Pozzolanic reaction of the waste glass sludge incorporating precipitation additives
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Computers and Concrete
  • Volume 17, Issue 2,  2016, pp.255-269
  • Publisher : Techno-Press
  • DOI : 10.12989/cac.2016.17.2.255
 Title & Authors
Pozzolanic reaction of the waste glass sludge incorporating precipitation additives
You, Ilhwan; Choi, Jisun; Lange, David A.; Zi, Goangseup;
The waste glass sludge is a waste produced in the glass industry. It is in a dust form and disposed with water. In the disposal process, various cohesive agents are incorporated in order to precipitate the glass particles efficiently. In this paper, we investigate the pozzolanic reaction of the waste glass sludge incorporating precipitation additives experimentally. The consumption of calcium hydroxide, the setting time and the compressive strength and the pore structure were tested for two different types of the waste glass sludge depending on whether precipitation additives were used. It was found that the waste glass sludge incorporating the precipitation additives had a higher pozzolanic potential than the reference waste glass sludge without precipitation additives.
waste glass sludge;precipitation additives;cohesive agent;coagulant aid;caustic soda;alkali activation;pozzolanic reaction;
 Cited by
Allahverdi, A. and Ghorbani, J. (2006), "Chemical activation and set acceleration of lime-natural pozzolan cement", Ceramic. Silikaty, 50(4), 193.

Almeida, A.E.F.D.S. and Sichieri, E.P. (2006), "Thermogravimetric analyses and mineralogical study of polymer modified mortar with silica fume", Mater. Res., 9(3), 321-326. crossref(new window)

Altwair, N.M., Johari, M.A.M. and Hashim, S.F.S. (2011), "Strength activity index and microstructural characteristics of treated palm oil fuel ash", Struct., 11(5), 100-107.

ASTM C150 / C150M-15 (2015), "Standard specification for Portland cement", American Society for Testing and Materials International, West Conshohocken, PA.

ASTM C191-13 (2013), Standard test methods for time of setting of hydraulic cement by vicat needle, American Society for Testing and Materials International, West Conshohocken, PA.

ASTM C311 / C311M-13 (2013), Standard test methods for sampling and testing fly ash or natural pozzolans for use in Portland-cement concrete, American Society for Testing and Materials International, West Conshohocken, PA.

ASTM C618-15 (2015), "Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete", American Society for Testing and Materials International, West Conshohocken, PA.

Bazant, Z.P., Zi, G., and Meyer, C. (2000), "Fracture mechanics of ASR in concretes with waste glass particles of different sizes", J. Eng. Mech., 126(3), 226-232. crossref(new window)

Berra, M., Carassiti, F., Mangialardi, T., Paolini, A.E. and Sebastiani, M. (2012), "Effects of nanosilica addition on workability and compressive strength of Portland cement pastes", Constr. Build. Mater., 35, 666-675. crossref(new window)

Bjornstrom, J., Martinelli, A., Matic, A., Borjesson, L. and Panas, I. (2004), "Accelerating effects of colloidal nano-silica for beneficial calcium-silicate-hydrate formation in cement", Chem. Phys. Lett., 392(1), 242-248. crossref(new window)

Bondar, D., Lynsdale, C.J., Milestone, N.B. and Hassani, N. (2014), "Sulfate resistance of alkali activated pozzolans", Int. J. Concrete Struct. Mater., 9(2), 1-14.

Bynum Jr, D., Evertson, J.F. and Fleisher, H.O. (1972), "Scrap tire-beer bottle concrete", Materiaux et Construction, 5(3), 151-157. crossref(new window)

Chindaprasirt, P., Jaturapitakkul, C. and Sinsiri, T. (2007), "Effect of fly ash fineness on microstructure of blended cement paste", Constr. Build. Mater., 21(7), 1534-1541. crossref(new window)

Dhir, R.K., Dyer, T.D. and Tang, M.C. (2009), "Alkali-silica reaction in concrete containing glass", Mater. Struct., 42(10), 1451-1462. crossref(new window)

Divsholi, B.S., Lim, T.Y.D. and Teng, S. (2014), "Durability properties and microstructure of ground granulated blast furnace slag cement concrete", Int. J. Concrete Struct. Mater., 8(2), 157-164. crossref(new window)

Du, H. and Tan, K.H. (2013), "Use of waste glass as sand in mortar: Part II-Alkali-silica reaction and mitigation methods", Cement Concrete Comp., 35(1), 118-126. crossref(new window)

Espinosa, R.M. and Franke, L. (2006), "Influence of the age and drying process on pore structure and sorption isotherms of hardened cement paste", Cement Concrete Res., 36(10), 1969-1984. crossref(new window)

Jin, W., Meyer, C. and Baxter, S. (2000), "Glascrete concrete with glass aggregate", ACI Mater. J., 97(2), 208-213.

