Evaluation of Bonding Strength of Larch Cross-Laminated Timber
Song, Yo-Jin; Hong, Soon-Il;
  PDF(new window)
The delamination along the annual ring on the cross-section of laminae and the bonding strength according to the tangential angle between laminae were evaluated for the production of 3-ply cross-laminated timber (CLT) using domestic larch. Since there is no standard for CLT in Korea, the production and test of specimens for bonding strength followed the standard procedure of "Structural glued laminated timber" (KS F 3021). The standard specifies to exclude any measurement from the cracks of timbers resulted from drying or knots during delamination test of the glued laminated timbers. However, the failure of cross-sectional tissues along the annual rings was observed near the glue-line of all specimens during the delamination test. Because this phenomenon can generate defects in the CLT that may be exposed to various temperatures and relative humidities after the actual construction, the delamination percentage was measured by including this wood failure. As a result, the delamination percentage of the CLT which had been combined in such a way that the annual rings of outer lamina were directed inward was the lowest, which was around 13%, regardless of the annual ring direction of the middle lamina. On the other hand, the delamination percentage of the CLT which had been combined in such a way that the annual rings of outer lamina were directed outward was the highest, which was around 26%. Furthermore, end-split occurred in the outer lamina during the drying process of the boiling delamination test, which affected the delamination percentage. Therefore, the soaking delamination test was found to be more appropriate for evaluating the delamination strength of CLT. The block shear strength of larch CLT was MPa on average, which was 46% lower than the block shear strength requirement (7.1 MPa) of the standard, but satisfied the criteria of the block shear strength (3.5 MPa) of the European Standard (prEN 16351: 2013).
cross-laminated timber;Larix kaempferi;delamination;block shear;rolling shear;wood failure;
 Cited by
Bergman, R. 2010. Drying and control of moisture content and dimensional changes. In Wood Handbook: Wood as an Engineering Material. General Technical Report FPL-190. USDA, Forest Service, Madison, WI, pp. 13-20.

Ceccotti, A. 2008. New technologies for construction of medium-rise buildings in seismic regions: the XLAM case, Structural Engineering International 18, pp. 156-165. crossref(new window)

Ceccotti, A., Yasumura, M., Minowa, C., Lauriola, MP., Follesa, M., Sandhaas, C. 2006. Which Seismic Behaviour Factor for Multi-Storey Buildings made of Cross-Laminated Wooden Panels?, Proceedings CIB W18 Meeting 2006, Florence, Italy.

Darby, H.J., Elmualim, A.A., Kelly, F. 2013. A case study to investigate the life cycle carbon emissions and carbon storage capacity of a cross laminated timber, multi-storey residential building, in: SB13 Implementing Sustainability-Barriers and Chances. Presented at the Sustainable Building, Munich, Germany.

Fellmoser, P., Blass, H.J. 2004. Influence of rolling shear modulus on strength and stiffness of structural bonded timber elements. CIB-W18 (37-6-5).

FPInnovations. 2011. CLT Hand Book cross-laminated timber.

Kim, H.K., Oh, J.K., Jeong, G.Y., Yeo, H.M., Lee, J.J. 2013. Shear performance of PUR adhesive in cross laminating of red pine. Journal of The Korean Wood Science and Technology 41(2): 158-163. crossref(new window)

Korea Forest Service. 2014. Statistical Yearbook of Forestry.

Korean Standards Association. 2008. Determination of resistance to soaking delamination for adhesive-bonded wood products. KS F 2160.

Korean Standards Association. 2013. Structural glued laminated timber. KS F 3021.

Mandegarian, A., Milev, S. Cross laminated timber. Civil 510-Term project University of British Columbia.

Mohammad, M., Gagnon, S., Douglas, B., Podesto, L. 2012. Introduction to cross laminated timber. A Journal of Contemporary Wood Engineering 22(2): 3-12.

Park, J.C., Shin, Y.J., Hong, S.I. 2009. Bonding performance of glulam reinforced with glass fiber-reinforced plastics. Journal of The Korean Wood Science and Technology 37(4); 357-363.

Pei. S., Berman, J., Dolan, D., van de Lindt, J., Ricles, J., Sause, R., Blomgren, H.E., Popovski, M., Rammer, D. 2014. Progress on the development of seismic resilient tall clt buildings in the pacific northwest. World Conference on Timber Engineering.

Per Wilinder. 2010. Fire resistance in cross-laminated timber. Bachelor thesis. Jonkoping University, Jonkoping, Sweden.

Popovski, M., Karacabeyli, E. 2012. Seismic Behaviour of Cross-Laminated Timber Structures. Proceedings of the 12th World Conference on Timber Engineering, Auckland, New Zealand.

prEN 16351:2013. Timber structures-Cross laminated timber-Requirements, CEN.

Robertson, A.B., Lam, F.F., Cole, R.J. 2012. A Comparative cradle-to-gate life cycle assessment of mid-rise office building construction alternatives: Laminated timber or reinforced concrete. Buildings 2(3): 245-270. crossref(new window)

van de Kuilen, J.-W., Ceccotti, A., Xia, Z., He, M., Li, S. 2010. Wood concrete skyscrapers. World Conference on Timber Engineering.