A Study on the 43 Degradation Behavior of Cast Stainless Steel(CF8M)(I);Evaluation of Degradation mechanism, Static and Fatigue Strength
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
A Study on the 43 Degradation Behavior of Cast Stainless Steel(CF8M)(I);Evaluation of Degradation mechanism, Static and Fatigue Strength
Gwon, Jae-Do; Park, Jung-Cheol; Lee, Yong-Seon; Lee, U-Ho; Park, Yun-Won;
  PDF(new window)
 Abstract
The five classes of the thermally aged CF8M specimen are prepared using an artificially accelerated aging method. Namely, after the specimens are held for 100, 300, 900, 1800, and 3600hrs at 430 respectively, the specimens are water-cooled to room temperature. The impact energy variations are measures for both the aged and virgin specimens through the Charpy impact tests in addition to the microstructure observation, tensile, hardness and fatigue crack growth tests. From the present investigation the following results are obtained : 1) The difference among the thermally degraded specimens can be distinguished through their microstructures, 2) Hardness and tensile strength are increased to 300hrs, degradation specimen, while elongation and reduction area are decreased to 3600hrs degradation specimen, and impact energy is decreased to 1800hrs degradation specimen, 3) The FCG rates for thermally degraded specimens are larger than that of the virgin specimen.
 Keywords
CF8M;Thermal Aging;Virgin Material;Degraded Material;Observation of Microstructure;Microhardness Test;Tensile Test;Impact Test;Fatigue Crack Growth Test;
 Language
Korean
 Cited by
1.
주조 스테인리스강 CF8M의 43$0^{\circ}C$ 열화거동에 관한 연구 (III) - 탄소성 파괴인성 평가 -,권재도;인재현;박중철;최성종;박윤원;

대한기계학회논문집A, 2000. vol.24. 10, pp.2405-2412 crossref(new window)
 References
1.
Solomon, H. D. and Levinson, Lionel M., 1978, 'Mossbauer Effect Study of 475$^{circ}C$ Embrittlement of Duplex and Ferritic Stainless Steels,' Acta Metallurgical, Vol. 26, pp. 429-442 crossref(new window)

2.
Chung, H. M. and Leax, T. R., 1989 August 1-2,'Embrittlement of Laboratory and Reactor Aged CF3, CF8 and CF8M Duplex Stainless Steel,' International Workshop on Intermediate-Temperature Embrittlement Processes in Duplex Stainless Steel, Oxford, England

3.
Chopra, O. K. and Chung, H. M., 1989, 'Initial Assessment of the Process and Significance of Thermal Aging in cast stainless Steels,' NUREG/CP-097, Vol. 3, pp. 519-546

4.
Chopra, O. K. and Chung, H. M., 1989, 'Aging Degradation of Cast Stainless Steels : Effect on Mechanical Properties,' Environmental Degradation of Materials in Nuclear Power Systems, pp. 737-748

5.
International Atomic Energy Agency Advanced Incident Reporting System 분석자료, 1996

6.
日本原子力硏究委員會, 1993, 原子力發電プラントの保守 經年化對策に關する國內シンポジウム

7.
Eiber, R. J., Maxey, W. A., Duffy, A. R., and Atterbruy, T. J., July 1969, 'Investigation of the Initiation and Extent of Ductile pipe Rupture,' BMI 1866

8.
Prepared under the direction of the ASM International Handbook Committee, 1996, 'Fatigue and fracture properties of stainless steels,' ASM handbook Vol. 18(Fatigue and fracture), pp. 717-718

9.
Nichol, T. J., Datta, A. and Aggen, G., 1980, 'Embrittlement of Ferritic Stainless Steels,' Metallurgical Transactions A, Vol. 11A, pp. 573-587 crossref(new window)

10.
Vrinat, M., Cozar, R., and Meyzaud, Y., 1986, 'Precipitated Phase in the Ferrite of Aged Cast Duplex Stainless Steels,' Scripta Metallurgica, Vol. 20, pp. 1101-1106 crossref(new window)

11.
이봉상 외 4명, 1994, '국내 원전 주조스테인리스강 부품의 열취화 평가,' 한국원자력 연구소

12.
Hideo Kitagawa, Jae Do Kwon, Yuuji Nakasone, and Tsuyoshi Shimazaki, 1986, 'Fatigue Crack Growth Life Prediction of a Cr-Mo Steel Degraded in Long Service (1st Report, Fatigue Crack Growth Properties in a Long-service-degraded Material),' Transactions of the Japan Society of Mechanical Engineers A Tokyo, Vol. 52, No. 480, pp. 1749-1756

13.
Slima, G., Petrequin, P., and Mager, T., 1983, 'Effect of Aging on Mechanical Properties of Austenitic Stainless Steel Casting and Weld,' Structural Integrity of LWR, 7th SMiRT, pp. 211-240