The Preparation and Property of Carbon Foams from Carbon Black Embedded Pitch Using PU Template
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Korean Chemical Engineering Research
  • Volume 54, Issue 2,  2016, pp.268-273
  • Publisher : The Korean Institute of Chemical Engineers
  • DOI : 10.9713/kcer.2016.54.2.268
 Title & Authors
The Preparation and Property of Carbon Foams from Carbon Black Embedded Pitch Using PU Template
Lee, Sangmin; Kim, Ji-Hyun; Jeong, Euigyung; Lee, Young-Seak;
  PDF(new window)
To improve mechanical strength of carbon foams, the carbon black (CB) added carbon foams were fabricated by impregnating different contents of carbon black (CB) and mesophase pitch using polyvinyl alcohol (PVA) solution into polyurethane foam and being followed by heat treatment. The cell wall-thicknesses of carbon foams were controlled by adding amounts of CB, and it was confirmed that the compressive strength of carbon foams was increased as increasing cell wall-thickness. The compressive strength had the highest value of with the highest bulk density of when adding 5 wt% CB in carbon foam. However, the thermal conductivity was decreased by adding CB in carbon foam. The results indicated that the thermal conductivities of carbon foams were reduced by increased interlayer spacing () with the addition of CB in carbon foams.
Pitch;Template;Carbon Foam;Carbon Black;Compressive Strength;
 Cited by
불소화 메조페이스 핏치로 제조된 그라파이트 폼의 물리/화학적 특성,김지현;김도영;이형익;이영석;

Korean Chemical Engineering Research, 2016. vol.54. 6, pp.830-837 crossref(new window)
Polyurethane Composite Foams in High-Performance Applications: A Review, Polymer-Plastics Technology and Engineering, 2018, 57, 4, 346  crossref(new windwow)
Kim, W. and Gong, H. J., "Properties of Epoxy Adhesive Modified with Siloxane-imide," Elastom. Compos., 43, 39-48(2008).

Roh, J. S., Ahn, J. S., Kim, B. J., Jeon, H. Y., Seo, S. K., Kim, S. H. and Lee, S. W., "Thermal Emissivity Changes as a Function of Degree of Flakes Alignment on the Graphite Surface," J. Korean Inst. Surf. Eng., 42, 95-101(2009). crossref(new window)

Im, H. and Kim, J. H., "Study on the Electrical Conductivity in Polysiloxane/Metal Composite Containing Metal Oxide," J. Korean Ind. Eng. Chem., 20, 307-312(2009).

Glazer, J., "Current Development in Electronic Packaging Materials," Jom. J. Miner. Met. Mater. Soc., 43(6), 7-7(1991).

Lei, S., Guo, Q., Shi, J. and Liu, L., "Prepartion of Phenolic-Based Carbon Foam with Controllable Pore Structure and High Compressive Strength," Carbon, 48, 2644-2673(2010). crossref(new window)

Kyung, J. J., "Preparation and Characterization of SiC Coated Graphite Foam," J. Korean Ceram. Soc., 44, 622-626(2007). crossref(new window)

Mehta, R., Anderson, D. P. and Hager, J. W., "Graphitic Open-Celled Carbon Foams: Processing and Characterization," Carbon, 41, 2159-2179(2001).

Klett, J., Hardy, R., Romine, E., Walls, C. and Burchell, T., "High-Thermal-Conductivity, Mesophase-Pitch-Derived Carbon Foams: Effect of Precursor on Structure and Properties," Carbon, 38, 953-973(2000). crossref(new window)

Yang, Y., Gupta, M. C., Dudley, K. L. and Lawrence, R. W., "Conductive Carbon Nanofiber-Polymer Foam Structures," Adv. Mater., 17, 1999-2003(2005). crossref(new window)

Bekyarova, E., Thostenson, E. T., Yu, A., Kim, H., Gao, J., Tang, J., Hahn, H. T., Chou, T, W., Itkis, M. E. and Haddon, R. C., "Multiscale Carbon Nanotube-Carbon Fiber Reinforcement for Advanced Epoxy Composites," Langmuir, 23, 3970-3974(2007). crossref(new window)

Shahil, K. M. F. and Balandin, A. A., "Graphene-Multilayer Graphene Nanocomposites as Highly Efficient Thermal Interface Materials," Nano Lett., 12, 861-867(2012). crossref(new window)

Nah, C. W., Kim, W. D. and Lee, S., "Effects of Carbon Black Content and Vulcanization Type on Cure Characterstics and Dynamic Mechanical Property of Styrene-Butadiene Rubber Compound," Korea Polym. J., 9, 157-163(2001).

Li, W. Q., Zhang, H. B., Xiong, X. and Xiao, F., "A Study of the Properties of Mesophase-Pitch-based Foam/Graphitized Carbon Black Composites," Mater. Sci. Eng.: A, 528(6), 2999-3002(2001).

Sedeh, M. M. and Khodadadi, J. M., "Thermal Conductivity Improvement of Phase Change Materials/Graphite Foam Composites," Carbon, 60, 117-128(2013). crossref(new window)

Ji, H., Zhang, L., Pettes, M. T., Li, H., Chen, S., Li, S., Piner, R. and Ruoff, R. S., "Ultrathin Graphite Foam: A Three-Dimensional Conductive Network for Battery Electrodes," Nano lett., 12, 2446-2451(2012). crossref(new window)

Ji, J., Ji, H., Zhang, L. L., Zhao, X., Bai, X., Fan, X., Zhang, F. and Ruoff, R. S., "Graphene-Encapsulated Si on Ultrathin-Graphite Foam as Anode for High Capacity Lithium-Ion Batteries," Adv. Mater., 25, 4673-4677(2013). crossref(new window)

Yadav, A., Kumar, R., Bhatia, G. and Verma, G. L., "Development of Mesophase Pitch Derived High Thermal Conductivity Graphite Foam Using a Template Method," Carbon, 49, 3622-3630(2011). crossref(new window)

Im, J. S., Kim, J. G. and Lee, Y. S., "Fluorination Effects of Carbon Black Additives for Electrical Properties and EMI Shielding Efficiency by Improved Dispersion and Adhesion," Carbon, 47, 2640-2647(2009). crossref(new window)

Moon, Y. E., Yun, J. M., Kim, H. I. and Lee, Y. S., "Effect of Graphite Oxide on Photodegradation Behavior of Poly(vinyl alcohol)/Graphite Oxide Composite Hydrogels," Carbon Lett., 12, 138-142(2011). crossref(new window)

Li, Z. Q., Lu, C. J., Xia, Z. P., Zhou, Y. and Luo, Z., "X-ray Diffraction Patterns of Graphite and Turbostratic Carbon," Carbon, 45, 1686-1695(2007). crossref(new window)

Park, S. J., Kim, K. S. and Hong, S. K., "Preparation and Characterization of Expaned Graphites by Wet Process," Korean Chem. Eng. Res., 41, 802-807(2003).

Cho, K. Y., Kim, K. J. and Riu, D. H., "Effect of Heating Rate and Pressute on Pore Growth of Porous Carbon Materials," Carbon Latt., 7, 271-276(2006).

Manocha, S. M., Patel, K. and Manocha, L. M., "Development of Carbon Foam from Pphenolic Resin via Template Route," Indian J. Eng. Mater. Sci., 17, 338-342(2010).