Friction and Wear Characteristics of Plasma Coated Surface of Casting Aluminum Alloy
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Friction and Wear Characteristics of Plasma Coated Surface of Casting Aluminum Alloy
Chae, Young-Hun; Ren, Jing-Ri; Park, Jun-Mock; Kim, Seock-Sam;
  PDF(new window)
 Abstract
The wear characteristics and wear mechanisms of plasma sprayed Al/sub 2/ O/sub 3/-40%TiO/sub 2/ and Cr/sub 2/O/sub 3/ deposited on casting aluminum alloy(AC4C) were investigated. Specimens were processed for various coating thicknesses. Ball on disk type wear tester was used for wear test. The scratch test on plasma sprayed coating surface showed that critical load to break the coating layer was greater than 40 N. The critical load increase with the increase of coating thickness of specimens. The friction coefficient of Cr/sub 2/O/sub 3/ coating layer was less than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. The wear resistance of Cr/sub 2/O/sub 3/ coating layer was greater than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. Microscopic observation of worn surfaces was made by SEM. SEM observation showed that the main mechanism of wear for Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer was abrasive wear under 50 N. For the case of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer, as the surface cracks perpendicular to sliding direction propagated, the wear debris was generated in wear track. However, the main mechanism of wear for Cr/sub 2/O/sub 3/ coating layer was brittle fracture under 150 N.
 Keywords
Wear Mechanism;Plasma Spray;Casting Aluminum Alloy;Critical Load;Specific Wear Rate;