Preparation of Anatase Particles through Electro-Dialysis of TiCl4 Aqueous Solution
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Preparation of Anatase Particles through Electro-Dialysis of TiCl4 Aqueous Solution
Chang, Myung Chul;
  PDF(new window)
 Abstract
Anatase particles of titanium dioxide were prepared from aqueous solution by using an electro-dialysis [ED] process. For the preparation of an aqueous solution of precipitates, liquid frozen in ice was transferred to a neck flask and then hydrolyzed using deionized [DI] . During the hydrolysis of the solution at , a slurry solution of was obtained and the color changed from red to orange. The ED process was applied for the removal of chlorine content in the slurry solution. Two kinds of hydrolyzed slurry solution with lower [] and higher [] were sampled and the ED process was applied for the samples according to the removal time of []. With de-chlorination, the solution status changed from sol to gel and the color quickly changed to blue. Finally, white crystalline powders were formed and the phase was confirmed by XRD to be anatase crystallites. The morphology of the hydrous titania particles in the solution was observed by FE-SEM. The hydrous titania particles were nano-crystalline, and easily coagulated with drying.
 Keywords
Titanium tetrachloride;Anatase;Electrodialysis;Nano-particles;Anion membrane;
 Language
English
 Cited by
 References
1.
A. L. Linsebigler, G. Q. Lu, and J. T. Yates, "Photocatalysis on $TiO_2$ Surfaces: Principles, Mechanisms, and Selected Results," Chem. Rev., 95 [3] 735-58 (1995). crossref(new window)

2.
B. O'Regan and M. Gratzel, "A Low-Cost, High-Efficiency Solar Cell Based on Dye-Sensitized Colloidal $TiO_2$ Films," Nature, 353 737-40 (1991). crossref(new window)

3.
L. D. Birkefeld, A. M. Azad, and S. A. Akbar, "Carbon Monoxide and Hydrogen Detection by Anatase Modification of Titanium Dioxide," J. Am. Ceram. Soc., 75 [11] 2964-68 (1992). crossref(new window)

4.
H. Wang, Y. Wu, and B. Q. Xu, "Preparation and Characterization of Nanosized Anatase $TiO_2$ Cuboids for Photocatalysis," Appl. Catal., B, 59 [3] 139-46 (2005). crossref(new window)

5.
S. D. Park, Y. H. Cho, W. W. Kim, and S.-J. Kim, "Understanding of Homogeneous Spontaneous Precipitation for Monodispersed $TiO_2$ Ultrafine Powders with Rutile Phase around Room Temperature," J. Solid State Chem., 146 [1] 230-38 (1999). crossref(new window)

6.
L. Vechot, J. E. H. Buston, J. Kay, G. A. Round, S. Masharani, G. A. Tickle, and R. Rowlands, "Experimental Study of the Liquid Phase Hydrolysis Reaction in Titanium Tetrachloride," Hazards XXII, Symposium Series No. 156, 238-45 (2011).

7.
M. C. Chang, "Yttrium-Stabilized Zirconia Particles Prepared Using Electro-dialysis of $(Zr,Y)OCl_2$ Aqueous Solution," J. Korean Ceram. Soc., 51 [5] 466-71 (2014). crossref(new window)

8.
M. C. Chang and R. DeLong, "Calcium Phosphate Formation in Gelatin Matrix Using Free Ion Precursors of $Ca^{2+}$ and Phosphate Ions," Dent. Mater., 25 [2] 261-68 (2009). crossref(new window)

9.
Y. Chen, A. Lin, and F. Gan, "Preparation of Nano-$TiO_2$ from $TiCl_4$ by Dialysis Hydrolysis," Powder Technol., 167 [3] 109-16 (2006). crossref(new window)

10.
S. J. Kim, S. D. Park, Y. H. Jeong, and S. Park, "Homogenous Precipitation of $TiO_2$ Ultrafine Powders from Aqueous $TiOCl_2$ Solution," J. Am. Ceram. Soc., 82 [4] 927-32 (1999). crossref(new window)

11.
S. J. Kim, C. H. Jung, S. D. Park, S. C. Kwon, and S. Park, "Preparation of Crystalline $TiO_2$ Ultrafine Powders from Aqueous $TiCl_4$ Solution by Precipitation Process," J. Korean Ceram. Soc., 35 [4] 325-32 (1998).

12.
A. D. Paola, G. Cufalo, M. Addamo, M. Bellardita, R. Campostrini, M. Ischia, R. Ceccato, and L. Palmisano, "Photocatalytic Activity of Nanocrystalline $TiO_2$ (Brookite, Rutile and Brookite-based) Powders Prepared by Thermohydrolysis of $TiCl_4$ in Aqueous Chloride Solutions," Colloids Surf., A, 317 [1-3] 366-76 (2008). crossref(new window)

13.
Q.-H. Zhang, L. Gao, and J.-K. Guo, "Preparation and Chracterization of Nanosized $TiO_2$ Powders from Powders from Aqueous $TiCl_4$ Solution," Nanostruct. Mater., 11 [8] 1293-300 (1999). crossref(new window)

14.
J. H. Lee and Y. S. Yang, "Effect of HCl Concentration and Reaction Time on the Change in the Crystalline State of $TiO_2$ Prepared from Aqueous $TiCl_4$ Solution by Precipitation," J. Eur. Ceram. Soc., 25 3573-78 (2005). crossref(new window)

15.
T.-H. Wang, A. M. Navarrete-Lopez, S. Li, D. A. Dixon, and J. L. Gole, "Hydrolysis of $TiCl_4$: Initial Steps in the Production of $TiO_2$," J. Phys. Chem. A, 114 [28] 7561-70 (2010). crossref(new window)

16.
J. Wang, C. Xu, M. Taya, and Y. Kuga, "A Flemion-Based Actuator with Ionic Liquid as Solvent," Smart Mater. Struct., 16 [2] S214-19 (2007). crossref(new window)

17.
K.-L. Huang, T. M. Holsen, and J. R. Selman, "Anion Partitioning in and Diffusion through a Nafion Membrane," Ind. Eng. Chem. Res., 42 [9] 3620-25 (2003). crossref(new window)

18.
W. Wang and W.R. Hu, "Concentration Distribution in Solution Crystal Growth: Effect of Moving Interface Conditions," J. Cryst. Growth, 203 [1-2] 227-33 (1999). crossref(new window)

19.
P.-Pong Chang and M. D. Donohue, "A Kinetic Approach to Crystallization from Ionic Solution, I. Crystal Growth," J. Colloid Interface Sci., 122 [1] 230-50 (1988). crossref(new window)

20.
P.-Pong Chang, M. D. Donohue, and J. L. Katz, "Kinetic Approach to Crystallization from Ionic Solution II. Cystal Nucleation," J. Colloid Interface Sci., 122 [1] 251-65 (1988). crossref(new window)

21.
P.-Pong Chang and M. D. Donohue, "The Effect of Complex Ions on Crystal Nucleation and Growth," J. Colloid Interface Sci., 126 [2] 579-91 (1988). crossref(new window)

22.
O. Sohnel, "The Mechanism of Crystallization; A Revision of Cencepts. Comment," Mater. Res. Bull., 9 [4] 489-94 (1974). crossref(new window)

23.
S. P. F. Humphreys-Owen, "Crystal Growth from Solution," Proc. R. Soc. London, Ser. A, 197 [1049] 218-37 (1949). crossref(new window)