Ultrasonic linear and nonlinear properties of fatigued aluminium 6061-T6 with voids
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Ultrasonic linear and nonlinear properties of fatigued aluminium 6061-T6 with voids
Kang, To; Song, Sung-Jin; Na, Jeong K.; Park, Jin-Ho;
  PDF(new window)
 Abstract
It is known that in aluminum 6061-T6, which is composed of and , void nucleation grows around of Al606-T6. In this work, growth of voids was checked by scanning a 6061-T6 specimen with SEM observation. The effects of dislocation damping, coherency strain and voids on ultrasonic attenuation and nonlinearity parameters were experimentally measured. It was observed that a nonlinearity parameter increases until 75 percent of fatigue life and decreases after that. From the results, the authors inferred that dislocation damping and coherency damping increase nonlinearity parameters and void nucleation decreases them as ultrasonic scattering increases with void. The application of nonlinearity parameters in estimating degradation of materials with complex microstructures through fatigue process, therefore, should be carefully considered.
 Keywords
Al6061-T6;voids;attenuation;nonlinearity parameter;
 Language
Korean
 Cited by
 References
1.
Wang, Q. G., "Microstructural effects on the tensile and fracture behavior of aluminum casting alloys A356/357", Metall Mater Trans A, 34(12), 2887-2899, (2003) crossref(new window)

2.
Ran, G., Zhou, J. E., Wang, Q. G., "Precipitates and tensile fracture mechanism in a sand cast A356 aluminum alloy", Jounral of Material Process Technology, 207(1-3), 46-52, (2008) crossref(new window)

3.
Agarwal, H., Gokhale, A. M., Graham, S., Horstemeyer M. F., "Void growth in 6061-aluminum alloy under triaxial stress state", Materials Science Engineering A, 341(1-2), 35-42, (2003) crossref(new window)

4.
Raj, R., Ashby, M. F., "Intergranular fracture at elevated temperature", Acta Metall, 23, 363-371, (1975)

5.
Joshi, N.R., Green Jr. R.E., "Ultrasonic detection of fatigue damage", Engineering Fracture Mechanics, 4(3), 577-583, (1972) crossref(new window)

6.
Hirao, M., Ogi, H., Suzuki, N., Ohtani, T., "Ultrasonic attenuation peak during fatigue of polycrystalline copper", Acta Materilia, 48(2), 517-524, (2000) crossref(new window)

7.
Cantrell, J.H., Yost, W.T., "Nonlniear ultrasconic characterization of fatigue micro structures", International Journal of Fatigue, 23(1), 487-490, (2001) crossref(new window)

8.
Kang, T., Kim, H. H., Song, S. J., Kim, H. J., "Characterization of fatigue damage of Al6061-T6 with ultrasound", NDT & E International., 52, pp. 51-56, (2012) crossref(new window)

9.
Truell, R., Elbaum, C., Chick, B.B., Ultrasonic methods in solid state physics, Academic Press, New York and London, (1969)

10.
Na, J. K., Yost, W. T., Cantrell, J. H., Kessel, G. L., "Effect of surface roughness and nonparallelism on the measruement of the acoustic nonliearity parameter in steam turbine blades", Review of Progress in Quantitative Nondestructive Evaluation, 19, 1417-1424

11.
Gauster, W.B., Breazeale M.A., "Detector for measurement of ultrasonic strain amplitudes in solid", 37(11), Review of Scientific Instruments, 1544-1548, (1966) crossref(new window)

12.
Kang, T., Na, J.K., Song, S.-J., Park, J.H., "Nonlinear acoustics for practical applications", Proc. of SPIE, 9473, 94370U1-94370U 2, (2015)

13.
Wang, Q. G., "Fatigue voids in structural Al-alloys under high-frequency cyclic loading", Journal of Materials Science, 39(1), 365-367, (2004) crossref(new window)

14.
Martin B.G., "Ultrasonic attenuation due to voids in fiber-reinforced plastics", NDT&E International, 9(5), 242-246, (1976) crossref(new window)