Oil Absorbencies of Fibers of Biodegradable and Microbial Polymers Prepared by Electrospinning Method
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Oil Absorbencies of Fibers of Biodegradable and Microbial Polymers Prepared by Electrospinning Method
Jang, Ei-Sup; Lee, Won-Ki; Park, Chan-Young; Min, Sung-Kee; Jang, Seong-Ho;
  PDF(new window)
Fibers of microbial polyesters, poly(3-hydroxy butyrate) (PHB) and poly(3-hydroxy butyrate-co-3-hydroxy valerate) (HB-co-HV) were prepared by electrospinning method. The obtained fibers were evaluated by differential scanning calorimetry, scanning electron microscopy, and oil absorption. The formation of fibers was strongly dependent on a concentration of solution. At a low concentration, the fibers contained beads which is from aggregation of polymer due to short evaporation time. The fine fibers with diameter were obtained at 20 wt% concentration. The contact angle measurement showed that the fiber had higher water contact angle than the film due to the lotus-like effect. Oil absorbency showed that the fiber had higher than the film. Specially, the HB-co-HV fiber which was spinned from 20 wt% absorbed 65% oil which is much higher than that of a normal polypropylene-based oil paper.
Microbial polyester;Electrospinning;Lotus effect;Oil absorbency;
 Cited by
Electrospinning법으로 제조된 PZT 섬유의 구조분석 및 특성평가,박춘길;윤지선;정영훈;남중희;조정호;백종후;정대용;

한국세라믹학회지 , 2013. vol.50. 6, pp.466-469 crossref(new window)
화장용 기름 종이로 이용하기 위한 폴리에틸렌옥사이드 나노섬유 쉬트의 기름 흡수능력 평가,윤옥자;

폴리머, 2016. vol.40. 6, pp.985-991 crossref(new window)
Structural Analysis and Characterization of PZT Fiber Fabricated by Electrospinning, Journal of the Korean Ceramic Society, 2013, 50, 6, 466  crossref(new windwow)
Bhardwaj, N., Kundu, S. C., 2010, Electrospinning: a fascinating fiber fabrication technique, Biotechnol. Adv., 28, 325-347. crossref(new window)

Dalton, P. D., Grafahrend, D., Klinkhammer, K., Klee, D., Moller, M., 2007, Electrospinning of polymer melts: Phenomenological observations, Polymer, 48, 6823-6833. crossref(new window)

Deitzel, J. M., Kleinmeyer, J., Harris, D., Beck T., N. C., 2001, The effect of processing variables on the morphology of electrospun nanofibers and textiles, Polymer, 42, 261-272. crossref(new window)

Deitzel, J. M., Kleinmeyer, J. D., Hirvonen, J. K., Beck Tan, N. C., 2001, Controlled deposition of electrospun poly(ethylene oxide) fibers, Polymer, 42, 8163-8170. crossref(new window)

Frenot, A., Chronakis, I. S., 2003, Polymer nanofibers assembled by electrospinning, Curr. Opin. Colloid Interface Sci., 8, 64-75. crossref(new window)

Gopferich, A., 1996, Mechanisms of polymer degradation and erosion, Biomaterials, 17, 103-114. crossref(new window)

Huang, Z. M., Zhang, Y. Z., Kotaki, M., Ramakrishn, S., 2003, A review on polymer nanofibers by electrospinning and their applications in nanocomposites, Compos. Sci. Technol., 63, 2223-2253. crossref(new window)

Karlsson, S., Albertsson, A. C., 1998, Biodegradable polymers and environmental interaction, Polym. Eng. Sci., 38, 1251-1253. crossref(new window)

Kim, C., Kim, Y. J., Kim, Y. A., 2004, Fabricatio1n and structural characterization of electro-spun polybenzimidazol- derived carbon nanofiber by graphitization, Solid State Commun., 132, 567-571. crossref(new window)

Leung, W. W. F., Hung, C. H., Yuen, P. T., 2010, Effect of face velocity, nanofiber packing density and thickness on filtration performance of filters with nanofibers coated on a substrate, Sep. Purif. Technol., 71, 30-37. crossref(new window)

Marmur, A., 2004, The lotus effect: Superhydrophobicity and metastability, Langmuir, 20, 3517-3519. crossref(new window)

Moore, C. J., 2008, Synthetic polymers in the marine environment: a rapidly increasing, long-term threat, Environ. Res., 108, 131-139. crossref(new window)

Rios, L. M., C. Moore, C., Jones, P. R., 2007, Persistent organic pollutants carried by synthetic polymers in the ocean environment, Mar. Pollut. Bull., 54, 1230-1237. crossref(new window)

Shin, C., 2006, Filtration application from recycled expanded polystyrene, J. Colloid Interface Sci., 302, 267-271. crossref(new window)

Sudesh, K., Abe, H., Doi, Y., 2000, Synthesis, structure and properties of polyhydroxyalkanoates: biological polyesters, Prog. Polym. Sci., 25, 1503-1555. crossref(new window)

Swift, G., 1993, Directions for environmentally biodegradable polymer research, Acc. Chem. Res., 26, 105-110. crossref(new window)

Volova, T., Shishatskaya, E., Sevastianov, V., Efremov, S., 2003, Results of biomedical investigations of PHB and PHB/PHV fibers, Biochem. Eng. J., 16, 125-133. crossref(new window)

Wang, C., Hsu, C. H., Hwang, I. H., 2008, Scaling laws and internal structure for characterizing electrospun poly[(R)-3-hydroxybutyrate] fibers, Polymer, 49, 4188-4195. crossref(new window)

Williams, S. F., Martin, D. P., Horowitz, D. M., Peoples, O. P., 1999, PHA applications: addressing the price performance issue I. Tissue engineering, Int. J. Biol. Macromol., 25, 111-121. crossref(new window)