Evaluation of Shear Bond Strength and Microleakage of Bulk-fill Resin Composites
Lee, Hanbyeol; Seo, Hyunwoo; Lee, Juhyun; Park, Howon;
  PDF(new window)
The aim of this study was to evaluate shear bond strength (SBS) of bulk-fill resin composites (RCs) to dentin and their micro-leakage. One high-viscosity bulk-fill RC and 2 low-viscosity bulk-fill RCs were compared with 1 conventional RC. 7thgenerationbondingagentswereused. In order to evaluate SBS values, 40 permanent molars were selected and divided into 4 groups. The bulk-fill RCs were applied in 4 mm thickness, whereas the conventional RC was applied in 2 mm thickness. In order to evaluate micro-leakage, class I cavities () were prepared in 32 permanent molars. The teeth were divided into 4 groups and restored with resin composites in an increment of 4 mm for the bulk-fill RC and in 2 horizontal increments of 2 mm for the conventional RC. The mean SBS value of conventional RC showed no statistically significant difference when compared with those of low-viscosity bulk-fill RCs. However, the mean SBS value of high-viscosity bulk-fill RC was significantly lower than that of conventional RC (p < 0.05). There were no statistically significant differences in micro-leakage between the 4 groups. For SBS and micro-leakage, the use of low-viscosity bulk-fill RCs might help clinicians simplify the procedure.
Bulk-fill resin composites;Shear bond strength;Micro-leakage;7thgenerationbondingagent;
 Cited by
Bulk-fill 복합레진과 전통적 복합레진의 물성비교,노태환;송은주;박소영;표애리;권용훈;김지연;김신;정태성;

대한소아치과학회지, 2016. vol.43. 4, pp.365-373 crossref(new window)
Comparison of the Mechanical Properties between Bulk-fill and Conventional Composites, THE JOURNAL OF THE KOREAN ACADEMY OF PEDTATRIC DENTISTRY, 2016, 43, 4, 365  crossref(new windwow)
Evaluation of Microhardness of Bulk-base Composite Resins According to the Depth of Cure, THE JOURNAL OF THE KOREAN ACADEMY OF PEDTATRIC DENTISTRY, 2017, 44, 3, 335  crossref(new windwow)
Evaluation of Cavity Wall Adaptation of Bulk-fill Resin Composites in Class II Cavities of Primary Molar, THE JOURNAL OF THE KOREAN ACADEMY OF PEDTATRIC DENTISTRY, 2017, 44, 4, 446  crossref(new windwow)
Kubo S, Yokota H, Yokota H, Hayashi Y : The effect of light-curing modes on the microleakage of cervical resin composite restorations. J Dent, 32:247-254, 2004. crossref(new window)

Karthick K, Sivakumar K, Geetha P, Shankar S : Polymerization Shrinkage of Composites - A Review. J Ind Acad Dent Spec, 2:32-36, 2011.

Winkler MM, Katona TR, Paydar NH : Finite element stress analysis of three filling techniques for class V light-cured composite restorations. J Dent Res, 75:1477-1483, 1996. crossref(new window)

Versluis A, Douglas WH, Cross M, Sakaguchi RL : Does an incremental filling technique reduce polymerization shrinkage stresses? J Dent Res, 75:871- 878, 1996. crossref(new window)

Manhart J, Hickel R : Bulk-fill-composites. Modern application technique of direct composites for posterior teeth. Swiss Dent J, 124:19-37, 2014.

Czasch P, Ilie N : In vitro comparison of mechanical properties and degree of cure of bulk fill composites. Clin Oral Investig, 17:227-235, 2013. crossref(new window)

Bucuta S, Ilie N : Light transmittance and micromechanical properties of bulk fill vs. conventional resin based composites. Clin Oral Investig, 18:1991- 2000, 2014. crossref(new window)

Moorthy A, Hogg CH, Fleming GJ, et al. : Cuspal deflection and microleakage in premolar teeth restored with bulk-fill flowable resin-based composite base materials. J Dent, 40:500-505, 2012. crossref(new window)

Campos EA, Ardu S, Krejci I, et al. : Marginal adaptation of class II cavities restored with bulk-fill composites. J Dent, 42:575-581, 2014. crossref(new window)

Alrahlah A, Silikas N, Watts DC : Post-cure depth of bulk fill dental resin-composites. Dent Mater, 30: 149-154, 2014. crossref(new window)

El-Damanhoury H, Platt J : Polymerization shrinkage stress kinetics and related properties of bulk-fill resin composites. Oper Dent, 39:374-382, 2014. crossref(new window)

Leprince JG, Palin WM, Leloup G, et al. : Physicomechanical characteristics of commercially available bulk-fill composites. J Dent, 32:247-254, 2014.

