Influence of Mo Addition on High Temperature Deformation Behavior of L12 Type Ni3Al Intermetallics
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Influence of Mo Addition on High Temperature Deformation Behavior of L12 Type Ni3Al Intermetallics
Han, Chang-Suk; Jang, Tae-Soo;
  PDF(new window)
The high temperature deformation behavior of and single crystals that were oriented near <112> was investigated at low strain rates in the temperature range above the flow stress peak temperature. Three types of behavior were found under the present experimental conditions. In the relatively high strain rate region, the strain rate dependence of the flow stress is small, and the deformation may be controlled by the dislocation glide mainly on the {001} slip plane in both crystals. At low strain rates, the octahedral glide is still active in above the peak temperature, but the active slip system in changes from octahedral glide to cube glide at the peak temperature. These results suggest that the deformation rate controlling mechanism of is viscous glide of dislocations by the <110>{111} slip, whereas that of is a recovery process of dislocation climb in the substructures formed by the <110>{001} slip. The results of TEM observation show that the characteristics of dislocation structures are uniform distribution in and subboundary formation in . Activation energies for deformation in and were obtained in the low strain rate region. The values of the activation energy are 360 kJ/mol for and 300 kJ/mol for .
high temperature deformation;;strain rate;dislocation glide;slip;
 Cited by
C. S. Oh and C. S. Han, Korean J. Mater. Res., 22, 42 (2012). crossref(new window)

C. S. Han, K. W. Koo and D. C. Oh, Korean J. Mater. Res., 16, 241 (2006). crossref(new window)

S. U. An, S. C. Kim, O. D. Im, S. H. Kim, Y. H. Jin, J. S. Choe, J. H. Lee, S. J. Lee, D. L. Seo, T. H. Lee and M. Y. Heo, Korean J. Mater. Res., 8, 1165 (1998).

S. I. Rao, D. M. Dimiduk and T. A. Parthasarathy, Scripta Mater., 66, 410 (2012). crossref(new window)

J. R. Nicholls and R. D. Rawlings, J. Mater. Sci., 12, 2456 (1977). crossref(new window)

Y. Q. Sun and N. Yang, Intermetallics, 9, 979 (2001). crossref(new window)

T. Suzuki, Y. Mishima and S. Miura, ISIJ Int., 29, 1 (1989). crossref(new window)

B. V. Petukhov, M. Bartsch and U. Messerschmidt, Appl. Phys., 9, 89 (2000).

J. N. Wang and T. G. Nieh, Scripta Metall. Mater., 33, 633 (1995). crossref(new window)

B. V. Petukhov, Crystallogr. Rep., 42, 161 (1997).

S. Takeuchi, Philos. Mag. A, 71, 1255 (1995). crossref(new window)

S. A. Sajjadi and S. Nategh, Mater. Sci. Eng. A, 307, 158 (2001). crossref(new window)

M. M. P. Janssen, Metall. Trans., 4, 1623 (1973).

K. Hoshino, S. J. Rothman and R. S. Averback, Acta Metall. Mater., 36, 1271 (1988). crossref(new window)

S. Frank, J. Rüsing and Chr. Herzig, Intermetallics, 4, 601 (1996). crossref(new window)