Effects of Air Void at the Steel-Concrete Interface on the Corrosion Initiation of Reinforcing Steel in Concrete under Chloride Exposure
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effects of Air Void at the Steel-Concrete Interface on the Corrosion Initiation of Reinforcing Steel in Concrete under Chloride Exposure
Nam Jin-Gak; Hartt William H.; Kim Kijoon;
  PDF(new window)
 Abstract
A series of reinforced G109 type specimens was fabricated and pended with a 15 weight percent NaCl solution. Mix design variables included 1) two cement alkalinities (equivalent alkalinities of 0.32 and 1.08), 2) w/c 0.50 and 3) two rebar surface conditions (as-received and wire-brushed). Potential and macro-cell current between top and bottom bars were monitored to determine corrosion initiation time. Once corrosion was initiated, the specimen was ultimately autopsied to perform visual inspection, and the procedure included determination of the number and size of air voids along the top half of the upper steel surface. This size determination was based upon a diameter measurement assuming the air voids to be half spheres or ellipse. The followings were reached based upon the visual inspection of G109 specimens that were autopsied to date. First, voids at the steel-concrete interface facilitated passive film breakdown and onset of localized corrosion. Based upon this, the initiation mechanism probably involved a concentration cell with contiguous concrete coated and bare steel serving as cathodes and anodes, respectively. Second, the corrosion tended to initiate at relatively large voids. Third, specimens with wire-brushed steel had a lower number of voids at the interface for both cement alkalinities, suggesting that air voids preferentially formed on the rough as-received surface compared to the smooth wire brushed one.
 Keywords
air void;cement alkalinity;steel-concrete interface;passive film;cathode;
 Language
English
 Cited by
 References
1.
D. A. Hausmann, 'Steel Corrosion in Concrete- How Does It Occur',' Material Protection, Vol.6, 1967, pp.19-23

2.
P. Sandberg, K. Pettersson, H.E. S\$\emptyset$rensen, and H. Arup, Critical chloride concentrations for the onset of active reinforcement corrosion, RILEM, 1997, pp.453-459

3.
G. K. Glass and N. R. Buenfeld, Chloride threshold levels for corrosion induced deterioration of steel in Concrete, RILEM, 1997, pp.429-440

4.
T. Yonezawa, V. Ashworth and R. P. M. Procter, 'Pore Solution Composition and Chloride Effects on the Corrosion of Steel in Concrete,' Corrosion Engineering, Vol. 44, No.7, 1988, pp.489-499 crossref(new window)

5.
G. E. Monfore and G. J. Verbeck, 'Corrosion of Prestressed Wire in Concrete,' ACI Journal, Vol.32, 1960, pp.491-515

6.
G. K. Glass and B Reddy, The Influence of the Steel Concrete Interface on the Risk of Chloride Induced Corrosion Initiation, COST521 Workshop, Luxembourg, 2002

7.
Robert A. Perks, Chloride Thresholds for Initiation of Corrosion of Steel Reiniforcement in Concrete, Master thesis, Ocean Engineering Department, Florida Atlantic University, 2000

8.
J.A Gonzalez, E. Ramirez, A. Bautista, and S. Feliu, 'The Behavior of Pre-Rusted Steel in Concrete,' Cement and Concrete Research, Vol.26, 1996, pp.501-511 crossref(new window)

9.
L. Li, Pitting Corrosion and Chloride Corrosion Threshold of Reinforced Steel in Alkaline Solutions, University of South Florida, 2000, 3pp

10.
T. Mehmood, S. N. Absan, and Mohammad S. AlMughaidi, Atmospheric Rusting of Rebars and Its Effect on Reinforced Concrete Corrosion, CORROSION 1998, NACE International, Houston, 1998, Paper No. 00633

11.
M. Hansson and B. Sorensen, Corrosion Rates of Steel in Concrete, ASTM STP 1065, 1990, 3pp

12.
ASTM Standard Test Method G109-99, 'Determining the Effect of Chemical Admixture on the Corrosion of Embedded Steel Reinforcement in Concrete Exposed to Chloride Environments,' Annual book of ASTM standard, Vol.03.02, American Society for Testing and Materials, 100 Barr Harbor Drive, West Conshohocken, PA

13.
'Half-cell Potentials of Uncoated Reinforcing Steel in Concrete,' ASTM C876-91, Annual book of ASTM Standards, 1991, ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 USA

14.
R.L. Miller, W.H. Hartt, and R.P. Brown, 'Stray Current and Galvanic Corrosion of Reinforcing Steel in Concrete,' Materials Performance, Vol.15, 1976, pp. 20-27

15.
V. S. Dubovoy, S. H. Gebler, and P. Klieger. 'CementAlkalinity Levels as It Affects Air-Void Stability, Freeze-Thaw Resistance, and Deicer Scaling Resistance of Concrete,' Research and Development Bulletin RD 128

16.
T.U. Mohammed, T. Fukute, T. Yamaji, and H. Hamada, Long Term Durability of Concrete Made with Different Water Reducing Chemical Admixtures under Marine Environment, Concrete for Extreme Conditions, London, 2002, 233pp