Effects of Metal Anion Complexes in Electrolyte on the Properties of Anodic Oxide Films on ADC12 Al Alloy
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Effects of Metal Anion Complexes in Electrolyte on the Properties of Anodic Oxide Films on ADC12 Al Alloy
Yoo, Hyeonseok; Lee, Chulho; Oh, Kiseok; Choi, Jinsub;
  PDF(new window)
The anodization of ADC12 aluminum alloy was investigated in the metal anionic acid media. Anodic oxide films containing foreign elements were formed on ADC12 Al alloy by anodization in the anion complex solution. Furthermore, the rough surface and cracks were considerably smoothened by the deposit of metal anions. When the size of metal anion was small, relatively large amount of metal anions was loaded in anodic films. Existence of , and MgO was confirmed by XPS. According to the results of Tafel analysis, Mo oxide represented the most noble anti-corrosion potential due to formation. Corrosion current densities were generally higher than that of pristine anodic oxide without anion complexes.
Anion complex;ADC12;Aluminum alloy;Anodization;
 Cited by
W. A. Badawy, F. M. Al-Kharafi, A. S. El-Azab, Electrochemical behavior and corrosion inhibition of al, al-6061 and al-cu in neutral aqueous solutions, Corros. Sci 41 (1999) 709-727. crossref(new window)

V. Guillaumin, G. Mankowski, Localized corrosion of 2024 t351 aluminium alloy in chloride media, Corros. Sci. 41 (1999) 421-438.

C. Blanc, B. Lavelle, G. Mankowski, The role of precipitates enriched with copper on the susceptibility to pitting corrosion of the 2024 aluminium alloy, Corros. Sci. 39 (1997) 495-510. crossref(new window)

H. Dodiuk, A. E. Yaniv, I. E. Klein, N. Fin, L. Drori, Chemical interaction in the system aluminum oxide-primer-adhesive, Appl. Surf. Sci. 25 (1986) 137-153. crossref(new window)

J. Choi, J. K. Lee, J. H. Lim, S. J. Kim, Technology trends in fabrication of nanostructures of metal oxides by anodization and their applications, J. Korean Ind. Eng. Chem. 19 (2008) 249-258.

W. Lee, S. J. Park, Porous anodic aluminum oxide: anodization and templated synthesis of functional nanostructures, Chem. Rev. 114 (2014) 7487-7556. crossref(new window)

S. Ono, M. Saito, H. Asoh, Self-ordering of anodic porous alumina formed in organic acid electrolytes, Electrochem. Acta 51 (2005) 827-833. crossref(new window)

D. G. Eskin, Suyitno, L. Katgerman, Prog. Mechanical properties in the semi-solid state and hot tearing of aluminium alloys, Mater. Sci. 49 (2004) 629-711.

S. Moon, R. Arrabal, E. Matykina, 3-Dimensional structures of open-pores in PEO films on AZ31 Mg alloy, Mater. Lett. 116 (2015) 439-441.

S. Moon, Y Nam, Anodic oxidation of Mg-Sn alloys in alkaline solutions, Corros. Sci. 65 (2012) 494-501. crossref(new window)

S. Moon, Corrosion behavior of PEO-treated AZ31 Mg alloy in chloride solution, J. Solid State Electrochem. 18 (2014) 341-346. crossref(new window)

S. Moon, Y. Nam, C. Yang, Y. Jeong, Formation of anodic oxide films on as-cast and machined surfaces of al-si-cu casting alloy, J. Kor. Inst. Surf. Eng. 42 (2009) 260-266. crossref(new window)

S. Moon, C. Yang, S. Na, Effects of hydroxide and silicate ions on the plasma electrolytic oxidation of az31 mg alloy, J. Kor. Inst. Surf. Eng. 47 (2014) 147-154. crossref(new window)

S. Moon, S. Lee, K. Lee, D. Chang, Co-deposition of Si particles during electrodeposition of Fe in sulfate solution, J. Kor. Inst. Surf. Eng. 37 (2004) 319-325.

K. Nakata, Y. G. Kim, H. Fujii, T. Tsumura, T. Komazaki, Improvement of mechanical properties of aluminum die casting alloy by multi-pass friction stir processing, Mater. Sci. Eng. A437 (2006) 274-280. crossref(new window)

W. S. Miller, L. Zhuang, J. Bottema, A. J. Witterbrood, P. D. Smet, A. Haszler, A. Vieregge, Recent development in aluminium alloys for the automotive industry, Mater. Sci. Eng. A280 (2000) 37-49. crossref(new window)

D. S. Mehta, S. H. Masood, W. Q. Song, Investigation of wear properties of magnesium and aluminum alloys for automotive applications, J. Mater. Proce. Tech. 155 (2004) 1526-1531.

S. Moon, C. Yang, S. Na, Formation behavior of anodic oxide films on Al7075 alloy in sulfuric acid solution, J. Kor. Inst. Surf. Eng., 47, (2014) 155-161. crossref(new window)

M. Anwar, C. A. Hogarth, R. Bulpett, Effect of substrate temperature and film thickness on the surface structure of some thin amorphous films of $MoO_3$ studied by X-ray photoelectron spectroscopy (ESCA), J. Mater. Sci. 24 (1989) 3087-3090. crossref(new window)

Y. Tang, D. Wu, Y. Mai, H. Pan, J. Cao, C. Yang, F. Zhang, X. Feng, A two-dimensional hybrid with molybdenum difulfide nanocrystals strongly coupled on nitrogen-enriched graphene via mild temperature pyrolysis for high performance lithium storage, Nanoscale 6 (2014) 14679-14685. crossref(new window)

X. Hu, P. Jiang, J. Wan, Y. Xu, X. Sun, Study of corrosion and friction reduction of electroless Ni-P coating with molybdenum disulfide nanoparticles, J. Coat. Technol. Res. 6 (2009) 275-281. crossref(new window)

T. Lin, C. Yang, Z. Wang, H. Yin, X. Lu, F. Huang, J. Lin, X. Xie and M. Jiang, Effective nonmetal incorporation in black titania with enhanced solar energy utilization, Energy Environ. Sci. 7 (2014) 967-972. crossref(new window)

H.-L. Lu, S.-J. Ding, D. W. Zhang, Investigation of thermal stability of atomic-layer-deposited MgO thin films on Si(100) using x-ray photoelectron spectroscopy, electrochem. Solid-State Lett. 13 (2010) G25-G28. crossref(new window)