The Effect of Anodizing on the Electrical Properties of ZrO2 Coated Al Foil for High Voltage Capacitor
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
The Effect of Anodizing on the Electrical Properties of ZrO2 Coated Al Foil for High Voltage Capacitor
Chen, Fei; Park, Sang-Shik;
  PDF(new window)
 Abstract
and Al-Zr composite oxide film was prepared by vacuum assisted sol-gel dip coating method and anodizing. films annealed above have tetragonal structure. layers inside etch pits were successfully coated from the sol. The double layer structures of samples were obtained after being anodized at 100 V to 600 V. From the TEM images, it was found that the outer layer was , the inner layer was multi-layer of , Al-Zr composite oxide and Al hydrate. The capacitance of coated foil exhibited about 28.3% higher than that of non-coating foil after being anodized at 100 V. The high capacitance of coated foils anodized at 100 V can be attributed to the relatively high percentage of inner layer in total thickness. The electrical properties, such as withstanding voltage and leakage current of coated and non-coated Al foils showed similar values. From the results, and Al-Zr composite oxide is promising to be used as the partial dielectric of high voltage capacitor to increase the capacitance.
 Keywords
Anodizing;Sol-gel coating; film;Electrolytic capacitor;Capacitance;
 Language
English
 Cited by
 References
1.
R. S. Alwitt, H. Uchi, T. R. Beck, and R. C. Alkire, J. Electrochem. Soc. 131, 13 (1997).

2.
H. Takahashi, and M. Nagayama, Electrochim. Acta 23, 279 (1978). crossref(new window)

3.
L. Yao, J. Liu, M. Yu, S. Li, and H. Wu, Trans. Nonferrous Met. Soc. 20, 825 (2010). crossref(new window)

4.
S. Park, and B. Lee, J. Electroceram. 13, 111 (2004). crossref(new window)

5.
K. Watanabe, M. Sakairi, H. Takahashi, K. Takahiro, S. Nagata, and S. Hirai, J. Electrochem. Soc. 148, B473 (2001). crossref(new window)

6.
Y. Xu, Ceram. Int. 30, 1741 (2004). crossref(new window)

7.
X. Du, and Y. Xu, Surf. Coat. Technol. 202, 1923 (2008). crossref(new window)

8.
J. Liu, Q. Guo, M. Yu, S. Li, and L. Yao, ECS J. Solid State Sci. Technol. 2(3), N55 (2013).

9.
D. K. Fork, and D. B. Fenner, Appl. Phys. Lett. 57, 1137 (1990). crossref(new window)

10.
R. H. French, S. J. Glass, F. S. Ohuchi, Y. N. Xu, and W. Y. Ching, Phys. Rev. 49, 5133 (1994). crossref(new window)

11.
M. Shikanai, M. Sakairi, H.Takahashi, and M. Seo, J. Electrochem. Soc. 144(8), 2756 (1997). crossref(new window)

12.
Z. Feng, J. Chen, R. Zhang, and N. Zhao, Ceram. Int. 38, 3057 (2012). crossref(new window)

13.
K. Watanabe, M. Sakairi, H. Takahashi, S. Hirai, and S. Yamaguchi, J. Electroanal. Chem. 473, 250 (1999). crossref(new window)

14.
F. Chen, and S. S. Park, Sol-gel coating of $ZrO_2$ film in aluminum etch pit and anodizing properties, Kor. J. Mater. Res. 24(5), 259 (2014). crossref(new window)

15.
T. Ivanova, A. Harizanova, T. Koutzarova, N. Krins, and B. Vertruyen, Mater. Sci. Eng. B. 165, 212 (2009). crossref(new window)

16.
Y. H. Wang, J. Yang, and J. Z. Wang, Ceram. Int. 34, 1285 (2008). crossref(new window)

17.
T. Kudo and R. S. Alwitt, Electrochim. Acta 23, 341 (1978). crossref(new window)

18.
J. Chang, C. Liao, C. Chen, and W. Tsai, J. Electrochem. Soc. 150(6), B266 (2003). crossref(new window)

19.
J. Chang, C. Lin, C. Liao, C. Chen, and W. Tsai, J. Electrochem. Soc. 151(3), B188 (2004). crossref(new window)

20.
J. Chen, Z. Feng, M. Jiang, and B. Yang, J. Electroanal. Chem. 590, 26 (2006). crossref(new window)