Physical and Chemical Properties of Cement Mortar with Gamma-C2S
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Physical and Chemical Properties of Cement Mortar with Gamma-C2S
Lee, Sung-Hyun; Kim, Kyungnam; Mabudo, Mabudo; Song, Myong-Shin;
  PDF(new window)
 Abstract
Presently, for the cement industry, studies that seek to reduce , because of the development of the plastic industry and demand for reduction of energy use, have been actively conducted among them, studies attempting to use Gamma- to fix have been actively conducted. The compound has an important function in reacting to and stiffening through carbonatization in the air. The compound, reacting to in the air, generates within the pore structure of cement materials and densifies the pore structure this leads to an improvement of the durability and to the characteristic of resistance against neutralization. Therefore, in this experiment, in order to synthesize , limestone sludge and waste foundry sands are used these materials are plasticized for 30 or 60 minutes at , and are prevented from being cooled in the temperature range of when they are about to be cooled. XRD analysis and XRF analysis are used to determine the effects of this process on synthesization, the temperature at which a thing is plasticized, and the conditions for cooling that obtain in the plasticized clinker also, in order to confirm the capture function, analysis of the major hydration products is conducted through an analysis of carbonatization depth and compressive strength, and through MIP analysis and XRD Rietveld analysis. As a result of these analyses, it is found that when was synthesized, the clinker that was plasticized at for one hour demonstrated the highest yield rate the sample with which the was mixed generated when it reacted with therefore, carbonatization depth and porosity were reduced, and the compressive strength was increased.
 Keywords
capture;Pore;Vaterite;Gamma-;
 Language
English
 Cited by
 References
1.
C.-W. Park, "Eco-Friendly of Concrete," Mag. Korea Concr. Inst., 20 [6] 24-6 (2008).

2.
S.-H. Lee, "Hydration Mechanism of Ground Granulated Blast Furnace Slag," Mag. Korea Concr. Inst., 24 [6] 31-4 (2012).

3.
J. I. Escalante-Garcia, "Portland Cement-Blast Furnace Slag Mortars Activated Using Waterglass: Effect of Temperature and Alkali Concentration," Construct. Build. Mater., 66 323-28 (2014). crossref(new window)

4.
K. J. Mun, "The Effect of Slaked Lime, Anhydrous Gypsum and Limestone Powder on Properties of Blast Furnace Slag Cement Mortar and Concrete," Construct. Build. Mater., 21 1576-82 (2007). crossref(new window)

5.
H. Sakamoto, "pH Behavior of Hydrated Low-Alkalinity Cement," J. Nucl. Fuel Cycle Environ., 5 [2] 37-42 (1999). crossref(new window)

6.
F. Winnefeld, "Hydration of Calcium Sulfo-Aluminate Cements - Experimental Findings and Thermodynamic Modelling," Cem. Concr. Res., 40 1239-47 (2010). crossref(new window)