Durability Assessment of High Strength Concrete with High Volume Mineral Admixture
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Durability Assessment of High Strength Concrete with High Volume Mineral Admixture
Baek, Chul-Woo; Kim, Hoon-Sang; Choi, Sung-Woo; Jo, Hyun-Tae; Ryu, Deug-Hyun;
  PDF(new window)
The purpose of this study was to assess the durability of high-strength concrete with high volume mineral admixture (HVMAC) derived from previous studies within ternary blended concrete (TBC) and normal concrete (NC). Four durability evaluation types such as chloride penetration resistance, freezing and thawing resistance, carbonation resistance in two pre-treatment conditions, and sulfuric acid and sulfate resistance using 5% sulfuric acid (), 10% sodium sulfate (), and 10% magnesium sulfate () solution were selected and performed in this study. HVMAC showed the excellent chloride penetration resistance in any age and the freezing and thawing durability close to 100%. In addition, HVMAC affected more reduction in carbonation resistance than TBC. When the curing time was increased, to create a concrete internal organization densely improved resistance to carbonation. HVMAC also showed the most superior in sulfuric acid and sulfate resistance. As the reduction of calcium hydroxide and to apply a large amount of admixture reduced the swelling and cracking of concrete, the strength reduction and mass change of concrete was found to be small indicated.
high volume mineral admixture;durability;chloride penetration resistance;sulfuric acid and sulfate resistance;
 Cited by
박테리아 슬라임을 활용한 콘크리트 하수관거 내황산 코팅 기술,양근혁;윤현섭;이상섭;

한국콘크리트학회지, 2016. vol.28. 3, pp.18-22
3성분계 시멘트에서 FA 및 BS의 최적혼합비율 도출에 관한 연구,한천구;박성배;

한국건설순환자원학회논문집, 2016. vol.4. 2, pp.143-148 crossref(new window)
A Study on Optimum Proportion of FA and BS for Ternary Cement, Journal of the Korean Recycled Construction Resources Institute, 2016, 4, 2, 143  crossref(new windwow)
Cho, J. W., "$CO_2$ Reduction Cement", Technologies, Magazine of the Korea Concrete Institute, Vol.23, No.6, 2011, pp.32-35.

Park, C. B., Ryu, D. H., and Sae, C. H., "Hydration of High Volume Mineral Admixture Binder with Kind of Activators", Journal of the Architectural Institute of Korea Structure & Construction, Vol.28, No.10, 2012, pp.89-96.

Choi, S. W., Ryu, D. H., Kim, H. S., and Kim, G. Y., "Hydration Properties of Low Carbon type Low Heat Blended Cement", Journal of the Korea Institute of Building Construction, Vol.13, No.3, 2013, pp.218-226. crossref(new window)

Choi, Y. C., Moon, G. D., Kim, J. H., and Cho, Y. K., "Effect of Anhydrite on the Mechanical and Durability Properties of High Volume Slag Concrete", Journal of the Korean Recycled Construction Resources Institute, Vol.2, No.3, 2014, pp.239-246. crossref(new window)

Halit, Y., Mert, Y., Husyinn, Y., Serdar, A., and Selcuk, T., "Mechanical properties of reactive powder concrete containing high volumes of ground granulated blast furnace slag", Cement & Concrete Composite, Vol.32, 2010, pp.639-648. crossref(new window)

Choi, S., Lee, K. M., Jung, S. H., and Kim, J. H., "A Study on the Carbonation Characteristics of Fly Ash Concrete by Accelerated Carbonation Test", Journal of the Korea Concrete Institute, Vol.21, No.4, 2009, pp.449-455. crossref(new window)

Kim, J. P., "Selection of Portland Cement for Prevention of Sulfate Attack - Part 1 Sodium Sulfate Attack", Journal of the Korea Concrete Institute, Vol.21, No.4, 2009, pp.441-447. crossref(new window)

Bleszynski, R., Hooton, R. D., Thomas, M. D. A., and Rogers, C. A., "Durability of Ternary Blend Concrete with Silica Fume and Blast-Furnace Slag: Laboratory and Outdoor Exposure Site Studies", ACI Materials Journal, Vol.99, No.5, 2002, pp.499-508.

Song, H. W., Lee, C. H., Kim, J. H., and Ann, K. Y., "Chloride Penetration Resistance of Ternary Blended Concrete and Discussion for Durability", Journal of the Korea Concrete Institute, Vol.20, No.4, 2008, pp.439-449. crossref(new window)

Baek, C. W., Park, C. B., Choi, S. W., Jo, H. T., and Ryu, D. H., "Mechanical Properties of High Strength Concrete with High Volume Mineral Admixture", Journal of the Korean Recycled Construction Resources Institute, Vol.2, No.3, 2014, pp.180-187. crossref(new window)

Nordtest Method, NT-BUILD 492, Concrete, Mortar and Cement-Based Repair Materials, Chloride Migration Coefficient from Non-Steady-State Migration Experiments, Nordtest, Finland, 1999.

JSTM C 7401, "Method of test for chemical resistance of concrete in aggressive solution", 1999, pp.1-10.

Monteny, J., Vincke, E., Beeldens, A., Taerwe, L., Van Gemert, D., and Verstraete, W., "Chemical, Microbiological, and in Situ Test Methods for Biogenic Sulfuric Acid Corrosion of Concrete", Cement and Concrete Research, Vol.30, No.4, 2000, pp.623-634. crossref(new window)

Bae, S. H., Park, J. I., and Lee, K. M., "Influence of Mineral Admixtures on the Resistance to Sulfuric Acid and Sulfate Attack in Concrete", Journal of the Korea Concrete Institute, Vol.22, No.2, 2010, pp.219-228. crossref(new window)

Shanahan, N., and Zayed, A., "Cement Composition and Sulfate Attack Part", Cement and Concrete Research, Vol.37, No.4, 2007, pp.618-623. crossref(new window)

Santhanam, M., Cohen, M. D., and Olek, J., "Me-chanism of Sulfate Attack : A Fresh Look Part 2 : Proposed Mechanisms", Cement and Concrete Research, Vol.33, No.3, 2003, pp.341-346. crossref(new window)

Maruya Tsuyoshi, "Construction of the analysis method on the movement of the chloride ions in the concrete", Reaearch Report, The University of Tokyo, Japan, 1995, pp.41-45.