Emission Characteristics of Blue Fluorescent OLED with Anode Materials
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Emission Characteristics of Blue Fluorescent OLED with Anode Materials
Kong, Do-Hoon; Lee, Yo-Seb; Ju, Sung-Hoo; Yang, Jae-Woong;
  PDF(new window)
 Abstract
We studied the blue fluorescent OLED with Mg:Ag, Al, Ni as anode materials. Blue fluorescent OLEDs were fabricated using Anode / (3 nm) / 2-TNATA (60 nm) / NPB (30 nm) / SH-1 : BD-2 (5 vol.%, 30 nm) / Bphen (40 nm) / Liq (1 nm) / Al (150 nm). Current density of OLED with Mg:Ag was not measured due to too low work function, and that of OLED with Al showed at 12 V. Luminance and Current efficiency of OLED with Al showed and 0.9 cd/A. Current density of OLED with Ni of 8, 10, 12 nm thickness showed 10, 12.9, , respectively. Luminance and Current efficiency of OLED with Ni of 8, 10, 12 nm thickness showed 670.9, 991.2, and 6.7, 7.7, 3.6 cd/A, respectively. Transmittance of Al was 52.2% at 476 nm wavelength and that of Ni of 8, 10, 12 nm thickness was 79, 77, 74 %, respectively. In spite of best current density, OLED with Al showed the lowest luminance and current efficiency because of low work function and poor transmittance. When thickness of Ni was increased to 12nm, current efficiency was sharply lower owing to bad transmittance and unbalance of holes and electrons. Finally, OLED with Ni of 10 nm thicknes showed the highest current efficiency.
 Keywords
Emission Characteristic;Blue Fluorescent;OLED;Anode Materials;
 Language
Korean
 Cited by
 References
1.
T.H. Kwak, S.H. Ju, J. Kor. Inst. Surf. Eng., 47 (2014) 201

2.
K.Y. Lee, S.I. Kim, J.Y. Kim, K.E. Kwon, Y.W. Kang, J.W. Son, J.W. Jeon, M.C. Kim, C.W. Lee, Journal of the Korean Vacuum Society, 21 (2012) 328 crossref(new window)

3.
S.M. park, H.G. kim, D.C. Lee, The Transactions of the Korean Institute of Electrical Engineers, 52 (2003) 261

4.
Xinjun Xu, Gui Yu, Yunqi Liu, Daoben Zhu, Oraganic Displays, 27 (2006) 24 crossref(new window)

5.
Nam-Gyu Hwang, Young-Chan Kim, Se-Won Choi, Chang-Seok Kang, Sung-Kil Hong, Korea Institute of industrial Technology, 31 (2011) 130

6.
Samuel J. Rosenberg, Nationl Bureau of Standards Monograph, 106 (1968) 19

7.
Heqing Tang, Haixing Liao, Lihua Zhu, Chemical Physics Letters, 381 (2003) 605 crossref(new window)

8.
F. Garten, J. Vrijmoeth, A.R. Schlatmann, R.E. Gill, T.M. Klapwijk, G. Hadziioannou, Syntheric Metals, 76 (1996) 85 crossref(new window)

9.
S. Cheylan, D.S. Ghosh, D. Krautz, T.L. Chen, V. Pruneri, Organic Electronics, 12 (2011) 818 crossref(new window)