Corrosion Resistance Characteristics of Cold Rolled Steel by Cr-free Green Organic/Inorganic Hybrid Coating Solution
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Corrosion Resistance Characteristics of Cold Rolled Steel by Cr-free Green Organic/Inorganic Hybrid Coating Solution
Nam, Ki Woo; Kim, Jung Ryang; Choi, Chang Min;
  PDF(new window)
 Abstract
In the past, a very popular method for reducing the corrosion on zinc involved the use of chemical conversion layer coatings based on . However, there is an important problem with using chromium salts as a result of restrictive environmental protection legislation. This study investigated the optimum condition for galvanized steel using an organic/inorganic solution with a Ti composition. In the case of a fixed heat treatment time, the corrosion resistance values of LR-0727(1) and LR-0727(2) were improved as the heat treatment temperature increased, and the optimum minimum temperature decreased with the heat treatment time. At the optimum heat treatment condition of two coating solutions, the heat treatment time of the LR-0727(1) solution was shorter than LR-0727(2) for the same heat treatment temperature. LR-0727(1) coated specimens did not show desquamation, and all of the specimens showed a good adhesive property. In contrast, in the case of the LR-0727(2) coated specimens, desquamation arose. Therefore, the adhesive property of LR-0727(1) was superior to that of LR-0727(2). The pencil hardness had a 3H average for all of the coating solutions and heat treatment conditions. In the case of a corrosion resistance test with boiling water, the coated specimens of LR-0727(1) were discolored, but LR-0727(2) was not. Finally, LR-0727(1) was more moisture proof than LR-0727(2).
 Keywords
Organic/inorganic hybride solution;Corrosion resistance;Heat treatment time and temperature;
 Language
Korean
 Cited by
1.
열화한 STS316L에 대한 Cr-free 코팅액의 내식특성,이소영;김영수;정희록;안석환;남기우;

한국해양공학회지, 2015. vol.29. 6, pp.475-480 crossref(new window)
2.
자동차용 냉연강판 SPCC와 냉연고장력강판 SPCF590의 유/무기 하이브리드 용액에 의한 내식특성,이소영;이광호;정희록;남기우;

한국동력기계공학회지, 2015. vol.19. 5, pp.38-44 crossref(new window)
3.
Cr-free Si 변성 유/무기하이브리드 코팅액에 의한 열화된 STS310S 및 STS347H의 내식성,이소영;김영수;정희록;김귀식;남기우;

한국동력기계공학회지, 2015. vol.19. 6, pp.12-18 crossref(new window)
 References
1.
Seo, H.S., Moon, H.J., Kim, J.S., Ahn, S.H., Moon, C.K., Nam, K.W., 2010a. Corrosion Resistance According to the Heat Treatment Temperature of Cr-free Coating Solution on Zinc Coated Steel. Jornal of Ocean Engineering and Technology, 24(5), 60-66.

2.
Seo, H.S., Moon, H.J., Kim, J.S., Ahn, S.H., Moon, C.K., Nam, K.W., 2010b. Corrosion Resistance of Zinc Coating Steel Coated Cr-free Coating Solution According to the Teat Treatment Time. Jornal of Ocean Engineering and Technology, 24(5), 67-74.

3.
Seo, H.S., Moon, H.J., Kim, J.S., Ahn, S.H., Moon, C.K., Nam, K.W., 2010c. Corrosion Resistance of Galvanized Iron by Treating Modified Si Organic/Inorganic Hybrid Coating Solution. Jornal of Ocean Engineering and Technology, 25(1), 32-38.

4.
Zheludkevich, M.L., Miranda, S.I., Ferreira, M.G., 2005. Sol-gel Coatings for Corrosion Protection of Metals. Jornal of Mater. Chem, 15, 5099-5111. crossref(new window)