Correlation Research of Dispersion Factors on the Silica Sol Prepared from Fumed Silica
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Correlation Research of Dispersion Factors on the Silica Sol Prepared from Fumed Silica
Park, Min-Gyeong; Kim, Hun; Lim, Hyung Mi; Choi, Jinsub; Kim, Dae Sung;
  PDF(new window)
To study the dispersion factors of silica sol prepared from fumed silica powder, we prepared silica sol under an aqueous system using a batch type bead mill. The dispersion properties of silica sol have a close relationship to dispersion factors such as pH, milling time and speed, the size and amount of zirconia beads, the solid content of fumed silica, and the shape and diameter of the milling impellers. Especially, the silica particles in silica sol were found to show dispersion stability on a pH value above 7, due to the electrostatic repulsion between the particles having a high zeta potential value. The shape and diameter of the impellers installed in the bead mill for the dispersion of fumed silica was very important in reducing the particle size of the aggregated silica. The median particle size () of silica sol obtained after milling was also optimized according to the variation of the size and amount of the zirconia beads that were used as the grinding medium, and according to the solid content of fumed silica. The dispersion properties of silica sol were investigated using zeta potential, turbiscan, particle size analyzer, and transmission electron microscopy.
fumed silica;silica sol;dispersion factor;bead mill;milling impeller;
 Cited by
T. Kashiwagi, J. W. Gilman, K. M. Butler, R. H. Harris, J. R. Shields and A. Asano, Fire Mater., 24, 277 (2000). crossref(new window)

Y. M. Ahn, J. Y. Yoon, C. W. Baek and Y. K. Kim, Wear, 257, 785 (2004). crossref(new window)

H. Barthel, M. Dreyer, T. Gottschalk-Gaudig, V. Litvinov and E. Nikitina, Macromol. Symp., 187, 573 (2002).

I. A. Rahman and V. Padavettan, Nanomaterials., 2012, 15 (2012).

H. C. Lee, J. H. Kim and Y. H. Chang, J. Korean Ind. Eng. Chem., 17, 386 (2006) (in Korean).

A. M. Buckley and M. Greenblatt, J. Chem. Educ., 71, 599 (1994). crossref(new window)

S. E. Pratisinis, Prog. Energy Combust. Sci., 24, 197 (1998). crossref(new window)

R. V. Lakshmi, T. Bharathidasan and B. J. Basu, Appl. Surf. Sci., 257, 10421 (2011). crossref(new window)

K. Chrissafis, K. M. Paraskevopoulos, G. Z. Papageorgiou and D. N. Bikiaris, J. Appl. Polym. Sci., 110, 1739 (2008). crossref(new window)

M. J. Park, J. W. Ahn and H. Kim, J. Korean Ceram. Soc., 38, 343 (2001) (in Korean).

J. H. Yu, S. H. Jung, G. P. Hong, J. S. Mun and J. B. Kang, J. Korean Ceram. Soc., 46, 24 (2009) (in Korean). crossref(new window)

H. K. Kang, H. C. Park and H. C. Park, J. Korean Ind. Eng. Chem., 8, 704 (1997) (in Korean).

H. S. Park, B. S. Cho, E. S. Yoo, J. B. Ahn and S. T. Noh, Appl. Chem. Eng., 22, 384 (2011) (in Korean).

H. M. Lim, J. H. Lee, J. H. Jeong, S. G. Oh and S. H. Lee, Eng., 2, 998 (2010). crossref(new window)

T. Takatsuka, T. Endo, Y. Jianguo, K. Yuminoki and N. Hashimoto, Chem. Pharm. Bull., 57, 1061 (2009). crossref(new window)

D. H. Lee, G. S. Cho, H. M. Lim, D. S. Kim, C. Y. Kim and S. H. Lee, J. Ceram. Process. Res., 14, 274 (2013).

A. Amiri, G. Oye and J. Sjoblom, Colloids Surf. A, 349, 43 (2009). crossref(new window)

G. R. Wiese and T. W. Healy, Trans. Faraday Soc., 66, 490 (1970). crossref(new window)

K. H. Hwang, J. H. Park and T. K. Yoon, J. Korean Ceram. Soc., 31, 337 (1994) (in Korean).

K. Lee, University physics for scientists and engineers, 182, Hanbitacademy, Seoul, (2011).