Effect of Solution Treatment and Short Time Aging on Mechanical Properties of Cast Ti-6Al-4V Alloy
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effect of Solution Treatment and Short Time Aging on Mechanical Properties of Cast Ti-6Al-4V Alloy
Oh, Seong-Tak; Woo, Kee-Do; Kwak, Seung-Mi; Kim, Jae-Hwang;
  PDF(new window)
The effect of heat treatment on the microstructure and mechanical properties of cast Ti-6%Al-4%V alloy was investigated. Heat treatment of cast Ti-6Al-4V alloy was conducted by solution treatment at for 30 min; this was followed by water quenching and then aging at for 1 to 1440 min. The highest hardness of the heat-treated specimens was obtained by solution treatment and subsequent aging for 5 min due to precipitates of fine that formed from retained phase. The tensile strength of this alloy increased without dramatic decrease of the ductility due to microstructural refinement resulting from the decomposition of martensite into fine and phases, and also due to the fine phase formed from the retained phase by aging treatment for 5 min. In addition, this strengthening might be caused by the transformation induced plasticity (TRIP) effect, which is a strain-induced martensite transformation from the retained phase during deformation, and which occurs even after aging treatment at for 5 min.
cast Ti-6Al-4V alloy;heat treatments;microstructure;hardness;tensile properties;
 Cited by
Effect of Retained β Phase on Mechanical Properties of Cast Ti-6Al-4V Alloy, MATERIALS TRANSACTIONS, 2017, 58, 8, 1145  crossref(new windwow)
G. Lutjering and J. C. Williams, 1st ed., p.7, Springer-Verlag, Berlin (2003).

T. Morita, K. Hatsuoka, T. Iizuka and K. Kawasaki, Mater. Trans., 46, 1681 (2005). crossref(new window)

R. G. Sherman and H. D. Kessler, Trans. ASM, 48, 657 (1956).

F. J. Gil, M. P. Ginebra, J. M. Manero and J. A. Planell, J. Alloys Compd., 329, 142 (2001). crossref(new window)

G. Welsch, G. Lutjering, K. Gazioglu and W. Bunk, Metall. Mater. Trans. A, 8A, 169 (1977).

H. Geng, S. He and T. Lei, Metall. Mater. Trans. A, 28A, 1809 (1997).

D. G. Lee and S. H. Lee, J. Mater. Sci., 40, 4077 (2005). crossref(new window)

M. A. Imam and C. M. Gilmore, Metall. Mater. Trans. A, 14A, 233 (1983).

M. T. Jovanovic, S. Tadic, S. Zec, Z. Miskovic and I. Bobic, Mater. Des., 27, 192 (2006). crossref(new window)

D. G. Lee, S. H. Lee and Y. T. Lee, Mater. Sci. Eng. A, 486, 19 (2008). crossref(new window)

C. G. Rhodes and N. E. Paton, Metall. Mater. Trans. A, 10A, 1753 (1979).

M. Marteleur, F. Sun, T. Gloriant, P. Vermaut, P. J. Jacques and F. Prima, Scr. Mater. 66, 749 (2012). crossref(new window)