Responses of Ultrasonic Backscattered Energy and AE Charateristics on the Progressive Damage of Crossply Composite Laminates
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Responses of Ultrasonic Backscattered Energy and AE Charateristics on the Progressive Damage of Crossply Composite Laminates
Jeon, Heung-Jae;
  PDF(new window)
Responses of ultrasonic back scattered energy and AE (Acoustic Emission) characteristics related to the progressive damage of and crossply laminates were studied. It was found that the ultrasonic backscattered energy was sensitive to the matrix cracking but not sensitive to other failure mechanisms. However, AE was proved to be sensitive to matrix cracking as well as other failure mechanisms.AE signals were analyzed by investigating the amplitude and number of counts per event for corresponding applied strain. Loading and unloading tests were conducted separately. AE results showed Kaiser effect in the crossply composite laminates and ultrasonic results supported the AE results.
Crossply Composite Laminate;Progressive Damage;Ultrasonic Backscattered Energy;Acoustic Emission;
 Cited by
Charewicz, A. and Daniel, I. M., 1986, 'Damage Mechanisms and Accumulation in Graphite/Epoxy Laminates,' Composite Materials: Fatigue and Fracture, ASTM STP 907, ed. H. T. Hahn, ASTM, Philadelphia, pp. 274-297

Laws, N. and Dvorack, G. J., 1988, 'Progressive Transverse Cacking in Composite Laminates,' J. Comp. Mater. Vol. 22, pp. 900-916 crossref(new window)

Yang, J. N., Jones, D. L., Yang, S. H., and Meskin, A., 1990, 'A Stiffness Degradation Model for Graphite/Epoxy Laminates,' J. Comp. Mater., Vol. 24, pp. 753-769 crossref(new window)

Talreja, R., 1985, 'Transverse Cracking and Siffness Reduction in Composite Laminates,' J. Comp. Mater., Vol 19, pp. 335-375 crossref(new window)

Ogin, S. L., Smith, P. A., and Beaumont, P. W. R., 1985, 'Matrix Cracking and Stiffness Reduction During the Fatigue of $[0/90_2]_s$GFRP Laminate,' Composite Science and Technology, Vol. 22, pp. 22-31

Daniel, I. M., and Lee, J. W., 1990, 'Damage Development in Composite Laminates UnderMonotonic Loading,' J. Compos. Technol. Res.,Vol. 12, pp. 98-102

Tsai, C.-L., and Daniel, I. M., 1993, 'The Behavior of Cracked Cross-Ply Composite Laminates Under General In-Plane Loading,' Damage in Composite Materials, ed. G. Z. Voyiadjis, Elsevier, pp. 51-66

Daniel, I. M., Wooh, S. C. and Lee, J. W., 1990, 'Nondestructive Evaluation of Damage Development in Composite Materials,' Elastic Waves and Ultrasonic Nondestructive Evaluation, eds. S. K. Datta, J. D. Achenbach and Y. S, Elsevier, pp. 183-189

Bhat, T. M. Hutchins, D. A. and Mottram, J.T., 1993, Simultaneous Acoustic Emission and Ultrasonic Tomographic Imaging in Anisotropic Polymer Composite Material,' Journal of Acoustical Society of America, Vol. 94, pp. 944-953 crossref(new window)

Bakuckas, J. G., Prosser, W. H. and Johnson, W. S., 1994, 'Characterization of Fatigue Damage in Unidirectional GFRP Composites Through GFRP Acoustic-Emission Signal Analysis,' NDT & E International, Vol. 27, pp. 27-32 crossref(new window)

Luo, J. J., Wooh, S. C. and Daniel, I. M, 1995, 'Acoustic-Emission Study of Failure Mechanism in Ceramic-Matrix Composite Under Longitudinal Tensile Loading,' Journal of Composite Materials, Vol. 29, pp. 1946-1961

Barre, S. and Benzeggagh, M. L., 'On the Use of Acoustic-Emission to Investigate Damage Mechanisms in Glass-Fiber-Reinforced Polypropylene,' Composites Science and Technology, Vol. 52, pp. 369-376

윤동진, 권오양, 이재락, 1990, '음향 방출을 이용한 Loading-Unloading 인장시험시 CFRP의 파괴거동해석,' 한국복합재료학회지, 제3권 제2 호, pp. 22-30

이유태, 김상태, 권재도, 이택순, 岸 輝雄, 志 波光晴, 1995, '탄소섬유 강화 복합재료의 반복 하중에 의한 손상과 파괴에서의 AE특성,' 한국복합재료학회지, 제8권 제2호, pp. 40-51

김상태, 이유태, 김광수, 1997, '음향방출법을 이용한 탄소섬유강화 복합재료(CFRP)의 파괴인성평가,' 한국복합재료학회지, 제10권 제l호, pp. 23-33

전흥재, I. M. Daniel, 1998, '복합재료 직교 적층판의 손상과정에서의 AE특성에 관한 연구,' 한국복합재료학회지, 제11권 제5호, pp. 14-21