A Study on PTC/NTC Behavior of Fluorinated Carbon Black-filled HDPE Matrix Compounds
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
A Study on PTC/NTC Behavior of Fluorinated Carbon Black-filled HDPE Matrix Compounds
Soo-Jin Park; Su-Wan Song; Min-Kang Seo; Jae-Sup Shin; Kyuchul Kim;
  PDF(new window)
 Abstract
In this study, the fluorinated carbon blacks(CB) were used to reduce the negative temperature coefficient (NTC) phenomenon of the CB-filled high density polyethylene(HDPE) compounds in the fluorination pressure of 0.1-0.4 MPa. The changes in surface properties of the CB were investigated by using FT-IR, XPS and contact angle measurements. From the FT-IR results, the fluorinated CB showed the C-F absorption peak at 1400-1000 cm and the peak intensity was increased with increasing the fluorination pressure. Also, the analysis of XPS spectra of the fluorinated CB indicated that fluorine content was increased with increasing the fluorination pressure. Meanwhile, the surface free energy of the fluorinated CB was decreased with increasing the fluorination pressure. Consequently, the increase of fluorine contents on CB made a disappearance of NTC behaviors of CB/HDPE compounds, which was probably due to the reduction of CB reaggregation after melting point of the HDPE, resulting from decreasing the surface free energy of CB particles.
 Keywords
Negative Temperature Coefficient(NTC);Fluorination;Surface Free Energy;Reaggregation;
 Language
Korean
 Cited by
 References
1.
Norman, R.H. Conductive Rubber and Plastics; Elsevier:Amsterdam, 1970.

2.
Carmona, F.; Mouney, C. J. Mater. Sci. 1992, 27, 1322. crossref(new window)

3.
Harpaz, M.; Narkis, M. J. Polym. Sci. Part B: Polym. Phys. 2001, 39, 1415. crossref(new window)

4.
Doh, C. H.; Moon, S. I.; Kim, W. S. Bull. Korean Chem. Soc. 1996, 17, 861. crossref(new window)

5.
Donnet, J. B.; Bansal, R. C.; Wang, M. J. Carbon Black; Marcel Dekker: New York,1993. crossref(new window)

6.
Choi, S. S.; Kim, I. S. Bull. Korean Chem. Soc. 1998,19, 174. crossref(new window)

7.
Yang, G. Polym. Compo. 1997, 18, 484. crossref(new window)

8.
Park, S. J.; Kim, H. C.; Kim, H. Y. J. Colloid Interface Sci. 2002, 255, 145. crossref(new window)

9.
Sircar, A. K.; Wells, J. L. Polym. Eng. Sci. 1981, 21,809. crossref(new window)

10.
Wessling, B. Polym. Eng. Sci. 1991, 31, 1200. crossref(new window)

11.
Yacubowicz, J.; Narkis, M.; Benguigui, L. Polym. Eng. Sci. 1990, 30, 459. crossref(new window)

12.
Chen, X. B.; Devaux, J.; Issi, J-P.; Billaud, D. Polym. Eng. Sci. 1995, 35, 637. crossref(new window)

13.
Bueche, F. J. Appl. Phys. 1973, 44, 532. crossref(new window)

14.
Narkis, M.; Vaxman, A. J. Appl. Polym. Sci. 1984, 29,1639. crossref(new window)

15.
Park, S. J.; Jin, J. S. J. Colloid Interface Sci. 2001, 242,174. crossref(new window)

16.
Park, S. J.; Kim, J. S. J. Colloid Interface Sci. 2000,232, 311. crossref(new window)

17.
Park, S. J. In Interfacial Forces and Fields: Theory and Application; Hsu, J. P., Ed.; Marcel Dekker: New York, 1999. crossref(new window)

18.
Park, S. J.; Kim, J. S. J. Colloid Interface Sci. 2001,244, 336. crossref(new window)

19.
Wu, G. Z.; Zhang, C.; Miura, T. D. S.; Asai, S. G.; Sumita, M. S. J. Appl. Polym. Sci. 2001, 80, 1063. crossref(new window)

20.
Watanabe, N.; Nakajima, T.; Touhara, H. Graphite Fluorides;Elsevier: Amsterdam, 1998.

21.
Chong, Y. B.; Ohara, H. J. Fluorine Chem. 1992, 57, 169. crossref(new window)

22.
Takasima, M.; Fukami, S.; Nosaka, Y.; Unish, T. J. Fluorine Chem. 1992, 57, 131. crossref(new window)

23.
Panev, A. G.; Gruber, V.; Fripiat, J. J. J. Catal. 1997,168, 321. crossref(new window)

24.
Hayes, L. J. J. Fluorine Chem. 1976, 8, 69. crossref(new window)

25.
Bismarck, A.; Tahhan, R.; Springer, J.; Schuls, A.; Klapötke, T. M.; Zell, H.; Michaeli, W. J. Fluorine Chem.1997, 84, 127. crossref(new window)

26.
Wu, S. Polymer Interface and Adhesion; Marcel Dekker:New York, 1982.

27.
van Oss, C. J. Interfacial Forces in Aqueous Media;Marcel Dekker: New York, 1994. crossref(new window)

28.
Yi, X.; Wu, G.; Pan, Y. Polym. Intern. 1997, 44, 117. crossref(new window)

29.
Fowkes, F. M. In Physico-Chemical Aspects of Polymer Surfaces; Mittal, K. L., Ed.; Plenum: New York, 1983. crossref(new window)