A Study on the Corrosion Susceptibility and Corrosion Fatigue Characteristics on the Material of Turbine Blade
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
A Study on the Corrosion Susceptibility and Corrosion Fatigue Characteristics on the Material of Turbine Blade
Jo, Seon-Yeong; Kim, Cheol-Han; Ryu, Seung-U; Kim, Hyo-Jin; Bae, Dong-Ho;
  PDF(new window)
Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.
Fatigue Strength;Corrosion Potential;Corrosion Cell;Corrosion Current Density;Corrosion Rate;Intergranular Corrosion;Corrosion Fatigue;Stress Intensity Factor Range;Crack Growth Rate;
 Cited by
12Cr 합금강의 부식특성 및 인공열화된 12Cr합금강의 피로특성,조선영;김철한;배동호;

대한기계학회논문집A, 2001. vol.25. 6, pp.965-971 crossref(new window)
1985, 腐食과 破壞, pp. 71-74., 日本機械學會

ASTM G5, 1987, 'Standard Reference Test Mehtod for Making Potentiostatic and Potentiod-ynamic Anodic Polarization Measurements,' Annual Bool of ASTM standards, pp. 73-76

Dean, S. W., 1971, Handbook on Corrosion Testing and Evaluation, John Wiley, p. 171

ASTM A262, 1991, 'Standard Practice for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steel', Annual Bool of ASTM standards, pp. 46-50

ASTM STP425, 1966, 'Stress Corrosion Cracking of Stainless steels Mechanism of Crack Initiation in Chloride Solutions', p. 155

Herbert H. Uhlig and Winston, R. Revie, 1985, Corrosion and Corrosion Control, Wiley, 3rd ed., pp. 96-111

Speller, F.N., 1951, Corrosion, Causes and Prevention, McGraw-Hill, 3rd ed., p. 168

ASTM E647-95, 1995, 'Standard Test Method for Measurement of Fatigue Crack Growth Rates', Annual Bool of ASTM standards, pp. 578-614

Hicks, M. A. and Pickard, A. C, 1982, 'A Comparision of Theoretical and Experimental Me-thods of Calibrating the Electrical Potential Drop Technique for Crack Length Determination', International Journal of Fracture, Vol. 20, pp. 91-101