Preparation of Acrylic Tackifiers and Mechanical Properties of Acrylic Pressure-Sensitive Adhesives Containing Acrylic Tackifiers
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
  • Journal title : Textile Science and Engineering
  • Volume 52, Issue 6,  2015, pp.431-437
  • Publisher : The Korean Fiber Society
  • DOI : 10.12772/TSE.2015.52.431
 Title & Authors
Preparation of Acrylic Tackifiers and Mechanical Properties of Acrylic Pressure-Sensitive Adhesives Containing Acrylic Tackifiers
You, Ryong; Lee, Seo-Ho; Park, Won Ho;
  PDF(new window)
 Abstract
An acrylate tackifier was prepared for producing high performance acrylic pressure-sensitive adhesives (PSAs). PSAs exhibiting high adhesion values were prepared using 2-ethyl hexylacrylate (2-EHA), 2-carboxyethyl acrylate (-CEA), and acrylic acid (AA) monomers. The acrylate tackifier was prepared using an acrylic monomer for improving its compatibility with the acrylic PSA. The weight-average molecular weights of PSA and the acrylate tackifier were found to be around and 20,000-40,000 g/mol, respectively. Physical properties (such as the peel strength, tack, and the holding power) of the mixtures of acrylic PSA with different acrylate tackifiers were enhanced with an increase in the amount of tackifier added.
 Keywords
acrylate tackifier;pressure sensitive adhesives;adhesive properties;
 Language
Korean
 Cited by
 References
1.
J. Kajtna, B. Alic, M. Krajnc, and Sebenik, "Influence of Hydrogen Bond on Rheological Properties of Solventless UV Crosslinkable Pressure Sensitive Acrylic Adhesive Prepolymer", Int. J. Adhes. Adhes., 2014, 49, 103-108. crossref(new window)

2.
S. Sun, M. Li, and A. Liu, "A Review on Mechanical Properties of Pressure Sensitive Adhesives", Int. J. Adhes. Adhes., 2013, 41, 98-106. crossref(new window)

3.
Y. Peykova, O. V. Lebedeva, A. Diethert, P. Muller-Buschbaum, and Willenbacher, "Adhesive Properties of Acrylate Copolymers: Effect of the Nature of the Substrate and Copolymer Functionality", Int. J. Adhes. Adhes., 2012, 34, 107-116. crossref(new window)

4.
J. Kajtna and Krajnc, "Solventless UV Crosslinkable Acrylic Pressure Sensitive Adhesives", Int. J. Adhes. Adhes., 2011, 31, 822-831. crossref(new window)

5.
D. Satas, "Handbook of Pressure Sensitive Adhesive Technology", Van Nostrand Reinhold, NY, 1989.

6.
W. Brockmann and Huther, "Adhesion Mechanisms of Pressure Sensitive Adhesives", Int. J. Adhes. Adhes., 1996, 16, 81-86. crossref(new window)

7.
E. P. Chang, "Viscoelastic Windows of Pressure-sensitive Adhesives", J. Adhes., 1991, 34, 189-200. crossref(new window)

8.
K. Eba, H. Senom, and K. Horigome, "UV Curable Pressure-Sensitive Adhesives for Fabricating Semiconductors. I. Development of Easily Peelable Diciing Tapes", J. Appl. Polym. Sci., 2003, 90, 436-441. crossref(new window)

9.
J. D. Zhang, M. J. Yang, Y. R. Zhu, and H. Yang, "Synthesis and Characterization of Crosslinkable Latex with Interpenetrating Network Structure Based on Polystyrene and Polyacrylate", Polym. Int., 2006, 55, 951-960. crossref(new window)

10.
W. Jiang, F. L. Jin, and S. J. Park, "Synthesis of Ditrimethylolpropane Acrylate with Low Functionality for UVcurable Coatings", J. Ind. Eng. Chem., 2012, 18, 1577-1581. crossref(new window)

11.
A. B. Foster, P. A. Lovell, and M. A. Rabjohns, "Control of Adhesive Properties Through Structured Particle Design of Water-borne Pressure-sensitive Adhesives", Polymer, 2009, 50, 1654-1670. crossref(new window)

12.
Y. Xia, W. Yan, S. Shi, and S. Jiao, "Effect of Tackifiers on the Emulsion Polymerization of Acrylate", Journal of Beijing University of Chemical Technology (Natural Science Edition), 2007, 34, 44-47.

13.
L. Ming, X. Xiuven, L. Qin, and T. Xuedi, "The Influence of Tackifier Resins on the Adhesion of Polyacrylate Pressure-Sensitive Adhesive", J. China Adhesives, 1999, 5, 27-29.

14.
A. J. Crosby and K. R. Shull, "Adhesive Failure Analysis of Pressure-sensitive Adhesives", J. Polym. Sci. Part B: Polym. Phys., 1999, 37, 3455-3472.

15.
C. M. Ryu, B. L. Pang, H. I. Kim, J. W. Park, S. W. Lee, H. J. Kim, and K. M. Kim, "Variation of Adhesion Characteristics of Acryl Copolymer/Multi-functional Monomer Based PSA by UV Curing", Polymer Korea, 2011, 36, 315-320.