Reduction Leaching of Manganese Dioxide Ore Using Black Locust as Reductant in Sulfuric Acid Solution
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Korean Chemical Engineering Research
  • Volume 53, Issue 4,  2015, pp.509-516
  • Publisher : The Korean Institute of Chemical Engineers
  • DOI : 10.9713/kcer.2015.53.4.509
 Title & Authors
Reduction Leaching of Manganese Dioxide Ore Using Black Locust as Reductant in Sulfuric Acid Solution
Xue, Jianrong; Zhong, Hong; Wang, Shuai; Li, Changxin; Li, Jinzhong; Wu, Fangfang;
  PDF(new window)
 Abstract
We investigated the reduction leaching process of manganese dioxide ore using black locust as reductant in sulfuric acid solution. The effect of parameters on the leaching efficiency of manganese was the primary focus. Experimental results indicate that manganese leaching efficiency of 97.57% was achieved under the optimal conditions: weight ratio of black locust to manganese dioxide ore (WT) of 4:10, ore particle size of , , liquid to solid ratio (L/S) of 5:1, leaching time of 8 h, leaching temperature of 368 K and agitation rate of . The leaching rate of manganese, based on the shrinking core model, was found to be controlled by inner diffusion through the ash/inert layer composed of associated minerals. The activation energy of reductive leaching is . To conclude the reaction mechanism, XRD analysis of leached ore residue indicates manganese compounds disappear; FTIR characterization of leached residue of black locust sawdust shows hemicellulose and cellulose disappear after the leaching process.
 Keywords
Manganese Dioxide Ore;Black Locust Sawdust;Reduction Leaching;Reaction Mechanism;
 Language
English
 Cited by
 References
1.
Liu, Y. C., Lin, Q. Q., Li, L. F., Fu, J. G., Zhu, Z. S., Wang, C. Q. and Qian, D., Int. J. Min. Sci. Technol., 24, 567(2014). crossref(new window)

2.
Welham, N. J., Int. J. Miner. Process., 67, 187(2002). crossref(new window)

3.
Abbruzzese, C., Duarte, M. Y., Paponetti, B. and Toro, L., Miner. Eng., 3, 307(1990). crossref(new window)

4.
Naik, P. K., Sukla, L. B. and Das, S. C., Hydrometallurgy, 54, 217(2000). crossref(new window)

5.
Kanungo, S. B., Hydrometallurgy, 52, 313(1999). crossref(new window)

6.
Vu, H., Jandova, J., Lisa, K. and Vranka, F., Hydrometallurgy, 77, 147(2005). crossref(new window)

7.
Bafghi, M. S., Zakeri, A., Ghasemi, Z. and Adeli, M., Hydrometallurgy, 90, 207(2008). crossref(new window)

8.
Sahoo, R. N., Naik, P. K. and Das, C., Hydrometallurgy, 62, 157(2001). crossref(new window)

9.
Nayl, A. A., Ismai, I. M. and Aly, H. F., Int. J. Miner. Process., 100, 116(2011). crossref(new window)

10.
Tang, Q., Zhong, H., Wang, S., Li, J. Z. and Liu, G. Y., Trans. Nonferrous Met. Soc. China, 24, 861(2014). crossref(new window)

11.
Lasheen, T. A., Ei-Hazek, M. N., Helal, A. S. and Ei-Nagar, W., Int. J. Miner. Process., 92, 109(2009). crossref(new window)

12.
Su, H. F., Wen, Y. X., Wang, F., Sun, Y. Y. and Tong, Z. F., Hydrometallurgy, 93, 136(2008). crossref(new window)

13.
Su, H. F., Liu, H. K., Wang, F., Lv, X. Y. and Wen, Y. X., Chin. J. Chem. Eng., 18, 730(2010). crossref(new window)

14.
Cheng, Z., Zhu, G. C. and Zhao, Y. N., Hydrometallurgy, 96, 176(2009). crossref(new window)

15.
Tian, X. K., Wen, X. X., Yang, C., Liang, Y. J., Pi, Z. B. and Wang, Y. X., Hydrometallurgy, 100, 157(2010). crossref(new window)

16.
Yuksek, T., Catena, 90, 18(2012). crossref(new window)

17.
Tabari, M. and Salehi, A., J. Environ. Sci., 21, 1438(2009). crossref(new window)

18.
Mirko, G., Piero, O., Marco, C. C., Simone, F., Paolo, T., Francesco, C. and Andrea, B., US Patent, 20120104313A1(2012).

19.
Zhou, C., Wang, J. and Wang, N., Korean J. Chem. Eng., 30, 2037(2013). crossref(new window)

20.
Hariprasad, D., Dash, B., Ghosh, M. K. and Anand, S., Miner. Eng., 20, 1293(2007). crossref(new window)

21.
Baba, A. A. and Adekola, F. A., J. Saudi Chem. Soc., 16, 377(2012). crossref(new window)

22.
Ismail, A. A., Alie, E. A., Ibrahim, I. A. and Ahmed, M. S., Can. J. Chem. Eng., 82, 1296(2004).

23.
Senanayake, G., Hydrometallurgy, 73, 215(2004). crossref(new window)

24.
Park, K. H., Mohapatra, D., Nam, C. W. and Kim, H. I., Korean J. Chem. Eng., 24, 835(2007). crossref(new window)

25.
Tekin, T. and Bayramo lu, M., Hydrometallurgy, 32, 9(1993). crossref(new window)

26.
Chimentao, R. J., Lorente, E., Gispert-Guirado, F., Medina, F. and Lopez, F., Carbohydr. Polym., 111, 116(2014). crossref(new window)

27.
Sannigrahi, P., Ragauskas, A. J. and Miller, S. J., Bioenerg. Res., 1, 205(2008). crossref(new window)

28.
Pandey, K. K., J. Appl. Polym. Sci., 71, 1969(1999). crossref(new window)

29.
Abidi, N., Cabrales, L. and Haigler, C. H., Carbohydr. Polym., 100, 9(2014). crossref(new window)

30.
Stehfest, K., Toepel, J. and Wilhelm, Plant Physiol. Bioch., 43, 717(2005).

31.
Satyamurthy, P. and Vigneshwaran, N., Enzyme. Microb. Tech., 52, 20(2013). crossref(new window)

32.
Qian, Y. J., Zuo, C. J., Tan, J. and He, J. H., Energy, 32, 196(2007). crossref(new window)