The Characteristic Study of Plasma Electrolytic Oxidation in AZ31B Magnesium Alloy
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
The Characteristic Study of Plasma Electrolytic Oxidation in AZ31B Magnesium Alloy
Yu, Jae-Yong; Choi, Soon-Don; Yu, Jae-In; Yun, Jae-Gon; Ko, Hoon; Jung, Yeon-Jae;
  PDF(new window)
In this study low voltage Plasma Electrolytic Oxidation (PEO) was utilized to eliminate high voltage PEO drawbacks such as high cost, dimensional deformation and porosity. Low voltage PEO produces a thin coating which causes low corrosion resistance. In order to solve such problem, 0.1~0.6M pyrophosphates were added in a bath containing 1.4M NaOH, and 0.35M Na2SiO3. 70 V PEO was conducted at 25℃ for 3 minutes. Chemical composition, morphology and corrosion resistance of the anodized coating were analyzed. The anodized film was composed of MgO, Mg2SiO4, and Mg2O7P2. The morphology of film showed appropriately dense structure and low porosity in the anodized layers. It is found that low voltage Plasma Electrolytic Oxidation in cooperation with phosphating treatment can provide a good corrosion protection for the AZ31B magnesium alloy.
Magnesium;AZ31B;Plasma electrolytic oxidation;Pyrophosphate;Low voltage;
 Cited by
Y. Kojima, Mater. Sci. Forum, 3, pp. 350-354, 2000.

J. Jeon, S. Lee, B. Kim, B. Park, Y. Park, and I. Park, J. Kor. Inst. Met. Mater., 46, pp. 304-310, 2008.

H. Hoche, C. Rosenkranz, A. Delp, M.M. Lohrengel, E. Broszeit, and C. Berger, Surf. Coat. Technol. 193, pp. 178-182, 2005. crossref(new window)

Y.F. Jiang, X.W. Guo, Y.H. Wei, and C.Q. Zhai, W.J. Ding, Synthetic Metals 139, pp.335-342, 2003. crossref(new window)

K. Brunelli, M. Dabala, I. Calliari, and M. Magrini, Corros. Sci. 47, pp. 989-995, 2005. crossref(new window)

G. Ballerini, U. Bardi, R. bignucolo, and G. Ceraolo, Corros. Sci. 47, pp. 2173-2176, 2005.

Z. Shi, G. Song, and A. Atrens, Corros. Sci. 47, pp. 2760-2768, 2005. crossref(new window)

B.S. You, W.W. Park, and I.S. Chung., Scr. Mater. 42, pp. 1089-1095, 2000. crossref(new window)

E. A. Carter, T. F. Barton, and G. A. Wright, J. Surf. Treatments, pp. 169-175. 1999.

J.E. Gray and B. Luan, J. Alloy Compd. 336, pp. 88-93, 2002. crossref(new window)

Y.Q. Wang, M.Y. Zhang, and K. Wu, Mater. Lett. 59, pp. 1727-1732, 2005. crossref(new window)

L.R. Krishna, K.R.C. Somaraju, and G. Sundararajan, Surf. Coat. Technol. 163, pp. 484-488, 2003.

X. Nie, A. Leyland, H.W. Song, A.L. Yerokhin, S.J. Dowey, and A. Matthews, Surf. Coat. Technol. 116, pp. 1055-1062, 1999.

P.A. Dearnley, J. Gummersbach, H. Weiss, A.A. Ogwu, and T.J. Davies,Wear 225, pp. 127-132, 1999.

H.F. Guo, M.Z. An, S. Xu, and H.B. Huo, Thin Solid Films 485, pp. 53-65, 2005. crossref(new window)

J. Liang, B.G. Guo, J. Tian, H.W. Liu, J.F. Zhou, W.M. Liu, and T. Xu, Surf. Coat. Technol. 199, pp. 121-132, 2005. crossref(new window)

Y.Z. Lu, Q.D. Wang, X.Q. Zeng, W.J. Ding, C.Q. Zhai, and Y.P. Zhu, Mater. Sci. Eng. A 278, pp. 66-78, 2000. crossref(new window)

I.P. Moreno, T.K. Nandy, J.W. Jones, J.E. Allison, T.M. Pollock, Scr. Mater. 48, pp. 1029-1035, 2003. crossref(new window)

H. Duan, C. Yan, and F. Wang, Electrochimica Acta 52, pp. 5002-5009, 2007. crossref(new window)

V. Brass, S. Xia, R. Yue, G. Richard, and Rateick Jr., J. Electrochem. Soc., 151, 2004.

H. F. Guo, M. Z. An, H. B. Huo, S. Xu, and L. J. Wu, Appl. Surf. Sci., 252, pp. 7911-7923, 2006. crossref(new window)

Myung-Hwan Kim, Man-sig Lee, Sam-Tag Kwag and Myung-Jun Moon, J. Kor. Inst. Surf. Eng., 44-3, pp. 82-88, 2003.

A.L. Yerokhin, Surface and Coatings Technology 122, pp. 73-93, 1999. crossref(new window)

R. O. Hussein, D. O. Northwood, and X. Nie, J. Vac. Sci. Technol. 28, pp.766-769, 2010. crossref(new window)

J.W. Schultze, M.M. Lohrengel, Electrochimica Acta 45, pp. 2499-2513, 2000. crossref(new window)

M. Stern M, and A.L. Gery. J. Elcetrochem. Soc, pp. 56-63, 1957.