Evaluation of the Impact Shear Strength of Thermal Aged Lead-Free Solder Ball Joints
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Evaluation of the Impact Shear Strength of Thermal Aged Lead-Free Solder Ball Joints
Chung, Chin Sung; Kim, Ho Kyung;
  PDF(new window)
 Abstract
The present study investigates the impact shear strength of thermal aged Sn-3Ag-0.5Cu lead-free solder joints at impact speeds ranging from 0.5 m/s to 2.5 m/s. The specimens were thermal aged for 24, 100, 250 and 1000 hours at . The experimental results demonstrate that the shear strength of the solder joint decreases with an increase in the load speed and aging time. The shear strength of the solder joint aged averagely decreased by 43% with an increase in the strain rate. For the as-reflowed specimens, the mode II stress intensity factor () of interfacial IMC between Sn-3.0Ag-0.5Cu and a copper substrate also was found to decrease from to in the speed range tested here. The degradations in the shear strength and fracture toughness of the aged solder joints are mainly caused by the growth of IMC layers at the solder/substrate interface.
 Keywords
impact shear strength;lead-free solder joint;interface failure;thermal aging;fracture toughness;
 Language
Korean
 Cited by
 References
1.
E. H. Wong, S. K. W. Seah and V. P. W. Shim, "A Review of Board Level Solder Joints for Mobile Applications," Microelectronics Reliability, Vol. 48, pp. 1747-1758, 2008. crossref(new window)

2.
X. Hu, Y. Li, Y. Liu, Y. Liu and Z. Min, "Microstructure and Shear Strength of Sn37Pb/Cu Solder Joints Subjected to Isothermal Aging," Microelectronics Reliability, Vol. 54, pp. 1575-1582, 2014. crossref(new window)

3.
J. W. Yoon and S.B. Jung, "Reliability Studies of Sn-9Zn/Cu Solder Joints with Aging Treatment," J. Alloy. Compounds, Vol. 407, pp. 141-149, 2006. crossref(new window)

4.
S. M. Joo, T-. Y. Kim, W. Lim and H-. K. Kim, "Evaluation of the Joint Strength of Lead-free Solder Ball Joints at High Strain Rates", Jourmal of The Korean Society of Safety, Vol. 27, No. 6, pp. 7-13, 2012.

5.
H. D. Blair, T. Y. Pan, J. M. Nicholson, R. P. Cooper, S. W. Oh and A. R. Farah, "Manufacturing Concerns of the Electronic Industry Regarding Inter-metallic Compound Formation during the Soldering Stage," IEEE/CMPT Int. El. Mfg., Vol. 19, pp. 282-292, 1996.

6.
N. Mookam and K. Kanlayasiri, "Evolution of Intermetallic Compounds between Sn-0.3Ag-0.7Cu Low-silver Lead-free Solder and Cu Substrate during Thermal Aging," J. Mater. Sci. Technol. Vol. 28, No.1, pp. 53-59, 2012. crossref(new window)

7.
V. L. Nguyen and H. K. Kim, "Mechanical Properties of Lead-free Solder Joints under High-speed Shear Impact Loading," J. Electron. Mater., Vol. 43, pp. 4171-4178, 2014. crossref(new window)

8.
Y. H. Tian, C. J. Hang, C. Q. Wang, S. H. Yang and P.R. Lin, "Effects of Bump Size on Deformation and Fracture Behavior of Sn3.0Ag0.5Cu/Cu Solder Joints during Shear Testing," Mater. Sci. Eng. A, Vol. 529, pp. 468-478 , 2011. crossref(new window)

9.
J. W. Yoon and S. B. Jung, "Solder Joint Reliability Evaluation of Sn-Zn/Au/Ni/Cu Ball-grid-array Package during Aging," Mater. Sci. Eng. A, Vol. 452-453, pp. 46-54, 2007. crossref(new window)

10.
C. Y. Yu, W. Y. Chen and J.G. Duh, "Improving the Impact toughness of Sn-Ag-Cu/Cu-Zn Pb-free Solder Joints under High Speed Shear Testing," J. Alloy. Compound, Vol. 586, pp. 633-638, 2014. crossref(new window)