Photoluminescence Property of Lu2Si2O7:Ce3+ Powder for Scintillator
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Photoluminescence Property of Lu2Si2O7:Ce3+ Powder for Scintillator
Kim, Kyung-Nam; Cao, Guozhong;
  PDF(new window)
In this paper, cerium doped lutetium pyrosilicate (LPS) powders with cerium content (0.05 and 0.07 mol%) were prepared by sol-gel process. The formation of lutetium pyrosilicate (LPS) phase was confirmed by XRD analysis for the powders heated at ; in these powders, a single phase of (LPS) was observed. Cerium doped lutetium pyrosilicate (LPS) powder was agglomerated and constituted of small spherical particles with diameters of about 300 nm. The photoluminescence spectra of the powders showed the characteristic of excitation and there was an emission spectrum for in the host of . The emission spectrum shows a broad band in the range of 350-525 nm; the broad wavelength on the right side of the spectra should be ascribed to the same 5d-4f transitions of , as in the case of cerium doped single crystals.
 Cited by
C. L. Melcher and J. S. Schweitzer, IEEE Trans. Nucl. Sci., 39, 502 (1992). crossref(new window)

D. Pauwels, N. Le Masson, B. Viana, A. Kahn Harari, E. V. D. van Loef, P. Dorenbos and C.W.E. van Eijk, IEEE Trans. Nucl. Sci., 47, 1787 (2000). crossref(new window)

L. Pidol, B. Viana, A. Bessiere, A. Galtayries, P. Dorenbos and B. Ferrand, Mater. Sci. Forum, 555, 371 (2007). crossref(new window)

K. Takagi and T. Fukazawa, Appl. Phys. Lett., 42, 43 (1983). crossref(new window)

C. Yan, G. Zhao, Y. Hang, L. Zhang and J. Xu, J. Cryst. Growth, 281, 411 (2005). crossref(new window)

C. Yan, G. Zhao, Y. Hang, L. Zhang and J. Xu, Mater. Lett., 60, 1960 (2006). crossref(new window)

H. Feng, D. Ding, H. Li, S. Lu, S. Pan, X. Chen and G. Ren, J. Alloy. Compd., 509, 3855 (2011). crossref(new window)

C. Mansuy, R. Mahiou and J. M. Nedelec, Chem. Mater., 15, 3242 (2003). crossref(new window)

C. Mansuy, C. Dujardin, R. Mahiou and J .M. Nedelec, Opt. Mater., 31, 1334 (2009). crossref(new window)

D. Boyer, G Bertrand-Chadeyron, R. Mahiou, L. Lou, A. Brioude and J. Mugnier, Opt. Mater., 16, 21 (2001). crossref(new window)

J. Sokolnicki and M. Guzik, Opt. Mater., 31, 826 (2009). crossref(new window)

D. Y. Shin, G. Cao and K. N. Kim, Curr. Appl. Phys., 11, S309 (2011). crossref(new window)

H. L. Li, X. J. Liu, R. J. Xie, Y. Zeng and L. P. Hung, J. Am. Ceram. Soc., 87, 2536 (2006).

C. Mansuy, J. M Nedelec, C. Dujardin and R. Mahiou, J. Sol-Gel Sci. Technol., 32, 253 (2004). crossref(new window)

Z. Zhu, B. Liu, C. Cheng, Y. Yi, H. Chen and M. Gu, Appl. Phys. Lett., 102, 071909 (2013). crossref(new window)