Magnetic Field Dependence of Brownian Motion in Iron-oxide Nanoparticles
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Magnetic Field Dependence of Brownian Motion in Iron-oxide Nanoparticles
Jung, Eun Kyung; Yoon, Seok Soo; Kim, Dong Young;
  PDF(new window)
 Abstract
The ac magnetic susceptibility was measured in iron-oxide nanoparticles with average size of 26 nm, which were uniformly dispersed in organic solvent. The ac magnetic susceptibility measured under zero magnetic fields was well fitted with Debye relaxation model and the relaxation frequency was 370 Hz. The relaxation frequency of the nanoparticles coincided with relaxation time of the Brownian motion, which is due to the viscosity of the liquid medium in which magnetic nanoparticles dwell. The Brown relaxation frequencies were linearly increased with magnetic field.
 Keywords
nanoparticles;Ac magnetic susceptibility;brownian motion;relaxation frequency;
 Language
Korean
 Cited by
 References
1.
S. Laurent, D. Forge, M. Port, A. Roch, C. Robic, L. V. Elst, and R. N. Muller, Chem. Rev. 108, 2064 (2008). crossref(new window)

2.
N. K. Prasad, K. Rathinasamy, D. Panda, and D. Bahadur, J. Biomed. Mater. Part B: Appl. Biomater. 85B, 409 (2007).

3.
R. Hergt, S. Dutz, and M. Zeisberger, Nanotechnology 21, 015706 (2010). crossref(new window)

4.
I. Hilger, W. Andera, R. Hergt, R. Hiergeist, H. Schubert, and W. A. Kaiser, Radiology 218, 570 (2001). crossref(new window)

5.
J. Kliava and R. Berger, J. Magn. Magn. Mater. 205, 328 (1999). crossref(new window)

6.
Y. M. Jang and M. J. Hwang, J. Soc. Magn. Reson. Med. 7, 39 (2003).

7.
S. Vasseur, E. Duguet, J. Portier, G. Goglio, S. Mornet, E. Hadova, K. Knizek, M. Marysko, P. Veverka, and E. Pollert, J. Magn. Magn. Mater. 302, 315 (2006). crossref(new window)

8.
S. N. Ahmad, Y. Akin, and S. A. Shaheen, J. Appl. Phys. 97, 10Q902 (2005).

9.
J. Carrey, B. Mehdaoui, and M. Respaud, J. Appl. Phys. 109, 083921 (2011). crossref(new window)

10.
B. H. Erne, M. Claesson, S. Sacanna, M. Klokkenburg, E. Bakelaar, and B. W. M. Kuipers, J. Magn. Magn. Mater. 311, 145 (2007). crossref(new window)

11.
R. M. Ferguson, A. P. Khandhar, C. Jonasson, J. Blomgren, C. Johansson, and K. M. Krishnan, IEEE Trans Magn. 49, 3442 (2013).

12.
P. C. Fannin, L. C. Tannoudji, E. Bertrand, A. T. Giannitsis, C. M. Oireachtaigh, and J. Bibette, J. Magn. Magn. Mater. 303, 147 (2006). crossref(new window)

13.
S. Berkum, J. T. Dee, A. P. Philipse, and Ben H. Erne, Int. J. Mol. Sci. 14, 10162 (2013). crossref(new window)

14.
https://en.wikipedia.org/wiki/Dielectric#Debye_relaxation.

15.
G. F. Dionne, IEEE Trans. Magn. 39, 3121 (2003). crossref(new window)