Scotti N, Comba A, Berutti E, et al. : Microleakage at enamel and dentin margins with a bulk fills flowable resin. Eur J Dent, 8:1-8, 2014. crossref(new window)

Jang JH, Park SH, Hwang IN : Polymerization shrinkage and depth of cure of bulk-fill resin composites and highly filled flowable resin. Oper Dent, 40:172-180, 2015. crossref(new window)

Roggendorf MJ, Kramer N, Frankenberger R, et al. : Marginal quality of flowable 4-mm base vs. conventionally layered resin composite. J Dent, 39:643- 647, 2011. crossref(new window)

Van Ende A, De Munck J, Van Meerbeek B, et al. : Bulk-filling of high C-factor posterior cavities: effect on adhesion to cavity-bottom dentin. Dent Mater, 29:269-277, 2013. crossref(new window)

Ilie N, Schoner C, Bucher K, Hickel R : An in-vitro assessment of the shear bond strength of bulk-fill resin composites to permanent and deciduous teeth. J Dent, 42:850-855, 2014. crossref(new window)

Flury S, Peutzfeldt A, Lussi A : Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites. Dent Mater, 30:1104-1112, 2014. crossref(new window)

El-Safty S, Silikas N, Watts DC : Creep deformation of restorative resin-composites intended for bulk-fill placement. Dent Mater, 28:928-935, 2012. crossref(new window)

Goodis HE, Marshall GW Jr, Marshall SJ, et al. : Storage effects on dentin permeability and shear bond strengths. Dent Mater, 9:79-84, 1993. crossref(new window)

Kim CY, Shin DH : Microleakage of composite resin restoration according to the number of thermocycling. J Korean Acad Conserv Dent, 32:377-384, 2007. crossref(new window)

Venhoven BA, de Gee AJ, Davidson CL : Polymerization contraction and conversion of lightcuring BisGMA-based methacrylate resins. Biomaterials, 14:871-875, 1993. crossref(new window)

Sakaguchi RL, Wiltbank BD, Shah NC : Critical configuration analysis of four methods for measuring polymerization shrinkage strain of composites. Dent Mater, 20:388-396, 2004. crossref(new window)

Yamazaki PC, Bedran-Russo AK, Pereira PN, Wsift EJ Jr : Microleakage evaluation of a new lowshrinkage composite restorative material. Oper Dent, 31:670-676, 2006. crossref(new window)

Eick JD, Welch FH : Polymerization shrinkage of posterior composite resins and its possible influence on postoperative sensitivity. Quintessence Int, 17: 103-111, 1986.

Technical Manual - SureFil SDR Flow from Dentsply Caulk. Assessment service. Available from URL: files/SureFil_Technical _Manual.pdf (Assessd on September 7, 2014)

Scientific Compendium Venus BulkFill reported by Heraeus kulzer. Available from http://heraeus-kulzer- scientific _compendiums___from_hkg/Venus_Bulk_ Fill_Scientific_Compendium.pdf (Assessd on September 7, 2014)

Tetric N-Ceram Bulk Fill - Ivoclar Vivadent Asia. Assessment service. Available from URL: media/document/15761/Tetric+N-Ceram+Bulk+ Fill (Assessd on September 7, 2014)

Alshali RZ, Silikas N, Satterthwaite JD : Degree of conversion of bulk-fill compared to conventional resin-composites at two time intervals. Dent Mater, 29:e213-e217, 2013. crossref(new window)

Xu X, Sandras DA, Burgess JO : Shear bond strength with increasing light-guide distance from dentin. J Esthet Restor Dent, 18:19-27, 2006. crossref(new window)

A laboratory Evaluation of Bulk-Fill Versus Traditional Multi-Increment-Fill Resin-Based Composites reported by ADA Professional Product Review. Assessment service. Availabe from URL: http:// _VOL8_ISS3. ashx (Assessd on December 10, 2014)

Leloup G, D'Hoore W, Vreven J, et al. : Meta-analytical review of factors involved in dentin adherence. J Dent Res, 80:1605-1614, 2001. crossref(new window)

Hwang SJ, Shin DH : Estimation of relation for microleakage and SEM evaluation for marginal adaptation of the restoration. J Korean Acad Conserv Dent, 31:337-343, 2006. crossref(new window)

Knobloch LA, Gailey D, Kerby RE, et al. : Bond strengths of one- and two-step self-etch adhesive systems. J Prosthet Dent, 97:216-222, 2007. crossref(new window)

Margvelashvili M, Goracci C, Ferrari M, et al. : In vitro evaluation of bonding effectiveness to dentin of all-in-one adhesives. J Dent, 38:106-112, 2010. crossref(new window)