The Characteristics and Formation of Tungsten Nano-Powder by Ultrasonic Spray Pyrolysis Method
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
The Characteristics and Formation of Tungsten Nano-Powder by Ultrasonic Spray Pyrolysis Method
Lee, Ho-Jin; Yoon, Jung-Hyun; Choe, Jean-Il;
  PDF(new window)
 Abstract
Nanosize tungsten powder was synthesized by ultrasonic spray pyrolysis method through a solution containing ammonium metatungstate hydrate and reduction treatment. It was expected the improvement of mechanical properties due to increasing surface free energy and surface activity. Starting solutions with each concentration, reaction temperature and reduction treatment were significantly influenced on the formation of tungsten size and phase. It was found that particle size was decreased with concentration of starting solution and surface tension were decreased. The particle size was increased at thermal decomposition temperature above by neck growth of interparticles. Tungsten particles were formed by reduction reaction in atmosphere of hydrogen gas at the temperature above .
 Keywords
Nanosize tungsten powder;Ultrasonic spray pyrolysis method;Starting solution;
 Language
Korean
 Cited by
 References
1.
R. W. Siegel, G. E. Fougere, NanoStructured Materials, 6 (1995) 205 crossref(new window)

2.
K. Jia, T. E. Fisher, B. Gallois, ibid, 10 (1998) 875 crossref(new window)

3.
R. L. Holtz, V. Provenzamo, M. A. Imam, ibid, 7 (1996) 259 crossref(new window)

4.
B. K. Kim, H. S. Kim, G. H. Ha, H. S. Chung, PM. World Congress Proceeding (1993) 1252

5.
M. Langlet, J. C. Joubert, The Pyrosol Process and Pyrosis of Ultrasonically Generated Aerosol, Chemistry of Advanced Materials, Blackwell Scientific Publication, Oxford. (1993) 55

6.
L, Gao, B. H. Kear, Nanostructured Materials, 5 (1995) 555 crossref(new window)

7.
J. Lezansui, W. Rutkowski, Powder Met. Int., 19 (1987) 29

8.
R. J. Lang, J. Acoust. Soc. Am., 34 (1962) 6 crossref(new window)

9.
J. W. S. Layleigh, The Theory of Sound, Dover Publication, New York, (1945) 344

10.
S. C. Zhang, G. L. Messing, J. Am. Cer. Soc., 73 (1990) 61 crossref(new window)

11.
P. Walkder, J. W. Albiston, F. R. Sale, Powder Metallurgy, 28 (1985) 36 crossref(new window)