Emission Characteristics of White Tandem Organic Light Emitting Diodes Using Blue and Red Phosphorescent Materials
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Emission Characteristics of White Tandem Organic Light Emitting Diodes Using Blue and Red Phosphorescent Materials
Park, Chan-Suk; Ju, Sung-Hoo;
  PDF(new window)
 Abstract
We studied white tandem organic light-emitting diodes using blue and red phosphorescent materials. Optimized white single phosphorescent OLED was fabricated using CBP : FIrpic (12 vol.%, 9 nm) / CBP : : (1 vol.%, 1 vol.%, 1 nm) as emitting layer (EML). The single phosphorescent OLED showed maximum current efficiency of 22.5 cd/A, white emission with a Commission Internationale de l`Eclairage (CIE) coordinates of (0.342, 0.37) at , and variation of CIE coordinates with (, ) from 500 to . Optimized white tandem phosphorescent OLED was fabricated using CBP : FIrpic (12 vol.%, 7 nm) / CBP : : (1 vol.%, 1 vol.%, 3 nm) as EML. The tandem phosphorescent OLED showed maximum current efficiency of 49.2 cd/A, white emission with a CIE coordinates of (0.376, 0.366) at , variation of CIE coordinates with (, ) from 500 to . Maximum current efficiency of tandem phosphorescent OLED was more twice as high as single phosphorescent OLED. Our results suggest that tandem phosphorescent OLED was possible to control CIE coordinates and produce excellent color stability.
 Keywords
OLED;Tandem;Phosphorescent;White;Color stability;
 Language
Korean
 Cited by
 References
1.
C. -S. Park, S. -H. Ju, Emission characteristics of white organic light-emitting diodes using blue fluorescent and red phosphorescent materials, J. Korean Inst. Electr. Electron. Mater. Eng., 28 (2015) 704-710.

2.
C. W. Tang, S. V. Vanslyke, Organic electroluminescent diodes, Appl. Phys. Lett., 51 (1987) 913-915. crossref(new window)

3.
J. Kido, M. Kimura, K. Nagai, Multilayer white light-emitting organic electroluminescent devices, Science, 267 (1995) 1332-1334. crossref(new window)

4.
J. A. Lim, S. H. Ju, J. W. Yang, The effect of passivation film with inorganic/epoxy layers on life time characteristics of OLED device, J. Kor. Inst Surf. Eng., 42 (2009) 287-293. crossref(new window)

5.
F. Jing, L. Feng, G. Wenbao, L. Shiyong, White light emission from exciplex using tris-(8-hydroxyquinoline)aluminum as chromaticity-tuning layer, Appl. Phys. Lett., 78 (2001) 3947-3949. crossref(new window)

6.
C. W. Ko, Y. T. Tao, Bright white organic lightemitting diode, Appl. Phys. Lett., 79 (2001) 4234-4236. crossref(new window)

7.
C. -S. Park, D. -H. Kong, H. -H. Kang, S. -H. Yun, S. -H. Ju, White tandem organic light-emitting diodes using red and blue fluorescent materials, J. Kor. Inst. Surf. Eng., 48 (2015) 115-120. crossref(new window)

8.
V. Sivasubramaniam, F. Brodkorb, S. Hanning, H. P. Loebl, V. van Elsbergen, H. Boerner, U. Scherf, M. Kreyenschmidt, Fluorine cleavage of the light blue heteroleptic triplet emitter FIrpic, J. Fluor. Chem., 130 (2009) 640-649. crossref(new window)

9.
J. H. Seo, Y. K. Kim, Y. Ha, Efficient blue-green organic light-emitting diodes based on heteroleptic tris-cyclometalated iridium(III) complexes, Thin Solid Films, 517 (2009) 1807-1810. crossref(new window)

10.
M. -Y. Chan, S. -L. Lai, K. -M. Lau, M. K. Fung, C. -S. Lee, S. -T. Lee, Influences of connecting unit architecture on the performance of tandem organic light-emitting devices, Adv. Funct. Mater., 17 (2007) 2509-2514. crossref(new window)

11.
J. H. Burroughes, D. D. Bradley, A. R. Brown, R. N. Marks, K. Mackay, R. H. Friend, P. L.Burns, and A.B. Holmes, Light-emitting diodes based on conjugated polymers, Nature, 347 (1990) 539-541. crossref(new window)

12.
Y. H. Son, M. J. Park, J. H. Kwon, Good color stable phosphorescent white organic light-emitting diodes with double emissive layer structure, Organic Electronics, 14 (2013) 1183-1188. crossref(new window)

13.
Ji-Hyun Kim, Sung-Hoo Ju, Emission characteristics of multi-tandem OLED using MoOx with CGL, J. Kor. Inst. Surf. Eng., 48 (2015) 105-109. crossref(new window)