Fabrication of Transparent Color Coating Glass by Sol-gel Method
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Fabrication of Transparent Color Coating Glass by Sol-gel Method
Park, Jong-Guk; Jeon, Dae-Woo; Lee, Mi-Jai; Lim, Tea-Young; Hwang, Jonghee; Kim, Jin-Ho;
  PDF(new window)
 Abstract
Transparent color coating films were fabricated on a glass substrate by using sol-gel hybrid binder and organic dye. Sol-gel hybrid binder coating film fabricated with PTMS of 0.03 mole showed a very high pencil hardness of 9 H. As the withdrawal speed increased from 1.0 mm/s to 5.0 mm/sec, The yellowness () of coating glass also gradually increased. The transmittance of yellow color coating glass was 82.6% and the haze of coating glass was 0.35%. Red and blue color coating glasses also showed the high transmittance of 62.4% and 80.6% respectively. The surface hardness of color coating films was 6 H.
 Keywords
Color coating film;Sol-gel hybrid;Hardness;Wet process;Transmittance;
 Language
Korean
 Cited by
 References
1.
D. Moncke, M. Papageorgiou, A. W. Beckmann, and N. Zacharias, J. Archaeological Sci., 46, 23 (2014). [DOI: http://dx.doi.org/10.1016/j.jas.2014.03.007] crossref(new window)

2.
S. Sakka, Handbook of Sol-Gel Scienceand Technology Processing Characterization and Applications., 3, 599 (Kluwer Academic Press, Japan, 2005).

3.
W. Vogle, The American Ceramic Society, 153 (1985).

4.
D. Avnir, V. R. Kaufman, and R. Reisfeld, J. Non-cryst. Solids, 74, 395 (1985). [DOI: http://dx.doi.org/10.1016/0022-3093(85)90081-X] crossref(new window)

5.
P Judeinstein and C. Sanchez, J. Mater. Chem., 6, 511 (1996). [DOI: http://dx.doi.org/10.1039/jm9960600511] crossref(new window)

6.
U. Schubert, N. Husing, and A. Lorenz, Chem. Mater., 7, 2010 (1995). [DOI: http://dx.doi.org/10.1021/cm00059a007] crossref(new window)

7.
T. Iwamoto and J. D. Mackenzie, J. Mater. Sci., 30, 2566 (1995). [DOI: http://dx.doi.org/10.1007/BF00362135] crossref(new window)

8.
J. Schmidt, Non-Cryst. Solids, 178, 302 (1994). [DOI: http://dx.doi.org/10.1016/0022-3093(94)90299-2] crossref(new window)

9.
T. Iwamoto and J. D. Mackenzie, J. Mat. Sci., 30, 2566 (1995). [DOI: http://dx.doi.org/10.1007/BF00362135] crossref(new window)

10.
H. Schmidt, J. Non-Cryst. Solids, 178, 302 (1994). [DOI: http://dx.doi.org/10.1016/0022-3093(94)90299-2] crossref(new window)

11.
J. Kron, S. Amberg-Schwab, and G. Schottner, J. Sol-Gel Sci. Technol., 2, 189 (1994). [DOI: http://dx.doi.org/10.1007/BF00486239] crossref(new window)

12.
R. Kasemann and H. Schmidt, New J. Chem., 18, 1117 (1994).

13.
H. Schmidt and H. Wolter, J. Non-Cryst. Solids, 121, 428 (1990). [DOI: http://dx.doi.org/10.1016/0022-3093(90)90171-H] crossref(new window)

14.
S. Amberg-Schwab, H. Katschorek, U Weber, M. Hoffmann, and A. Burger, J. Sol-Gel Sci. Tech., 19, 125 (2000). [DOI: http://dx.doi.org/10.1023/A:1008738912173] crossref(new window)