High-Temperature Corrosion of T92 Steel in N2/H2O/H2S-Mixed Gas
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Corrosion Science and Technology
  • Volume 15, Issue 3,  2016, pp.125-128
  • Publisher : The Corrosion Science Society of Korea
  • DOI : 10.14773/cst.2016.15.3.125
 Title & Authors
High-Temperature Corrosion of T92 Steel in N2/H2O/H2S-Mixed Gas
Shi, Yuke; Kim, Min Jung; Park, Soon Yong; Abro, M. Ali; Yadav, Poonam; Lee, Dong Bok;
  PDF(new window)
 Abstract
The ASTM T92 steel was corroded at and at 1 atm of gas. The formed scales were thick and fragile. They consisted primarily of the outer FeS scale and the inner (FeS, )-mixed scale containing a small amount of the scale. This indicated that corrosion occurred mainly via sulfidation rather than oxidation due to the gas. Since FeS was present throughout the whole scale, T92 steel was non-protective, displaying high corrosion rates.
 Keywords
Fe-Cr alloys;corrosion;sulfidation;;
 Language
English
 Cited by
 References
1.
S. Mrowec and K. Przybylski, Oxid. Met., 23, 3 (1985).

2.
S. Mrowec, T. Walec and T. Werber, Oxid. Met., 1, 1 (1969). crossref(new window)

3.
S. Mrowec and M. Wedrychowska, Oxid. Met., 13, 6 (1979).

4.
H. J. Lee, H. M. Kim and C. H. Jang, Corros. Sci. Tech., 13, 2 (2014).

5.
T. D. Nguyen, J. Zhang and D. J. Young. Corros. Sci. Tech., 14, 3 (2015).

6.
M. Danielewski, S. Mrowec and A. Stolosa, Oxid. Met., 17, 1 (1982). crossref(new window)

7.
M. Schulte, A. Rahmel and M. Schutze, Oxid. Met., 49, 1 (1998). crossref(new window)