Study of Adhesion according to Various Surface Treatments for Lithium Ion Secondary Battery Pouch Film
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Study of Adhesion according to Various Surface Treatments for Lithium Ion Secondary Battery Pouch Film
Kim, Do Hyun; Bae, Sung Woo; Cho, Jung Min; Yoo, Min Sook; Kim, Dong Soo;
  PDF(new window)
Pouch film is manufactured by laminating aluminum foil, polyamide film and polypropylene film with an adhesive or extrusion resin. However, a surface treatment is required for the aluminum because bonding does not occur easily between the aluminum foil and the polymer film. Thus, for this study, surface treatment experiments were performed in order to confirm the effect on adhesion strength. First, a variety of surface treatment solutions were coated on aluminum foil, and contact angle and surface morphology analysis was carried out for the surface-treated aluminum. For lamination of the surface-treated aluminum foil with polyamide film, a polyurethane base adhesive was prepared for the adhesive strength test specimens. The adhesive strength between the aluminum foil and the polyamide film of the resulting specimens was measured (UTM). With such an experiment, it was possible to evaluate the effect on adhesive strength of the various surface treatments.
Lithium ion battery;Pouch film;Surface treatment;Lamination;Adhesive strength;
 Cited by
Xia, F. and Xu, S., "Effect of Surface Pre-Treatment on the Hydrophilicity and Adhesive Properties of Multilayered Laminate Used for Lithium Battery Packaging," Applied Surface Science, Vol. 268, No. pp. 337-342, 2013. crossref(new window)

Brunner, S., Gasser, P., Simmler, H., and Wakili, K. G., "Investigation of Multilayered Aluminium-Coated Polymer Laminates by Focused Ion Beam (FIB) Etching," Surface and Coatings Technology, Vol. 200, No. 20, pp. 5908-5914, 2006. crossref(new window)

Ashley, R., Cochran, M., and Allen, K., "Adhesives in Packaging," International Journal of Adhesion and Adhesives, Vol. 15, No. 2, pp. 101-108, 1995. crossref(new window)

Hwa Sung Co., Ltd., "Glossary, COMMON SENSE of Adhesive," (Accessed 19 February 2016)

Lin, C.-T., "Green Chemistry in Situ Phosphatizing Coatings," Progress in Organic Coatings, Vol. 42, No. 3, pp. 226-235, 2001. crossref(new window)

Chen, W.-K., Bai, C.-Y., Liu, C.-M., Lin, C.-S., and Ger, M.-D., "The Effect of Chromic Sulfate Concentration and Immersion Time on the Structures and Anticorrosive Performance of the Cr (III) Conversion Coatings on Aluminum Alloys," Applied Surface Science, Vol. 256, No. 16, pp. 4924-4929, 2010. crossref(new window)