Synthesis of Alkoxy Modified Silicone Using Alkali Catalyst
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Elastomers and Composites
  • Volume 51, Issue 2,  2016, pp.99-105
  • Publisher : The Rubber Society of Korea
  • DOI : 10.7473/EC.2016.51.2.99
 Title & Authors
Synthesis of Alkoxy Modified Silicone Using Alkali Catalyst
Lee, Kangseok; Shim, Sang Eun;
  PDF(new window)
Alkoxy modified silicone (PAMS) was synthesized from hydroxyl-terminated polydimethylsiloxane (OH-PDMS) and vinyltrimethoxysilane (VTMO) under alkali catalyst (NaOH and KOH) at room temperature () via condensation polymerization. Then, the structural verification of the synthesized PAMS was confirmed using -NMR and FT-IR spectroscopy. The reaction rate of PAMSs was studied in terms of the concentration variation of alkali catalyst. The reaction rate increased with the concentration of alkali catalyst, but no correlation between conversion and concentration of alkali catalyst was observed.
alkoxy modified silicone (PAMS);hydroxyl-terminated polydimethylsiloxane (OH-PDMS);vinyltrimethoxysilane (VTMO);alkali catalyst;
 Cited by
P. E. Tomlins and L. Zou, "Surface insulation resistance and the properties of conformal coatings," National Physical Laboratory, Teddington, U.K., Rep. A-267 (2000).

J. J. Licari, Coating Materials for Electronic Applications, William Andrew, New York (2003).

A. Forsgren, Corrosion Control Through Organic Coatings, CRC Press, London (2006).

F. M. Lewis, "The science and technology of silicone rubber", Rubber Chem. Technol., 35, 1222 (1962). crossref(new window)

E. G. Rochow, "The direct synthesis of organosilicon compounds", J. Am. Chem. Soc., 67, 963 (1945). crossref(new window)

E. G. Rochow, An Introduction to the Chemistry of Silicones, Wiley, New York (1946).

E. G. Rochow, USA, 2,380,995, General Electric Company, (1945).

F. S. Kipping and L. L. Lloyd, "XLVII.-Organic derivatives of silicon. Triphenylsilicol and alkyloxysilicon chlorides", J. Chem. Soc. Trans., 79, 449 (1901). crossref(new window)

F. S. Kipping, "The Bakerian lecture. Organic derivatives of silicon", Proc. R. Soc. A, 159, 139 (1937). crossref(new window)

B. Momper, T. Wagner, U. Maschke, M. Ballauff, and E. W. Fischer, "Preparation and characterization of narrowly distributed poly(methylphenylsiloxane) by anionic polymerization of the cyclic trimers", Polym. Commun., 31, 186 (1990).

K. P. Sau, D. Khastgir, and T. K. Chaki, "Electrical conductivity of carbon black and carbon fibre filled silicone rubber composites", Die Angewandte Makromol. Chemie., 258, 11 (1998). crossref(new window)

General Electric Company, Polysiloxaneimides and their production, U. S. Patent 3,325,450 (1967).

A. Noshay and J. E. McGrath, Block Copolymer, Academic Press, New York (1977).

V. H. Kuckertz, "Siloxanmodifizierte polypyromellitimide", Makromol. Chem., 98, 101 (1966). crossref(new window)

S. Maudgal and S. Clair, "Preparation and characterization of siloxane-containing thermoplastic polymides", J. Adhes. Adhes., 4, 87 (1984). crossref(new window)

M. Itoh, K. Iwata, J. Ishikawa, and Y. Takenaka, "A heatresistant silicon-based polymer", Adv. Mater., 9, 1187 (1997). crossref(new window)

I. Yilgor, J. E. McGrath, J. S. Riffle, and L. L. Wickes, "Siloxane-urea segmented copolymers: I. Synthesis and characterization of model polymers from MDI and ${\alpha},{\omega}$-bis(aminopropyl) poly(dimethyl-siloxane)", Polym. Bull., 8, 535 (1982).

G. Kossmehl, W. Neumaun, and H. Schafer, "Polymeric and oligomeric dimethylsiloxanes with alcoholic groups and their conversions into polymers with dimethylsiloxane and urethane moieties", Makromol. Chem., 187, 1381 (1986). crossref(new window)

J. P. Pascault and Y. Camberein, "Quantitative determination of the phase segregation degree in a poly(dimethyl siloxane)-based urethane", Polym, Commun., 27, 230 (1986).