Low Heat Input Welding to Improve Impact Toughness of Multipass FCAW-S Weld Metal
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Low Heat Input Welding to Improve Impact Toughness of Multipass FCAW-S Weld Metal
Bang, Kook-soo; Park, Chan; Jeong, Ho-shin;
  PDF(new window)
 Abstract
Multipass self-shielded flux cored arc welding with different heat inputs (1.3–2.0 kJ/mm) was conducted to determine the effects of the heat input on the proportion of the reheated region, impact toughness, and diffusible hydrogen content in the weld metal. The reheated region showed twice the impact toughness of the as-deposited region because of its fine grained ferritic-pearlitic microstructure. With decreasing heat input, the proportion of the reheated region in the weld metal became higher, even if the depth of the region became shallower. Accordingly, the greatest impact toughness, 69 J at −40℃, was obtained for the lowest heat input welding, 1.3 kJ/mm. Irrespective of the heat input, little difference was observed in the hardness and diffusible hydrogen content in the weld metal. This result implies that low heat input welding with 1.3 kJ/mm can be performed to obtain a higher proportion of reheated region and thus greater impact toughness for the weld metal without the concern of hydrogen cracking.
 Keywords
FCAW-S;Reheating;Heat input;Impact toughness;Hydrogen content;
 Language
English
 Cited by
 References
1.
Boniszewski, T., 1992. Self-shielded Arc Welding. Abington Publishing, Cambridge, UK.

2.
Dorling, D.V., Rodrigues, P.E.L.B., Rogerson, J.H., 1978. A Comparative Study of the Effect of Welding Conditions on the Microstructure and Toughness of Self-shielded Arc and Manual Metal Arc Weld Metals. Proceedings on Trends in Steels and Consumables for Welding. London, UK, 351-359.

3.
Dorling, D.V., Rogerson, J.H., 1982. The Factors Which Control the Toughness of Self-shielded Flux Cored Arc Weld Deposits in Carbon-manganese Structural Steels. Proceedings on Fracture Toughness Testing, Cambridge, UK, 239-249

4.
Easterling, K., 1992. Introduction to the Physical Metallurgy of Welding. 2nd Edition, Butterworth-Heinemann Ltd, Oxford, UK.

5.
Eisenhuttenleute, V.D., 1992. Steel. Handbook for Materials Research and Engineering. Springer-Verlag, Berlin.

6.
Evans, G.M., 1985. The Effects of Heat Treatment on the Microstructure and Properties of C-Mn All Weld Metal Deposits. Metal Construction, 17(10), 676-682.

7.
Hesbrrok, W.G., 1993. Adopting Self-shielded Wire Welding for Shipbuilding. Welding & Metal Fabrication, 6, 223-224.

8.
Keeler T., 1981. Innershield Welding. Part 1: Development and Application. Metal Construction, 13(11), 667-673.

9.
Killing, R., 1980. Welding with Self-shielded Wires-The Mechanism of Shielding and Droplet Transfer. Metal Construction, 12(9), 433-436.

10.
Kotecki, D.J., Narayanan, B., 2005. Welding Consumable Developments in the Aftermath of the Northridge Earthquake. Welding in the World, 49(1/2), 42-46. crossref(new window)

11.
Pisarski, H.G., Jones, R.L., Harrison, P.L., 1987. Influence of Welding Procedure Variables on the Fracture Toughness of Welds made with Self-shielded Flux Cored Wire. Proceedings of 6th Intl Symposium on Offshore Mechanics & Arctic Eng. Houston, USA, 111-119.

12.
Rodgers, K.J., Lochhead, J.C., 1987. Self-shielded Flux Cored Arc Welding-The Route to Good Fracture Toughness. Welding Journal, 66(7), 49-59.