Johnston, C.D. (1974), "Waste glass as coarse aggregate for concrete", J. Test. Eval., 2(5), 344-350. crossref(new window)

Kim, J., Moon, J.H., Sim, J.W., Sim, J., Lee, H.G. and Zi, G. (2014), "Durability properties of a concrete with waste glass sludge exposed to freeze-and-thaw condition and de-icing salt", Constr. Build. Mater., 66, 398-402. crossref(new window)

Kim, J., Yi. C.K. and Zi, G. (2015), "Waste glass sludge as a partial cement replacement in mortar", Constr. Build. Mater., 75(30), 242-246. crossref(new window)

Kontoleontos, F., Tsakiridis, P.E., Marinos, A., Kaloidas, V. and Katsioti, M. (2012), "Influence of colloidal nanosilica on ultrafine cement hydration: Physicochemical and microstructural characterization", Constr. Build. Mater., 35, 347-360. crossref(new window)

Korea Expressway Corporation Research Institute (2012), "Development of a concrete with high durability and better visibility by using waste-glass", Report of Korea Expressway Corporation Research Institute.

KS L 5108 (2007), Testing method for setting time of hydraulic cement by vicat needle, Korean Industrial Standards, Korea.

KS L 5201 (2006), "Portland cement", Korean Industrial Standards, Korea.

KS L ISO 679 (2006), Methods of testing cements-determination of strength, Korea Standards Association, Korea.

Malisch, R.W., Day, D.E., and Wixson, B.G. (1970), "Use of domestic waste glass as aggregate in bituminous concrete", Highway Res. Rec., 307, 1-10.

Maraghechi, H., Maraghechi, M., Rajabipour, F. and Pantano, C.G. (2014), "Pozzolanic reactivity of recycled glass powder at elevated temperatures: Reaction stoichiometry, reaction products and effect of alkali activation", Cement Concrete Comp., 53, 105-114. crossref(new window)

Meyer, C., Baxter, S. and Jin, W. (1996a), "Alkali-silica reaction in concrete with waste glass as aggregate", Materials for a New Millennium, proceedings of ASCE Materials Engineering Conference, Washington, D.C., 1388-1394.

Meyer, C., Baxter, S. and Jin, W. (1996b), "Potential of waste glass for concrete masonry blocks", Materials for a New Millennium, Proceedings of ASCE Materials Engineering Conference, Washington, D.C., 666-673.

Mindess, S., Young, J.F. and Darwin, D. (2003), Concrete, 2nd Edition, Prentice-Hall, New Jersey, USA.

Park, S.B. and Lee, B-C. (2006), "Expansion properties of mortar using waste glass and industrial byproducts", Int. J. Concrete Struct. Mater., 18(2), 125-132. crossref(new window)

Pelisser, F., Steiner, L.R. and Bernardin, A.M. (2012), "Recycling of porcelain tile polishing residue in portland cement: hydration efficiency", Envir. Sci. Tech., 46(4), 2368-2374. crossref(new window)

Perraki, T., Kakali, G. and Kontoleon, F. (2003), "The effect of natural zeolites on the early hydration of Portland cement", Micropor. Mesopor. Mat., 61(1), 205-212. crossref(new window)

Rashad, A.M., Seleem, H.E.D.H. and Shaheen, A.F. (2014), "Effect of silica fume and slag on compressive strength and abrasion resistance of HVFA concrete", Int. J. Concrete Struct. Mater., 8(1), 69-81. crossref(new window)

Richards, C.W. and Arnold, G.F. (1971), "Lightweight building materials from waste glass", Report No. 144, Department of Civil Engineering, Stanford University, Stanford, Calif.

Schwarz, N., Cam, H. and Neithalath, N. (2008), "Influence of a fine glass powder on the durability characteristics of concrete and its comparison to fly ash", Cement Concrete Comp., 30(6), 486-496. crossref(new window)

Shao, Y., Lefort, T., Moras, S. and Rodriguez, D. (2000), "Studies on concrete containing ground waste glass", Cement Concrete Res., 30(1), 91-100. crossref(new window)

Shayan, A. and Xu, A. (2004), "Value-added utilisation of waste glass in concrete", Cement Concrete Res., 34(1), 81-89. crossref(new window)

Shi, C. (2009), "Corrosion of glasses and expansion mechanism of concrete containing waste glasses as aggregates", J. Mater. Civil Eng., 21(10), 529-534. crossref(new window)

Shi, C., Roy, D. and Krivenko, P. (2006), Alkali-activated cements and concretes, CRC press, New York, NY, USA.

Shi, C., Wu, Y., Riefler, C. and Wang, H. (2005), "Characteristics and pozzolanic reactivity of glass powders", Cement Concrete Res., 35(5), 987-993. crossref(new window)

Yehia, S., Helal, K., Abusharkh, A., Zaher, A. and Istaitiyeh, H. (2015), "Strength and durability evaluation of recycled aggregate concrete", Int. J. Concrete Struct. Mater., 9(2), 219-239. crossref(new window)

Zeng, Q., Li, K., Fen-Chong, T. and Dangla, P. (2012), "Pore structure characterization of cement pastes blended with high-volume fly-ash", Cement Concrete Res., 42(1), 194-204. crossref(new window)