were manufactured with coal ash(fly ash, bottom ash). In order to apply alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate to concrete, several experimental studies were performed. Thus, it can be noticed the optimal mix proportion, basic characteristies, mechanical properties and environmental safety of alkali-activated coal ash(fly ash, bottom ash) solid and alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate. Also, the freezing-thawing test property of concrete using the alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate was investigated. As a result, the optimal mixing proportion of coal ash(fly ash, bottom ash) solid to make alkali-activated artificial lightweight aggregates was cement , water glass , NaOH , . Alkali-activated coal ash(fly ash, bottom ash) solid can achieve compressive strength of 36.4 MPa, at 7-days, after the paste was cured at air curing after moist curing during 24 hours in . Alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate that do impregnation to polymer was improved crushing strength , and was available to concrete.
 Keywords
alkali activation;fly ash;bottom ash;artificial lightweight aggregate;mechanical property;
 Language
Korean
 Cited by
1.
혼합재 치환율에 따른 경량소재의 물리적 특성,정연조;추용식;이종규;송훈;

한국세라믹학회지 , 2009. vol.46. 6, pp.633-638 crossref(new window)
2.
국산 매립회 골재를 사용한 콘크리트 구조물의 적용성 평가,이봉춘;정상화;채성태;권성준;

한국콘크리트학회논문집, 2011. vol.23. 5, pp.541-550 crossref(new window)
3.
국산 매립회의 골재특성 평가 및 매립회 콘크리트의 내구 성능 평가,이봉춘;정상화;김주형;권성준;

한국콘크리트학회논문집, 2011. vol.23. 3, pp.311-320 crossref(new window)
4.
알칼리 활성화 슬래그 모르타르의 특성에 미치는 혼합 활성화제의 영향,김태완;박현재;서기영;

한국구조물진단유지관리공학회 논문집, 2012. vol.16. 6, pp.26-33 crossref(new window)
5.
가성알칼리와 탄산나트륨을 혼합한 활성화제를 사용한 알칼리 활성화 고로슬래그 모르타르의 강도 특성,김태완;

한국콘크리트학회논문집, 2012. vol.24. 6, pp.745-752 crossref(new window)
6.
바텀 애시를 콘크리트 잔골재로 사용하기 위한 활용성에 관한 연구,김성수;이정배;박승호;

한국건설순환자원학회논문집, 2014. vol.2. 3, pp.173-179 crossref(new window)
1.
Evaluation for Properties of Domestic Pond Ash Aggregate and Durability Performance in Pond Ash Concrete, Journal of the Korea Concrete Institute, 2011, 23, 3, 311  crossref(new windwow)
2.
Influence of Blended Activators on the Physical Properties of Alkali-activated Slag Mortar, Journal of the Korea institute for structural maintenance inspection, 2012, 16, 6, 26  crossref(new windwow)
3.
The Strength Properties of Alkali-Activated Slag Mortars by Combined Caustic Alkali with Sodium Carbonate as Activator, Journal of the Korea Concrete Institute, 2012, 24, 6, 745  crossref(new windwow)
4.
Bottom Ash on the Application for Use as Fine Aggregate of Concrete, Journal of the Korean Recycled Construction Resources Institute, 2014, 2, 3, 173  crossref(new windwow)
5.
Evaluation for Applicability of Reinforced Concrete Structure with Domestic Pond Ash, Journal of the Korea Concrete Institute, 2011, 23, 5, 541  crossref(new windwow)
 References
1.
Donald W. Pfeifer, 'Fly Ash Aggregate lightweight Concrete,' International Ash Utilization Syposium, ACAA, 1971, pp.1993-1999

2.
Joseph. R. P. and Gary T. R. 'Aqeous Rection of Fly Ash and $Ca(OH)^2 $ to Produce Calcium Silicate Absorbent for Flue Gas Desulfurization', Environ. Sci-Technol. 1988, pp.1299-l304

3.
J. Wastiels, X. Wu, S. Faignet, and G. Patfoort, 'Mineral polymer based on fly ash,' Journal of Resource Managment and Technology, Vol22, No.3, 1994, p.135-141

4.
S. A Khadikar, M. V. Karandikar, D. Ghosh, and A. K. Chatterjee 'A novel clinkerization process for fly ash utilization,' 6th CANMET/ACI/JCI, Bangkok, Thailand, Vol.1, 1998, pp.225-239

5.
S. Wang and K.L. Scrivener 'Hydration products of alkali activated slag cement,' Cem. Concr. Res., Vol.25, No.3, 1995, pp.561-571 crossref(new window)

6.
W. Jian and D.M Roy, 'Hydrothemal processing of new fly ash cement,' Ceram Bull. Vol.71, No.4, 1992, pp.642 -647

7.
Wu. X and J. wastiels, 'Detoxification of Fly Ash from Incneration Plants,' Pro. of 13th Annual Conf. of Waste Prevention, Reduction and Recycling, Brussels, 1993, pp.1112-1116

8.
Z. P Bazant, 'Thermodynamics of Hindered Adsorption and Its Implication for Hardened Cement Paste and Concrete,' Cement and Concrete Research, Vol. 2, 1972, pp.1 -16 crossref(new window)

9.
T. Silverstrim, H. Rostami, Y. Xi, and J. Martin, 'High performance characterstics of chemically activated fly ash,' Proceedings cf the PCI/FHWA International. Symposium on HPC, New Orleans, LA, 1997, pp.135-147

10.
저자, '플라이애쉬의 시멘트 클링커 대체 성능과 재활용 수급전망', 한국과학기술정보원, 2003