Effect of Oxygen on the Microstructure and Mechanical Properties of Cr-O-N Coatings
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effect of Oxygen on the Microstructure and Mechanical Properties of Cr-O-N Coatings
Yun, Jun-Seo; Kwon, Se-Hun; Park, In-Wook; Lee, Jeong-Du; Kim, Kwang-Ho;
  PDF(new window)
 Abstract
Cr-O-N coatings having different oxygen contents were deposited on Si wafer and SUS 304 substrates by an arc ion plating technique using Cr target in gaseous atmosphere. As increasing oxygen content in the coating, the microstructure of Cr-O-N coating changed from polycrystalline having NaCl structure to amorphous structure. Further increase of oxygen content resulted in phase transformation from amorphous to rhombohedral structure. From the variations of d value and average grain size, it was revealed that the maximum solubility of oxygen in Cr-O-N coating was about 21 at.%. And the maximum micro-hardness of 2751HK was obtained in this composition. The lowest friction coefficient was measured in the coating having 34.8 at.% of oxygen. However, more narrow width of wear track was found in the coating having 30.1 at.% of oxygen.
 Keywords
Cr-O-N;Arc ion plating;Solid-solution;Hardness;Wear;
 Language
Korean
 Cited by
 References
1.
G. S. Kim, S. Y. Lee, J. H. Hahn, Surf. Coat. Technol., 193 (2005) 213 crossref(new window)

2.
J. Creus, H. Indriss, H. Mazille, F. Sanchette, P. Jacquot, Surf. Coat. Technol., 107 (1998) 183 crossref(new window)

3.
G. T. Liu, J. G. Duh, K .H. Chung, J. H. Wang, Surf. Coat. Technol., 200 (2005) 2100 crossref(new window)

4.
C. Rebholz, H. Ziegele, A. Leyland, A. Mattew, Surf. Coat. Technol., 115 (1999) 222 crossref(new window)

5.
J. Bujak, J. Walcowicz, J. Kusi ski, Surf. Coat. Technol., 180-181 (2004) 150 crossref(new window)

6.
K. H. Kim, D. S. Han, S. K. Kim, Surf. Coat. Technol., 163-164 (2003) 605 crossref(new window)

7.
S. Boelens, H. Veltrop, Surf. Coat. Technol., 33 (1987) 63 crossref(new window)

8.
P. Hones, R. Sanjines, F. Levy, Thin Solid Films, 332 (1998) 240 crossref(new window)

9.
K. H. Lee, C. H. Park, T. S. Yoon, J. J. Lee, Thin Solid Films, 385 (2001) 167 crossref(new window)

10.
E. Martinez, R. Sanjines, O. Banakh, F. Levy, Thin Solid Films, 447-448 (2004) 332 crossref(new window)

11.
T. Suzuki, J. Inoue, H. Saito, M. Hirai, H. Suematsu, W. Jiang, K. Yatsui, Thin Solid Films, 515 (2006) 2161 crossref(new window)

12.
S. Collard, H. Kupfer, G. Hecht, W. Hoyer, H.Moussaoui, Surf. Coat. Technol., 112 (1999) 181 crossref(new window)

13.
T. Suzuki, J. Inoue, H. Saito, M. Hirai, H. Suematsu, W. Jiang, K. Yatsui, Thin Solid Films, 515m (2006) 2161

14.
L. Castaldi, D. Kurapov, A. Reiter, V. Shklover, P. Schwaller, J. Patscheider, Surf. Coat. Technol., 203 (2008) 545 crossref(new window)

15.
C. Gautier, J. Machet, Surf. Coat. Technol., 94-95 (1997) 422 crossref(new window)

16.
K. H. Kim, D. S. Han, S. K. Kim, Surf. Coat. Technol., 163-164 (2003) 605 crossref(new window)

17.
S. Y. Yoon, S. R. Choi, M. H. Lee, W. H. Kim, J. Kor. Inst. Surf. Eng., 36 (2003) 2

18.
J. H. Park, W. S. Chung, Y. R. Cho, K. H. Kim, Surf. Coat. Technol., 188-189 (2004) 425 crossref(new window)

19.
Y. S. Hong, S. H. Kwon, K. H. Kim, J. Kor. Inst. Surf. Eng., 42 (2009) 73 crossref(new window)

20.
D. Gryaznov, J. Fleig, J. Maier, Solid State Ionics, 177 (2006) 1538

21.
H. C. Barshilia, N. Selvakumar, B. Deepthi, K. S. Rajam, Surf. Coat. Technol., 201 (2006) 2193 crossref(new window)

22.
B. Navinsek, P. Panjan, A. Cvelbar, Surf. Coat. Technol., 74-75 (1995) 155 crossref(new window)

23.
W. Xiaozhi, W. Shzofeng, Z. Hull, Cent. Eur. J. Phys., 6 (2008) 440 crossref(new window)

24.
P. Kratochvil, P. lukac, B. Sprusil, Czech. J. Physics, B23 (1973) 621

25.
W. O. Milligan, D. F. Mullica, H. O. Perkins, C. K. C. Lok, Acta Cryst., A40 (1984) 264

26.
M. Kalin, B. Hockey, S. Jahanmir, J. Mater. Res., 18 (2003) 27 crossref(new window)

27.
D. Y. Wang, M. C. Chiu, Surf. Coat. Technol., 137 (2001) 164 crossref(new window)

28.
A. Matthews, S. Franklin, Holmberg, J. Phys. D: Appl. Phys., 40 (2007) 5463 crossref(new window)

29.
H.-H. Jin, J. W. Kim, K. H. Kim, S.-Y. Yoon, J. Kor. Phys. Soc., 42 (2005) 88

30.
Q. Wang, I. W. Park, K. H. Kim, J. Vac. Sci. Technol., A26 (2008) 5