Properties of Dye Sensitized Solar Cells with Porous TiO2 Layers Using Polymethyl-Methacrylate Nano Beads
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Properties of Dye Sensitized Solar Cells with Porous TiO2 Layers Using Polymethyl-Methacrylate Nano Beads
Choi, Minkyoung; Noh, Yunyoung; Kim, Kwangbae; Song, Ohsung;
  PDF(new window)
We prepared polymethyl methacrylate (PMMA) beads with a particle size of 80 nm to improve the energy conversion efficiency (ECE) by increasing the effective surface area and the dye absorption ability of the working electrodes (WEs) in a dye sensitized solar cell (DSSC). We prepared the layer with PMMA beads of 0.0~1.0 wt%; then, finally, a DSSC with active area was obtained. Optical microscopy, transmission electron microscopy, field emission scanning electron microscopy, and atomic force microscopy were used to characterize the microstructure of the layer with PMMA. UV-VIS-NIR was used to determine the optical absorbance of the WEs with PMMA. A solar simulator and a potentiostat were used to determine the photovoltaic properties of the PMMA-added DSSC. Analysis of the microstructure showed that pores of 200 nm were formed by the decomposition of PMMA. Also, root mean square values linearly increased as more PMMA was added. The absorbance in the visible light regime was found to increase as the degree of PMMA dispersion increased. The ECE increased from 4.91% to 5.35% when the amount of PMMA beads added was increased from 0.0 to 0.4 wt%. However, the ECE decreased when more than 0.6 wt% of PMMA was added. Thus, adding a proper amount of PMMA to the layer was determined to be an effective method for improving the ECE of a DSSC.
polymethyl methacrylate;nano beads; layer;energy conversion efficiency;dye sensitized solar cell;
 Cited by
B. O'Regan and M. Gratzel, Nature, 353, 737 (1991). crossref(new window)

K. Wongcharee, V. Meeyoo and S. Chavadej, Sol. Energy Mater. Sol. Cells, 91, 566 (2007). crossref(new window)

M. Gratzel, J. Photochem. Photobiol. C, 4, 145 (2003). crossref(new window)

M. A. Green, K. Emery, Y. Hishikawa, W. Warta and E. D. Dunlop, Prog. Photovolt. Res. Appl., 22, 701 (2014). crossref(new window)

A. Hagfeldt, G. Boshloo, L. Sun, L. Koo and H. Pettersson, Chem. Rev., 110, 6595 (2010). crossref(new window)

L. Li, S. Chen, C. Zu, Y. Zhao, N. G. Rudawski and K. J. Ziegler, ACS Appl. Mater. Interfaces, 6, 20978 (2014). crossref(new window)

M. Gratzel, Inorg. Chem., 44, 6841 (2005). crossref(new window)

S. Lee, J. H. Noh, H. S. Han, D. H. Kim, J. K. Lee, J. Y. Kim, H. S, Jung and K. S. Hong, J. Phys. Chem. C, 113, 7443 (2009).

Y. Yao, G. Li, S. Ciston, R. M. Lueptow and K. A. Gray, Environ. Sci. Technol., 42, 4952 (2008). crossref(new window)

N. G. Park, J. V. Lagemaat and A. J. Frank, J. Phys. Chem. B, 104, 8989 (2000).

J. Bisquert, F. F. Santiago, I. M. Sero, G. G. Belmonte and S. Kimenez, J. Phys. Chem. C, 113, 17278 (2009). crossref(new window)

H. Xu, X. Tao, D. T. Wang, Y. Z. Zheng and J. F. Chen, Electrochim. Acta, 55, 2280 (2010). crossref(new window)

A. Agarwala, M. Kevin, A. S. W. Wong, C. K. N. P, V. Thavasi and G. W. Ho, ACS Appl. Mater. Interfaces, 2, 1844 (2010). crossref(new window)

R. Pater, S. H. Ahn, W. S. Chi and J. H. Kin, Ionics, 18, 395 (2012). crossref(new window)

M. Ferriol, A. Gentilhomme, M. Cochez, N. Oget and J. L. Mieloszunski, Polym. Degrad. Stabil., 79, 271 (2003). crossref(new window)

S. T. Camli, F. Buyukserin, O. Balci and G. G. Budak, J. Colloid Interface Sci., 344, 528 (2010). crossref(new window)