Effect of Al2O3-ZrO2 Composite Oxide Thickness on Electrical Properties of Etched Al Foil
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effect of Al2O3-ZrO2 Composite Oxide Thickness on Electrical Properties of Etched Al Foil
Chen, Fei; Park, Sang-Shik;
  PDF(new window)
To increase the capacitance of an Al electrolytic capacitor, the anodic oxide film, , was partly replaced by an (Al-Zr) composite film prepared by the vacuum infiltration method and anodization. The microstructure and composition of the prepared samples were investigated by scanning electron microscopy and transmission electron microscopy. The coated and anodized samples showed multi-layer structures, which consisted of an inner Al hydrate layer, a middle Al-Zr composite layer, and an outer layer. The thickness of the coating layer could go up to 220 nm when the etched Al foil was coated 8 times. The electrical properties of the samples, such as specific capacitance, leakage current, and withstanding voltages, were also characterized after anodization at 100 V and 600 V. The capacitances of samples with coating were 36.3% and 27.5% higher than those of samples without coating when anodized at 100 V and 600 V, respectively.
sol-gel;multi-layer film;anodization;capacitance;anodic oxide film;
 Cited by
R. S. Alwitt, H. Uchi, T. R. Beck and R. C. Alkire, J. Electrochem. Soc., 131, 13 (1984). crossref(new window)

H. Takahashi and M. Nagayama, Electrochim. Acta., 23, 279 (1978). crossref(new window)

C. T. Chen and G. A. Hutchins, J. Electrochem. Soc., 132, 1567 (1985). crossref(new window)

R. L. Chiu, P. H. Chang and C. H. Tung, Thin Solid Films, 260, 47 (1995). crossref(new window)

J. K. Chang, C. M. Lin, C. M. Liao, C. H. Chen, and W. T. Tsai, J. Electrochem. Soc., 151, B188 (2004). crossref(new window)

C. L. Ban, Y. D. He and X. Shao, Trans. Nonferrous Met. Soc. China, 21, 133 (2011). crossref(new window)

S. S. Park and B. T. Lee, J. Electroceram., 13, 111 (2004). crossref(new window)

M. Sunada, H. Takahashi, T. Kikuchi, M. Sakairi and S. Hirai, J. Solid State Electrochem., 11, 1375 (2007). crossref(new window)

Y. H. Wang, J. Yang and J. Z. Wang, Ceram. Int., 34, 1285 (2008). crossref(new window)

X. Du and Y. Xu, Surf. Coat. Technol., 202, 1923 (2008). crossref(new window)

J. Liu, Q. Guo, M. Yu, S. Li and L. Yao, ECS J. Solid state Sci. Technol., 2, N55 (2013).

F. Chen and S. S. Park, ECS J. Solid state Sci. Technol., 4, P293 (2015). crossref(new window)

H. Uchi, T. Kanno and R. S. Alwitt, J. Electrochem. Soc., 148, B17 (2001). crossref(new window)

R. S. Alwitt, C. K. Dyer and B. Noble, J. Electrochem. Soc., 129, 711 (1982). crossref(new window)