Study on the Growth of Monoclinic VO2 Phase Applicable for Thermochromic Ceramic Tile
Jung, DaeYong; Kim, Ungsoo; Cho, Wooseok;
  PDF(new window)
Vanadium dioxide () of monoclinic phase exhibits Metal Insulator Phase Transition (MIPT) phenomenon involving a sharp change in electrical and optical properties at . Solution-based process is applied to form uniform coating layer on ceramic tiles. This can selectively block the near-infrared light to possibly reduce the energy loss and prevent dew condensation caused by the temperature difference. Heat treatment conditions including temperature and dwell time were examined to obtain a monoclinic single phase. Both rutile and monoclinic phases were observed from in the tiles post-annealed below . Desired monoclinic single phase was grown in the tiles heat treated at . Nano facets of irregular size were observed in the monoclinic phase involving the phase-transition. Grain growth of monoclinic phase was observed as a function of dwell time at .
Thermochromic;Vanadium oxide;MIPT;Infrared block;Ceramic tile;
 Cited by
C. B. Greenberg, "Optically Switchable Thin Films: a Review," Thin Solid Films, 251 [2] 81-93 (1994). crossref(new window)

M. Borek, F. Qian, V. Nagabushnam, and R. K. Singh, "Pulsed Laser Deposition of Oriented $VO_2$ Thin Films on Rcuts App Hire Substrates," Appl. Phys. Lett., 63 [24] 3288- 90 (1993). crossref(new window)

A. D. Rata, A. R. Chezan, C. Presura, and T. Hibma, "Electrical Properties of Epitaxially Grown VOx Thin Films," Surf. Sci., 532 [10] 341-45 (2003).

R. Lindstrom, V. Maurice, S. Zanna, L. Klein, H. Groult, L. Perrigaud, C. Cohen, and P. Marcus, "Thin Film of Vanadium Oxide Grown on Vanadium Metal: Oxidation Conditions to Produce $V_2O_5$ Films for Li-intercalation Application sand Characterisation by XPS, AFM, RBS/NRA," Surf. Interface Anal., 38 [1] 6-18 (2006). crossref(new window)

C. H. Griffiths and H. K. Eastwood, "Influence of Stoichiometry on the Metal-semiconductor Transition in Vanadium Dioxide," J. Appl. Phys., 45 [5] 2201-6 (1974). crossref(new window)

C. Cao and Y. Gao, "Pure Single-crystal Rutile Vanadium Dioxide Powder: Synthesis, Mechanism and Phase-transformation Property," J. Phys. Chem., 112 [48] 18810-14 (2008).

M. Soltani, M. Chaker, E. Haddad, and R. V. Kruzelesky, "Thermochromic Vanadium Dioxide Smart Coatings Grown on Kapton Substrates by Reactive Pulsed Laser Deposition," J. Vac. Sci. Technol. A, 24 [3] 612-17 (2006). crossref(new window)

W. Burkhardt, T. Christmann, S. Franke, W. Kriegseis, D. Meister, B. K. Meyer, W. Niessner, D. Schalch, and A. Scharmann, "Tungsten and Fluorine Co-doping of $VO_2$ Films," Thin Solid Films, 402 [1] 226-31 (2002). crossref(new window)

H. Jerominek, F. Picard, and D. Vincent, "Vanadium-oxide Films for Optical Switching and Detection," Opt. Eng., 32 [9] 2092-99 (1993). crossref(new window)

C. Leroux and G. Nihoul, "From $VO_2(B)$ to $VO_2(R)$: Theoretical Structures of $VO_2$ Polymorphs and in Situ Electron Microscopy," Phys. Rev. B, 57 [9] 5111-21 (1998). crossref(new window)

S. Ji, Y. Zhao, F. Zhang, and P. Jin, "Synthesis and Phase Transition Behavior of W-doped $VO_2(A)$ Nanorods," J. Ceram. Soc. Jpn., 118 [1382] 867-71 (2010). crossref(new window)

P. E. Ngoepe, C. R. A. Catlow, and S. M. Woodley, "The Displacive Phase Transition of Vanadium Dioxide and the Effect of Doping with Tungsten," Chem. Mater., 20 [5] 1764-72 (2008). crossref(new window)

M. M. Qazilbash and D. N. Basov, "Mott Transition in $VO_2$ Revealed by Infrared Spectroscopy and Nano-imaging," Science, 318 [5857] 1750-53 (2007). crossref(new window)

S. M. Woodley, "The Mechanism of the Displacive Phase Transition in Vanadium Dioxide," Chem. Phys. Lett., 453 [4] 167-72 (2008). crossref(new window)

P. Jin, S. Ji, and F. Zhang, "Unexpected Phase Transformation from $VO_2(R)$ to $VO_2(A)$ during Hydrothermal Treatment in the $V_2O_5-H_2C_2O_4-H_2O$ System," Res. Chem. Intermed., 37 [2] 493-502 (2011). crossref(new window)

A. Cavalleri, All at once, Science; Vol. 318, pp. 755-56, New York, 2007. crossref(new window)

I. P. Parkin and T. D. Manning, "Intelligent Thermochromic Windows," J. Chem. Educ., 83 [3] 393-400 (2006). crossref(new window)

J. B. Torrance, P. Lacorre, C. Asavaroengchai. and R. M. Metzger, "Why are Some Oxides Metallic, While Most are Insulating," Physica C, 182 [4] 351-62 (1991). crossref(new window)

J. F. De Natale, P. J. Hood, and A. B. Harker, "Formation and Characterization of Grain-oriented $VO_2$ Thin Films," J. Appl. Phys., 66 [12] 5844-50 (1989). crossref(new window)

Y. T. Wang and C. H. Chen, "Facile Growth of Thermochromic $VO_2$ Nanostructure with Greatly Varied Phase and Morphologies," Inorg. Chem., 52 [5] 2550-55 (2013). crossref(new window)

Z. Gui, R. Fan, X. H. Chen, and Y. C. Wu, "New Metastable Phase of Needle-like Nanocrystalline $VO_2{\cdot}H_2O$ and Phase Transformation," J. Solid State Chem., 157 [2] 250-54 (2001). crossref(new window)

B. S. Guiton, Q. Gu, A. L. Prieto, M. S. Gudiksen, and H. Park, "Single-crystalline Vanadium Dioxide Nenowires with Rectangular Cross Sections," J. Am. Chem. Soc., 127 [2] 498-99 (2005). crossref(new window)

G. Armstrong, J. Canales, A. R. Armstrong, and P. G. Bruce, "The Synthesis and Lithium Intercalation Electrochemistry of $VO_2(B)$ Ultra-thin Nanowires," J. Power Sources, 178 [2] 723-28 (2008). crossref(new window)

L. Q. Mai, B. Hu, T. Hu, W. Chen, and E. D. Gu, "Electrical Property of Mo-Doped $VO_2$ Nanowire Array Film by Melting- quenching Sol-gel Method," J. Phys. Chem. B, 110 [39] 19083-86 (2006). crossref(new window)

S. A. Corr, M. Grossman, Y. Shi, K. R. Heier, G. D. Stucky, and R. Seshadri, "$VO_2(B)$ Nanorods: Solvothermal Preparation, Electrical Properties, and Conversion to Rutile $VO_2$ and $V_2O_3$," J. Master. Chem., 19 [32] 4362-67 (2009). crossref(new window)