Study on the Evaluation of Fracture Toughness at Welded Zone for the Pipe Steel by Gas Welding
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Study on the Evaluation of Fracture Toughness at Welded Zone for the Pipe Steel by Gas Welding
Na, Ui-Gyun; Yu, Hyo-Seon; O, Seok-Hyeong;
  PDF(new window)
 Abstract
The purpose of this study is to examine the fracture toughness of the welded pipe from the viewpoint of FATT for the S38 and S42 steels used widely as the pipe material. Post weld heat treatment(PW HT) was carried out like following conditions: temperature of 67, I hour of holding time and cooling in furnace. Fracture toughness was obtained by measuring the crack opening displacement(COD) of the notched specimens over the range of temperature from -14 to -. Hardness values at fusion line near around were the highest and the microstructures at welded zone were coarsened. Regardless of the pipe materials, COD and temperature curves of the as-welds were moved toward higher temperature compared with those of the parents. However, COD and temperature curves of the PWHT specimens were positioned at lower temperature compared with those of the as-welds. The more heat input causes to decrease the COD values at the constant temperature. It was verified through the recrystallization treatment that PWHT was attributed to move toward lower temperature region considerably due to the improved plastic deformation at the same applied COD value of 0.3mm and softening effect. In case of the weldment of S38 steel, cleavage fracture was observed at -105 unlike the structural steels, in which brittle fracture mode was generally shown at - 196.
 Keywords
Fracture Toughness;Pipe Material;Crack Opening Displacement;Recrystallization Treatment;Post Weld Heat Treatment;Plastic Deformation;Cleavage Fracture;
 Language
Korean
 Cited by
 References
1.
이재익, 1988, 'Plant설계의 손상경향에 대하여,' 한국부식학회지, Vol. 17, No. 3, pp. 172-198

2.
鄭世喜, 1977, ' 高張力鋼 溶接熱影響部の 溶接後熱處理 胞化に關する硏究,' 東京大學(日本) 博士學位論文

3.
Dolby, R. E., 1971, Metal Construction and British Welding Journal, p. 99

4.
Method for Crack Opening Displacement(COD) Testing, 1972, B.S. 6762

5.
Lancaster, J. F., 1974, Metallurgy of Welding, pp. 70-73

6.
엄기원, 1992, 최신 용접공학, 동명사, pp. 249-251

7.
박종완, 임대문, 김원중, 장태석 공역, 1999, 재료과학과 공학, Scitech, pp. 307-309

8.
Petch, N. J., 1953, Iron Steel Inst, Vol. 173, p. 25

9.
임재규, 1986, 'Cr-Mo강 용접부의 용접후 열처리가 파괴인성에 미치는 영향,' 전북대학교 박사학위논문

10.
정세희, 임재규, 1983, 'Cr-Mo강 용접열영향부의 파괴인성에 미치는 용접후열처리의 영향(I),' 대한기계학회논문집, 제8권 제2호, pp. 109-118

11.
정세희, 임재규, 1987, 'Cr-Mo강 용접열영향부의 용접후열처리 취화에 관한 연구,' 대한기계학회논문집, 제11권 제2호, pp. 314-321

12.
Rolfe, S. T., and Barsom, J. M., 1977, Fracture and Fatigue Control in Structures, pp. 7-10

13.
Knott, J. F., 1981, Fundamentals of Fracture Mechanics, pp. 172-173

14.
조규종, 1987, '재결정법과 유한요소법에 의한 연성파괴의 고찰,' 전북대학교 박사학위논문