Characteristics of LDPE resin film depending on RP contents
JO, Dong-Soo; Noh, Young-Tai; Park, Byung-Sun;
  PDF(new window)
 Abstract
Due to tightened environmental regulations on halogen type flame retardants, the portions of those based on phosphorous compounds that are non-halogen type is rising. When producing functional film, the physical and thermal properties become distinctly different depending on the amount of Red-phosphorus(RP) addition which causes flame resistance. The physical properties of resin fall in big scale when too much flame retardants are added, and it is hard to be applied to functional films such as shrink or anticorrosive film. The purpose of this research is to study the effects on mechanical, physical, and other properties of RP-LDPE films by changing the RP-MB contents. The LDPE film used for this study was produced through blow-type injection molding. The flame resistance was VTM-0, and the tear resistance showed inverse trends of MD and TD. Contraction percentage showed no relationship with the amount of RP content, but the anti-corrosive property showed 0.05 % better result than the national anti-corrosion shrink film reliability standard.
 Keywords
Flame retardant;LDPE (Low Density Polyethylene);MB (Master Batch);Red phosphorus;
 Language
Korean
 Cited by
 References
1.
M. Modesti, A. Lorenzetti, "Flame retardancy of polyisocyanurate-polyurethane foams: use of different charring agents", Polym. Degrad. Stab., 78, 341, 2002. DOI: http://dx.doi.org/10.1016/S0141-3910(02)00184-2 crossref(new window)

2.
W. Y. Chen, Y. Z. Wang, F. C. Chang, "Thermal and Flame Retardation Properties of Melamine Phosphate-Modified Epoxy Resins", J. Polym. Res., 11, 109, 2004. DOI: http://dx.doi.org/10.1023/B:JPOL.0000031069.23622.bc crossref(new window)

3.
O. P. Korobeinichev, V. M. Shvartsberg, A. G. Shmakov, D. A. Knyazkov, and I. V. Rybitskaya, Proceedings of the Combustion Institute, 31, 2741, 2007. DOI: http://dx.doi.org/10.1016/j.proci.2006.07.120 crossref(new window)

4.
M. Liu, Y. Liu, Q. Wang, "Flame-Retarded Poly(propylene) with Melamine Phosphate and Pentaerythritol/Polyurethane Composite Charring Agent", Macromol. Mater. Eng., 292, 206, 2007. DOI: http://dx.doi.org/10.1002/mame.200600353 crossref(new window)

5.
L. Song, Y. Hu, Y. Tang, R. Zhang, Z. Chen, W. Fan, "Study on the properties of flame retardant polyurethane/organoclay nanocomposite", Polym. Degrad. Stab., 87, 111, 2005. DOI: http://dx.doi.org/10.1016/j.polymdegradstab.2004.07.012 crossref(new window)

6.
F. Siminoi, M. Chechin, M. Modesti, A. Lorenzetti, "Influence of different flame retardants on fire behaviour of modified PIR/PUR polymers", Polym. Degrad. Stab., 74, 475, 2001. DOI: http://dx.doi.org/10.1016/S0141-3910(01)00171-9 crossref(new window)

7.
Y. Chen, Q. Wang, W. Yan, H. Tang, "Preparation of flame retardant polyamide composite with melamine cyanurate nanoparticles in situ formed in extrusion process", Polym. Degrad. Stab., 91, 2632, 2006. DOI: http://dx.doi.org/10.1016/j.polymdegradstab.2006.05.002 crossref(new window)

8.
B. Y. Jo, S. C. Moon, J. K. Choi, "Effect of Waste Ground Tire Rubber on Flame Retardancy and Foaming Properties of the NBR foams", Elast. Compos., 38, 251, 2003.

9.
U. Braun, B. Schartel, M. A. Fichera, C. Jager, "Flame retardancy mechanisms of aluminium phosphinate in combination with melamine polyphosphate and zinc borate in glass-fibre reinforced polyamide 6,6", Polym. Degrad. Stab., 92, 1528, 2007. DOI: http://dx.doi.org/10.1016/j.polymdegradstab.2007.05.007 crossref(new window)

10.
M. Thirumal, D. Khastgir, N. K. Singha, B. S. Manjunath, Y. P. Naik, "Effect of expandable graphite on the properties of intumescent flame-retardant polyurethane foam", J. Appl. Polym. Sci., 110, 2586, 2008. DOI: http://dx.doi.org/10.1002/app.28763 crossref(new window)

11.
T. M. Jayaweera, C. F. Melius, W. J. Pitz, C. K. Westbrooka, O. P. Korobeinichev, V. M. Shvartsberg, A. G. Shmakov, I. V. Rybitskaya, and H. J. Curran, "Combustion and Flame", 140, 103 2005. DOI: http://dx.doi.org/10.1016/j.combustflame.2004.11.001 crossref(new window)

12.
J. G. Uhlmann, J. D. Oelberg, K. D. Sikkema, and R. G. Nelb, "Plastics Additives and Compounding", May/June, 38 1993.

13.
T. Akiyoshi and S. Tamura, European Patent Application 1,055,705 2000.

14.
D. Hoang, J. Kim, and B. N. Jang, Polym. Degrad. Stabil., 93, 2042 2008. DOI: http://dx.doi.org/10.1016/j.polymdegradstab.2007.10.020 crossref(new window)

15.
G. Kumar and A. Z. Worku, PCT Patent Application WO 00/17268 2000.

16.
Korean Standard Association, KS T 1043, KSA, 2011

17.
Korean Standard Association, KS M ISO 6383-2, 2010

18.
Korean Standard Association, KS M ISO 9773, 2011

19.
KRICT, RS-KRICT-006, 2011.