Synthesis and Characterization of Low-Dimensional Chalcogenide Compound via a Molten Salt Method
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Synthesis and Characterization of Low-Dimensional Chalcogenide Compound via a Molten Salt Method
Choi, Duc-Su; Yun, Hye-Sik; Oh, Hwa-Suk; Kim, Don; Yun, Ho-Seop; Park, Youn-Bong;
  PDF(new window)
 Abstract
The reaction of Cu metal with mixed alkali metal polyselenide flux () produced large plate-like crystals of . The structure of , determined with X-ray single crystal diffraction techniques, is tetragonal (P4/mmm, a=4.013(1)), c=9.712(1)), z=1, R=6.7%). The structure is composed double layers which are made of fused anti PbO-type Cu2Se2 layers. Temperature variable resistivity measurement on single crystal of shows metallic behavior ranging from (at 300 K) to (at 20 K).
 Keywords
Alkali Metal Polyselenide Flux;Layer Compound;Metallic Conductor;Low-dimensional Selenide Compound;Chalcogenide Compound;
 Language
Korean
 Cited by
 References
1.
Bowden, W. L.; Barnette, L. H.; DeMuth, D. L. J.Elec. Soc. 1988, 135, 1. crossref(new window)

2.
Chevrel, R.; Sergent, M. In Crystal Chemistry and Properties of materials with Quasi-One-Dimensional Structures, J. Rouxel Ed., 1986, 315

3.
Dubois, M. R. Chem. Rev. 1989, 89, 1. crossref(new window)

4.
Berger, R.; Van Bruggen, C. F. J. Less-Comm. Met.1984, 99, 113 crossref(new window)

5.
Fleming, R. M.; ter Harr, L. W.; DiSalvo,F. J. Phy. Rev. 1987, 35B, 5388

6.
Monceau, P.;Richard, J.; Renard, M. Phy. Rev. 1982, 25B, 931

7.
Rouxel, J. Crystal Chemistry and Properties of Materialswith Quasi One-Dimensional Structures J. Rouxel,Reidel, Dordrecht, The Netherlands, 1986

8.
Bronger,W.; Muller, P. J. Less-Comm. Met. 1984, 100, 241 crossref(new window)

9.
Bronger, W. Angew. Chem. Int. Ed. Engl. 1981, 20, 52. crossref(new window)

10.
Amato, I. Science, 1991, 252, 644. crossref(new window)

11.
Steine, A.; Keller, S. W.; Mallouk, T. E. Science, 1993,259, 1558. crossref(new window)

12.
Rao, C. N. R.; Gopalakrishnan, J. New Directions in Solid State Chemistry Cambridge University Press, 1986.

13.
Laudise, R. A. C&EN, 1987, Sept. 30

14.
Liao, J. H.; Kanatzidis, M. G. Inorg. Chem. 1992, 31, 431. crossref(new window)

15.
Kanatzidis, M. G. Chem. Mater. 1990, 2, 353. crossref(new window)

16.
Warren, C. J.; Dhingra, S.; Ho, D. M.; Haushalter, R.C.; Bocarsly, A. B. Inorg. Chem. 1994, 33, 2709. crossref(new window)

17.
Bronger, W. Pure and Appl. Chem. 1985, 57, 1363. crossref(new window)

18.
Park, Y.; Liao, J-H.; Kim, K-W.; Kanatzidis, M. G. InInorganic and Organometallic Oligomers and Polymers,J. F. Harrod, R. M. Laine Eds., Kluwer AcademicPublishers, 1991, 263.

19.
Park, Y.; Kanatzidis, M. G. Chem. Mater. 1991, 3, 781. crossref(new window)

20.
Park, Y. "Low-Temperature Synthesis of New Ternary Chalcogenide Compounds of Cu, Au, and Hg, Using Alkali metal Polychalcogenide Fluxes", Ph.D. Dissertation, Michigan State University, 1992.

21.
Park, Y.; Choi, D. Bull. Korean Chem. Soc. 2004, 25,1095. crossref(new window)

22.
Park, Y.; Yun, H.; Oh, H. Bull. Korean Chem. Soc.1999, 20, 605.

23.
Smith, D. K.; Nichols, M. C.; Zolensky, M. J. E. POWD10: A Fortran IV Program for Calculating X-rayPowder Diffraction Patterns, version 10. PennsylvaniaState University, 1983.

24.
Sheldrick, G. M. In Crystallographic Computing 3;Sheldrick, G. M.; kruger, C.; Doddard, R., Eds. OxfordUniversity Press, Oxford, England, 1985, 175-189.

25.
SHELXTL: Single Crystal Structure Analysis Software,Version 6.0, 1999. Bruker Inc.

26.
Stroll, P.; Naether, C.; Jess, I.; Bensch, W. Acta. CrystallographicaC. 1999, 55, 286. crossref(new window)

27.
Kanatzidis, M. G.; Park, Y. J. Am. Chem. Soc., 1989,111, 3767. crossref(new window)

28.
Jansen, M. Angew. Chem., Int. Ed. Engl. 1987, 26, 1098 crossref(new window)

29.
Scherbaum, F.; Huber, B.; Muller, G.; Schmitbaur,H. Angew. Chem. Int. Ed. Engl. 1988, 27, 1542. crossref(new window)