Fatigue Fracture Characteristics by Corrosion Degradation of 12Cr Alloy Steel
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Fatigue Fracture Characteristics by Corrosion Degradation of 12Cr Alloy Steel
Jo, Seon-Yeong; Kim, Cheol-Han; Bae, Dong-Ho;
  PDF(new window)
In order to investigate the fatigue fracture characteristics by corrosion degradation of 12Cr alloy steel, both the fatigue characteristics in air of them artificially degraded during long period and the corrosion fatigue characteristics were experimentally evaluated in various environments which were determined from electro-chemical polarization tests. And also, their fracture mechanisms were analyzed and compared, fractographyically. From their results, the fracture mechanical characteristics of it artificially degraded during long period in the distilled water, 3.5 wt.% NaCl solution and 12.7wt.%(1M) NaSOsolution of 25, 60 and 90 did not show distinguishable difference comparing with non-corroded one in regardless of temperature and degradation period. It means that degradation of the material by just surface corrosion does not remarkably affect to fatigue crack growth. On the other hand, the crack growth rates by corrosion fatigue increased due to activity increase of corrosive factors such as OH(sub)-,Cl(sup)- and SO(sup)- at the crack tip with temperature increase. Therefore, the crack growth rates by corrosion fatigue were more faster than that in air of the artificially degraded specimen due to the such difference of crack growth mechanism.
Corrosion Degradation;12Cr Alloy Steel;Fatigue;Corrosion Fatigue;Stress Intensity Factor Range;Crack Growth Rate;SEM Fractography;
 Cited by
1984, 機械.構造物の破損事例と解析技術, 日本機械學會, pp. 286-290

1985, 腐植と破壞, 日本機械學會編, pp. 71-74

1980, 屬の割れ.破壞總合資料集, 日本金屬の割れ.破壞對策硏究會, pp. 521-526

1987, 材料强度問題の最近の話題, 日本機械學會, pp. 114-119

Evert D. D., 1997, 'Corrosion Atlas,' Elsevier, 3rd ed., p. 71, p. 300, p. 313

조선영, 2000, '터빈블레이드 재료의 부식열화에 의한 파괴특성 평가.' 박사학위 논문

ASTM G5, 1987, 'Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements,' Annual Book of ASTM standards, pp. 73 -76

조선영, 김철한, 류승우, 김효진, 배동호, 2000, 'Turbine Blade재료의 부식민감성과 부식피로특성에 관한 연구,' 대한기계학회 논문집 A권, 제24권 제3호, pp. 603-612

1995, 'Standard Test Method for Measurment of Fatigue Crack Growth Rates,' ASTM E647-95, pp. 578-614

1993, 'Guideline for Electric Potential Difference Determination of Crack Size,' ASTM E647, pp. 695 -700

小寺澤良, 1983, 'フラクトグラフイとその應用,' 日刊工業新聞社, pp. 31-76

R. P. Wei and J. D. Landes, 1969, 'ASTM Material Research Standard 9-7,' p. 25