Effects of Pre-Sintering Surface Treatment and Liner Application on the Shear Bond Strength of Zirconia and Pressable Ceramic
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effects of Pre-Sintering Surface Treatment and Liner Application on the Shear Bond Strength of Zirconia and Pressable Ceramic
Lee, Gwang-Young; Cho, Mi-Hyang; Choi, Sung-Min;
  PDF(new window)
 Abstract
Purpose: This study was intended to investigate the effect of applying liner for chemical bonding and physical surface roughness created on zirconia by using a sandpaper before sintering on the bond strength between the two materials. Methods: Zirconia blocks were cut using a low-speed cutter. Plate-shaped specimen() was fabricated by sintering after giving surface roughness according to four kinds of sandpapers. Depending on whether or not to use liner, 60 specimens were divided into two groups ZN(non-liner), ZL(liner), and the two groups were subdivided into four groups respectively in accordance with sandpaper used, totaling eight groups (n
 Keywords
zirconia;shear bonding strength;surface treatment;pressing ceramics;
 Language
Korean
 Cited by
 References
1.
Aboushelib MN, De Jager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater, 21(10), 984-991, 2005. crossref(new window)

2.
Aboushelib MN, de Kler M, van der Zel JM, Feilzer AJ. Effect of veneering method on the fracture and bond strength of bilayered zirconia restorations. International Journal of Prosthodontics, 21(3), 237-240, 2008.

3.
Aboushelib MN, Kleverlaan CJ, Feilzer AJ, Microtensile bond strength of different components of core veneered all-ceramic restorations: Part II: Zirconia veneering ceramics. Dent Mater, 22(9), 857-863, 2006. crossref(new window)

4.
Albakry M, Guazzato M, Swain MV. Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials. J Dent, 31(3), 181-188, 2003. crossref(new window)

5.
Al-Dohan HM, Yaman P, Dennison JB, Razzoog ME, Lang BR. Shear strength of core-veneer interface in bi-layered ceramics. J prosthet Dent 91(4), 349-355, 2004. crossref(new window)

6.
Choi MS, Kim YS, Suh KW, Ryu JJ. Effect of surface treatmet on the shear bond strength of a zirconia core to veneering ceramic. The journal of Korean academy of prosthodontics. 47(2), 199-205, 2009. crossref(new window)

7.
Derand T, Molin M, Kvam K. Bond strength of composite luting cement to zirconia ceramic surfaces. Dent Mater, 21(12), 1158-1162, 2005. crossref(new window)

8.
DeJager N, Pallav P, Feilzer AJ. The influence of design parameters on the FEA-determined stress distribution in CAD-CAM produced all-ceramic crowns. Dent Mater, 21, 242-251, 2005. crossref(new window)

9.
Dundar M, Ozcan M, Gokce B, CBomlekogelu E, Leite F, Valandro LF, Comparison of two bond strength testing methodologies for bilayered allceramics. Dent Mater 23(5), 630-636, 2007. crossref(new window)

10.
Fischer J, Stawarczyk B, Hammerle CHF. Flexural strength of veneering ceramics for zirconia. J dent, 36(5), 316-321, 2008. crossref(new window)

11.
Guazzato M, Quach L, Albakry M, Swain MV. Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic. J Dent, 33(1), 9-18, 2005. crossref(new window)

12.
Isgro G, Pallav P, van der Zel JM, Feilzer AJ. The influence of the veneering porcelain and different surface treatments on the biaxial flexure strength of a heat-pressed ceramic. J Prosthet Dent, 90, 465-473, 2003. crossref(new window)

13.
Kim CY, Choi SM. A study on interfacial characteristics of Ni-Cr alloy by Nb content for Porcelain Fused to Metal Crown. The Journal of Korean academy of dental technology, 27(1), 97-104, 2005.

14.
Lee JH, Ahn JS. Effect of surface and heat treatment on the bond strength of veneering ceramics to zirconia(Y-TZP). The Journal of Korean academy of dental technology, 35(4), 271-280, 2013. crossref(new window)

15.
Sundh A, Sj ogren G. A comparison of fracture strength of yttrium oxide& ipartially stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramics. J Oral Rehabil, 31(7), 682-688, 2004. crossref(new window)

16.
Tinschert J, Natt G, Mautsch W, Spiekermann H, Anusavice KJ. Marginal fit of alumina-and zirconia-based fixed partial dentures produced by a CAD/CAM system. Oper Dent, 26(4), 367-374, 2000.

17.
Wegner SM, Kern M, Long-term resin bond strength to zirconia ceramic. J Adhes Dent, 2(2), 139-147, 2000.