Electrochemical Corrosion Behavior of Duplex Stainless SteelAISI 2205 in Ethylene Glycol-Water Mixture in the Presence of50 W/V % LiBr
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Electrochemical Corrosion Behavior of Duplex Stainless SteelAISI 2205 in Ethylene Glycol-Water Mixture in the Presence of50 W/V % LiBr
Goodarzi, A.; Danaee, I.; Eskandari, H.; Nikmanesh, S.;
  PDF(new window)
 Abstract
The corrosion behavior of duplex stainless steel AISI 2205 was investigated in ethylene glycol-water mixture in the presence of 50 W/V % LiBr at different concentrations and different temperatures. Cyclic polarization, impedance measurements and Mott-Schottky analysis were used to study the corrosion behavior the semi conductive properties of the passive films. The results showed that with increasing in the ethylene glycol concentration to 10 V/V%, the corrosion rate of the steel alloy substrate increased. In higher concentrations of ethylene glycol, corrosion current of steel decreased. The results of scanning electron microscopy of electrode surface confirmed the electrochemical tests. Electrochemical experiment showed that duplex steel was stable for pitting corrosion in this environment. The increase in the ethylene glycol concentration led to increasing the susceptibility to pitting corrosion. The corrosion current increased as the temperature rise and also pitting potentials and repassivation potentials shifted towards the less positive values as the temperature increased. According to Mott-Schottky analysis, passive films of stainless steel at the different temperatures showed both n-type and p-type semiconductor behavior in different potential.
 Keywords
Duplex stainless steel;Corrosion;Ethylene glycol;Impedance;Mott-Schottky;
 Language
English
 Cited by
 References
1.
R. Sánchez-Tovar, M.T. Montañés and J. García-Antón, Corros. Sci., 68, 91 (2013). crossref(new window)

2.
E. Sarmiento, J. Uruchurtu, J. G. González-Rodriguez, C. Menchaca and O. Sarmiento, Corrosion, 67, 105004 (2011). crossref(new window)

3.
E. Samiento-Bustos, J. G. González Rodriguez, J. Uruchurtu, G. Dominguez-Patiño and V. M. Salinas-Bravo, Corros. Sci., 50, 2296 (2008). crossref(new window)

4.
A. I. Muñoz, J. G. Antón, S. L. Nuévalos, J. L. Guiñón and V. P. Herranz, Corros. Sci., 46, 2955 (2004). crossref(new window)

5.
I. Danaee, M. N. Khomami and A. A. Attar, Mater. Chem. Phys. 135, 658 (2012). crossref(new window)

6.
E. Samiento-Bustos, J. G. González-Rodriguez, J. Uruchurtu and V. M. Salinas-Bravo, Corros. Sci., 51, 1107 (2009). crossref(new window)

7.
A. Ehsani, R. Moshrefi and M. Ahmadi, J. Electrochem. Sci. Technol., 6, 7 (2015). crossref(new window)

8.
E. J. Kim, S. J. Park, J. H. Heo and H. C. Shin, J. Electrochem. Sci. Technol., 1, 112 (2010). crossref(new window)

9.
Z. Ahmadian, I. Danaee and M. A. Golozar, Materials Testing, 55, 294 (2013). crossref(new window)

10.
K. V. Rybalka, V. S. Shaldaev, L. A. Beketaeva, A. N. Malofeeva and A. D. Davydov, Russ. J. Electrochem., 46, 196 (2010). crossref(new window)

11.
I. Danaee, J. Electroanal. Chem., 662, 415 (2011). crossref(new window)

12.
J. R. Macdonald, Solid State Ion., 13, 147 (1984). crossref(new window)

13.
E. Guilminot, F. Dalard and C. Degrigny, Corros. Sci., 44, 2199 (2002). crossref(new window)

14.
Z. Ahmadian, I. Danaee and M. A. Golozar, Arch. Metall. Mater., 59, 25 (2014).

15.
M. Naghizadeh, D. Nakhaie, M. Zakeri and M. H. Moayed, Corros. Sci., 94, 420 (2015). crossref(new window)

16.
H. Jafari, I. Danaee, H. Eskandari and M. RashvandAvei, Ind. Eng. Chem. Res., 52, 6617 (2013). crossref(new window)

17.
S. RameshKumar, I. Danaee, M. RashvandAvei and M. Vijayan, J. Mol. Liq., 212, 168 (2015). crossref(new window)

18.
T. Osaka, H. Nara, D. Mukoyama and T. Yokoshima, J. Electrochem. Sci. Technol., 4, 157 (2013). crossref(new window)

19.
F. Jamali, I. Danaee and D. Zaarei, Mater. Corros., 66, 459 (2015). crossref(new window)

20.
I. Danaee and M. N. Khomami, Material Wiss. Werkst., 43, 942 (2012). crossref(new window)

21.
M. Gholami, I. Danaee, M. H. Maddahy and M. RashvandAvei, Ind. Eng. Chem. Res., 52, 14875 (2013). crossref(new window)

22.
K. R. Ansari and M.A. Quraishi, J. Ind. Eng. Chem. 20, 2819 (2014). crossref(new window)

23.
H. Jafari, I. Danaee, H. Eskandari and M. RashvandAvei, J. Mater. Sci. Technol., 30, 239 (2014). crossref(new window)

24.
I. Danaee, M. Niknejad Khomami and A. A. Attar, J. Mater. Sci. Technol., 29, 89 (2013). crossref(new window)

25.
M. BenSalah, R. Sabot, E. Triki, L. Dhouibi, Ph. Refait and M. Jeannin, Corros. Sci., 86, 61 (2014). crossref(new window)

26.
M. D. Krotova, Yu. V. Pleskov, A. A. Khomich, V. G. Ralchenko, D. N. Sovyk and V. A. Kazakov, Russ. J. Electrochem., 50, 101 (2014). crossref(new window)

27.
F. La Mantia, H. Habazaki, M. Santamaria, F. Di Quarto, Russ. J. Electrochem., 46, 1306 (2010). crossref(new window)

28.
J. Ding, L. Zhang, M. Lu, J. Wang, Z. Wen and W. Hao, Appl. Surf. Sci., 289, 33 (2014). crossref(new window)

29.
A. Fattah-alhosseini and S. Vafaeian, J. Alloy Comp., 639, 301 (2015). crossref(new window)

30.
M. Yazýcý, O. Çomaklý, T. Yetim, A. F. Yetim and A. Çelik, Surf. Coat. Technol., 261, 181 (2015). crossref(new window)

31.
H. Luo, C. F. Dong, X. G. Li and K. Xiao, Electrochim. Acta, 64, 211 (2012). crossref(new window)

32.
R. M. Fernández-Domene, E. Blasco-Tamarit, D.M. García-García and J. García-Antón, Thin Solid Films, 558, 252 (2014). crossref(new window)

33.
R. M. Fernández-Domene, E. Blasco-Tamarit, D. M. García-García and J. García-Antón, Electrochim. Acta, 95, 1 (2013). crossref(new window)