Synthesis and Ozone Resistance Characteristic of Fluorine-containing modified Polyurea
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Korean Chemical Engineering Research
  • Volume 54, Issue 2,  2016, pp.175-180
  • Publisher : The Korean Institute of Chemical Engineers
  • DOI : 10.9713/kcer.2016.54.2.175
 Title & Authors
Synthesis and Ozone Resistance Characteristic of Fluorine-containing modified Polyurea
Kim, Sung Rae; Park, Ji Yong; Lee, Jong Dae;
  PDF(new window)
 Abstract
The fluorine-containing modified polyurea was synthesized using the PTPE-diol to improve the ozone-resistance. Three types (PFDIA-10C, PFDIA-20C, PFDIA-30C) of the modified polyurea containing the fluorine content from 10 wt% to 30 wt% were prepared. After ozone treatment on the prepared films, the weight loss of film was investigated and analyzed the film properties such as hardness, wear resistance, tensile stress, elongation, etc. Also, the film surfaces were observed by the optical microscopy after ozone-resistance tests at 10 ppm for 336 h. It was shown that the defects such as the cracking, the bleaching and the mass loss were reduced and the ozone-resistance of films were improved when the contents of PFPE-diol are more than 20 wt%. It was found that the intensity of O-H peak in PFDIA compounds confirmed by FT-IR was decreased as fluorine contents were increasing.
 Keywords
Perfluoropolyether Diol;Perfluorine Diisocyanate;Polyfluorineurea;Ozone-resistance;
 Language
Korean
 Cited by
 References
1.
Cooper, S. L. and Tobolsky, A. V., "Properties of Linear Elastomeric Polyurethanes," J. Appl. Polym. Sci., 10, 1837(1966). crossref(new window)

2.
Paul, C. J., Nair, M. G. R., Koshy, P. and Idage, B. B., "Recent Advances in Polymer Nanocomposites," J Appl Polym Sci., 74, 706(1999). crossref(new window)

3.
Van Bogart, J. W. V., Gibson, P. E. and Cooper, S. L., "Structureproperty Relationships in Polycaprolactone-polyurethanes," J. Polym. Sci: Polym. Phys. Ed., 21, 65(1983).

4.
Joo, J., Kim, H. S., Yoo, H. J., Lee, J. R. and Cheong, I. W., "Synthesis and Characterization of Epoxy Silane-modified Silica/Polyurethane-urea Nanocomposite Films," Korea Chem. Eng. Res., 50, 371(2012). crossref(new window)

5.
Kim, S. R., Lee, S. G., Yang, J. M. and Lee, J. D., "Preparation and Characterization of Hybrid Ozone Resistance Coating Film Using Carbon Nanotube," Polym. Soc. Korea, 38, 573(2014). crossref(new window)

6.
Nasar, A. S., Subramani, S. and Radhakrishnan, G., "Synthesis and Properties of Imidazole-blocked Diisocyanates," Polym Int., 48, 614(1999). crossref(new window)

7.
Sasaki, N., Yokoyama, T. and Tanaka, T., "Properties of Isocyanurate- type Crosslinked Polyurethanes," J. Polym. Sci. Polym. Chem. Ed., 11, 1765(1973). crossref(new window)

8.
Benrashid, R., Nelson, G. L., Linn, J. H. and Hanley, K. H., "Surface Characterization of Segmented Siloxane-urethane Block Copolymers," J. Appl. Polym. Sci., 49, 523(1993). crossref(new window)

9.
Hong, Y. T., Lee, J. H. and Kim, Y. S., "Fluoropolymer Films," Polym. Sci. Tech., 13, 724(2002).

10.
Bayer, O., "Das Di-Isocyanat-Polyadditionsverfahren (Polyurethane0)," Angew. Chem., A59, 257(1947).

11.
Barbeau, P., Gerard, J. F., Magny, B. and Pascault, J. P., "Effect of the Diisocyanate on the Structure and Properties of Polyurethane Acrylate Prepolymers," J. Polym. Sci: Part. B: Polym. Phys., 38, 2750(2000).

12.
Won, J. U., Jun, J. P. and Lee, B. J., "Functional Polyurethanes," Polym. Sci. Tech., 12, 724(2001).

13.
Karatas, S., Kizilkaya, C., Kayaman-Apohan, N. and Gungor, A., "Preparation and Characterization of Sol-Gel Derived UV Curable Organo-Silica-Titania Hybrid Coatings," Prog. Org. Coat., 60, 140 (2007). crossref(new window)

14.
Lee, C. H., Lee, S. G., Kim, S. R. and Lee, J. D., "Preparation of UV-curable Ozone Resistance Coating Solutions using Fluoromonomer," Korea Chem. Eng. Res., 50, 421(2012). crossref(new window)

15.
Gururaj, T., Subasri, R., Soma Raju, K. R. C. and Padmanabham, G., "Effect of Plasma Pretreatment on Adhesion and Mechanical Properties of UV-Curable Coatings on Plastics," Appl. Surf. Sci., 257, 15(2011).

16.
Won, J. U., Joen, J. P. and Lee, B. J., "Recent Development of Fluoropolymers," Polym. Sci. Tech., 14, 206(2003).

17.
Asif, A. and Shi, W., "Synthesis and Properties of UV Curable Waterborne Hyperbranched Aliphatic Polyester," Eur Polym J, 39, 933(2003). crossref(new window)

18.
Wei, H., Lu, Y., Shi, W., Yuan, H. and Chen, Y., "UV Curing Behavior of Methacrylated Hyperbranched Poly(amine-ester)s," J. Appl. Polym. Sci., 80, 51(2001). crossref(new window)