Synthesis and Characterization of Covalently Cross-Linked SPEEK/Cs-substituted MoSiA/Ceria Composite Membranes with MoSiA for Water Electrolysis
facebook(new window)  Pirnt(new window) E-mail(new window) Excel Download
 Title & Authors
Synthesis and Characterization of Covalently Cross-Linked SPEEK/Cs-substituted MoSiA/Ceria Composite Membranes with MoSiA for Water Electrolysis
  PDF(new window)
To improve the electrochemical and mechanical characteristics, engineering plastic of the sulfonated polyether ether ketone (SPEEK) as polymer matrix was prepared in the sulfonation reaction of polyether ether ketone (PEEK). The SPEEK organic-inorganic blended composite membranes were prepared by sol-gel casting method. It was loaded with the highly dispersed ceria and cesium-substituted molybdosilicic acid (Cs-MoSiA) and 1,4-diiodobutane which was cross-linking agent contents of . Cs-MoSiA was added to increase proton conductivity. Ceria () was used as a free radical scavenger which degrade the membrane in polymer electrolyte membrane water elctrolysis (PEMWE). In conclusion, CL-SPEEK/Cs-MoSiA/Ceria 1% composite membrane showed high proton conductivity 0.2104 S/cm at which was better than Nafion 117 membrane.
PEMWE;SPEEK;Cs-MoSiA(Cs-substituted MoSiA);Ceria(Cerium(IV) oxide);radical scavenger;
 Cited by
수전해용 술폰화 폴리에테르 에테르 케톤과 셀룰로오스 고분자 복합막의 제조 및 특성,송유리;차진산;윤영요;문상봉;정장훈;

한국수소및신에너지학회논문집, 2016. vol.27. 5, pp.478-484 crossref(new window)
Preparation and Characterization of SPEEK/Cellulose Polymer Composite Membranes for Water Electrolysis, Transactions of the Korean hydrogen and new energy society, 2016, 27, 5, 478  crossref(new windwow)
A. Yilanci, I. Dincer, and H. K. Ozturk, "A review on solar-hydrogen/fuel cell hybrid energy systems for stationary applications", Prog. Energy Combust., Vol. 35, 2009, pp. 231-244. crossref(new window)

O. S. Joo, "Hydrogen Production Technology", Korean Chem. Eng. Res., Vol. 49, No. 6, December, 2011, pp. 688-696. crossref(new window)

M. Carmo, David L. Fritz, J. Mergel, and D. Stolten, "A comprehensive review on PEM water electrolysis", Int. J. Hydrogen Energy, Vol. 38, 2013, pp. 4901-4934. crossref(new window)

P. W. T. LU, S. Srinivasan, "Advances in water electrolysis technology with emphasis on use of the solid polymer electrolyte", J. Appl. Elecrochem., Vol. 9, 1979, pp. 269-283. crossref(new window)

T. Higashihara, K. Matsumoto, and M. Ueda, "Sulfonated aromatic hydrocarbon polymers as proton exchange membranes for fuel cells", Polymer, Vol. 50, 2009, pp. 5341-5357. crossref(new window)

T. J. Schmidt, U. A. Paulus, H. A. Gasteiger, and R. J. Behm, "The oxygen reduction reaction on a Pt/carbon fuel cell catalyst in the presence of chloride anions", J. Electroanal. Chem., Vol. 508, 2001, pp. 41-47. crossref(new window)

P. Trogadas, J. Parrondo, and V. Ramani, "Degradation Mitigation in Polymer Electrolyte Membranes Using Free-Radical Scavengers", ECS Transactions, Vol. 16, No. 2, 2008, pp. 1725-1733. crossref(new window)

D. Zhao, B. L. Yi, H. M. Zhang, H. M. Yu, L. Wang, Y. M. Ma, and D. M. Xing, "Cesium substituted 12- tungstophosphoric ($Cs_xH_{3-x}PW_{12}O_{40}$)loaded on ceriadegradation mitigation in polymer electrolyte membranes", J. Power Sources, Vol. 190, 2009, pp. 301-306. crossref(new window)

V. Ramani, H. R. Kunz, and J. M. Fenton, "Stabilized heteropolyacid/Nafion composite membranes for elevated temperature/low relative humidity PEFC operation", Electrochimica Acta, Vol. 50, No. 5, 2005, pp. 1181-1187. crossref(new window)

V. Ramani, H. R. Kunz, and J. M. Fenton, "Investigation of Nafion$^{(R)}$/HPA composite membranes for high temperature/low relative humidity PEMFC operation", J. Membrane Science, Vol. 232, 2004, pp. 31-44. crossref(new window)

S. L. Rhoden, and C. A. Linkous, "The optimization of SPEEK membranes using Phosphotungstic acid as a dopant", ECS Trans., Vol. 16, No. 2, 2008, 1461-1469. crossref(new window)

M. L. Ponce, "Organic-Inorganic hybrid membranes with heteropolyacids for DMFC applications", Ph. D. Dissertation, University of Hamburg, Hamburg, 2004.

Z. Cui, Y. Xiang, J. Si, M. Yang, Q. Zhang, and T. Zhang, "Ionic interactions between sulfuric acid and chitosan membranes", Carbohydrate Polymer, Vol. 73, 2008. pp. 111-116. crossref(new window)

H. Dogan, T. Y. Inan, E. Unveren, and M. Kaya, "Effect of cesium salt of tungstophosphoric acid (Cs-TPA) on the properties of sulfonated polyether ether ketone (SPEEK) composite membranes for fuel cell applications", Int. J. Hydrogen Energy, Vol. 35, 2010, pp. 7784-7795. crossref(new window)

S. S. Mohtar, A. F. Ismail, and T. Matsuura, "Preparation and characterization of SPEEK/MMT-STA composite membrane for DMFC application", J. Membrane Science, Vol. 371, 2011, pp. 10-19. crossref(new window)

G. R. Rao, and T. Rajkumar, "Interaction of Keggin anions of 12-tungstophosphoric acid with $Ce_xZr_{1-x}O_2$ solid solutions", J. Colloid Interface Sci., Vol. 324, 2008, pp. 134-141. crossref(new window)

Q. Huang, S. Wang, J. Huang, L. Zhuo, and Y. Guo, "Study on the heterogeneous degradation of chitosan with hydrogen peroxide under the catalysis of phosphotungstic acid", Carbohydrate Polymer, 68, 2007, pp. 761-765. crossref(new window)