A Study on Correlation Between Cyclic Drying-Wetting Accelerated Corrosion Test and Long-term Exposure Test
Park, Sang-Soon;
  PDF(new window)
There are various method for evaluating the durability life of concrete structures due to salt damage. The best way is to perform a corrosion test for a rebar embedded in concrete specimen was exposure to marine environment. However, this method has the disadvantage that it takes a long period of time. Also, accelerated corrosion test which was complemented complements the time-consuming weakness is limited to apply because it could not reveal a correlation between long-term exposure test. Accordingly, the purpose of this study is to derive a correlation coefficient between cycle drying-wetting accelerated corrosion test and long-term exposure test. Corrosion initiation time was measured in four types of concrete samples, i.e., two samples mixed with fly ash(FA) and blast furnace slag(BS), and the other two samples having two water/cement ratio(W/C
Accelerated corrosion test;Long-term exposure test;Corrosion of rebar;Cyclic drying-wetting condition;Correlation coefficient;
 Cited by
R.K. Dhir, M.R. Jones, and H.E.H. Ahmed.(1991), Concrete Durability : Estimation of Chloride Concentration During Design Life, Magazine of Concrete Research, 43(154), 37-44. crossref(new window)

A.V. Saetta, R.V. Scotta, and R.V. Vitaliani.(1993), Analysis of Chloride Diffusion into Partially Saturated Concrete, ACI Materials Journal, ACI, 90(47), 441-451.

M. Otieno, H. Beushausen and M. Alexander.(2014), Chloride-induced Corrosion of Steel in Cracked Concrete-Part II: Corrosion Rate Prediction Models, Cement and Concrete Research, 79, 386-394.

Oh, B.H., Lee, S.K., Lee, M.K., and Jung, S.H.(2005), Influence of Carbonation for Chloride Diffusion in Concrete, Journal of the Korea Concrete Institute, KCI, 17(2), 179-189. crossref(new window)

Bae, S.H., Lee, K.M., Kim, J.S., and Kim, Y.S.(2007), Estimation of Critical Chloride Content for Corrosion of Reinforcing Steel in Concrete by Accelerated Corrosion Tests, Journal of the Korean Society of Civil Engineers, KSCE, 27(5), 771-776.

Yang, S.K., Kim, D.S., Um, T.S., Lee, J.R., and Katsuya K.(2008), Study on the Critical Threshold Chloride Contents for Steel Corrosion in Concrete with Various Cement Contents, Journal of the Korea Concrete Institute, KCI, 20(4), 416-421.

KS F 2599-2.(2008), Standard test method for the accelerated corrosion of reinforced concrete (wet-drying cycles method), Korean Industrial Standards.

ASTM G 109-99a.(1999), Standard Test Method for Determining the Effects of Chemical Admixtures on the Corrosion of Embedded Steel Reinforcement in Concrete Exposed to Chloride Environment, The American Society for Testing and Materials.

Park, S.S. and Jeong, J.W.(2014), A Study of Accelerated Corrosion Test and Chloride Penetration Analysis with Artificial Seawater Immersion Condition, Journal of the Korea Institute for Structural Maintenance and Inspection, ,KSMI, 18(1), 93-99.

NT Build 492.(1999), Concrete, Mortar and Cement-base Repair Materials : Chloride Migration Coefficient From Non-Stead-State Migration Experiments, Nordtest Method.

ASTM C 876-91.(1999), Standard Test Method for Half-cell Potentials of Un-coated Reinforcing Steel in Concrete, The American Society for Testing and Materials.

Park S.S and Lee M.W.(2014), Study on the Correlation Between Long-term Exposure tests and Accelerated Corrosion tests by the Combined Damage of Salts, Corrosion Science and Technology, KCSS, 13(6), 214-223. crossref(new window)